Critical Flux and Fouling Analysis of PVDF-Mixed Matrix Membranes for Reclamation of Refinery-Produced Wastewater: Effect of Mixed Liquor Suspended Solids Concentration and Aeration

Innovative Approaches to Poultry Processing Wastewater Treatment: The Stainless Steel Ultrafiltration Membrane as a Viable Option

In pursuit of sustainability, we explored replacing conventional dissolved air floatation (DAF) in poultry processing wastewater (PPW) treatment with a precisely tuned 0.02 µm stainless-steel ultrafiltration (SSUF) membrane. SSUF is a robust, homogenously porous membrane with strong chemical resistance, ease of cleaning, and exceptional resistance to organic fouling. Unlike polymeric membranes, it can be regenerated multiple times, making it a cost-effective choice due to its compatibility with harsh chemical cleaning. The PPW used for the study was untreated wastewater from all processing units and post-initial screening. Our study revealed the SSUF membrane's exceptional efficiency at eliminating contaminants. It achieved an impressive removal rate of up to 99.9% for total suspended solids (TSS), oil, grease, E. coli, and coliform. Additionally, it displayed a notable reduction in chemical oxygen demand (COD), biochemical oxygen demand (BOD), and total Kjeldahl nitrogen (TKN), up to 90%, 76%, and 76%, respectively. Our investigation further emphasized the SSUF membrane's ability in pathogen removal, affirming its capacity to effectively eradicate up to 99.99% of E. coli and coliform. The measured critical flux of the membrane was 48 Lm-2h-1 at 38 kPa pressure and 1.90 m/s cross-flow velocity. In summary, our study highlights the considerable potential of the SSUF membrane. Its robust performance treating PPW offers a promising avenue for reducing its environmental impact and advocating for sustainable wastewater management practices.

Preparation and Characterization of PVDF-TiO2 Mixed-Matrix Membrane with PVP and PEG as Pore-Forming Agents for BSA Rejection

Polymeric membranes offer straightforward modification methods that make industry scaling affordable and easy; however, these materials are hydrophobic, prone to fouling, and vulnerable to extreme operating conditions. Various attempts were made in this study to fix the challenges in using polymeric membranes and create mixed-matrix membrane (MMMs) with improved properties and hydrophilicity by adding titanium dioxide (TiO₂) and pore-forming agents to hydrophobic polyvinylidene fluoride (PVDF). The PVDF mixed-matrix ultrafiltration membranes in this study were made using the non-solvent phase inversion approach which is a simple and effective method for increasing the hydrophilic nature of membranes. Polyvinylpyrrolidone (PVP) and polyethylene glycol (PEG) as pore-forming chemicals were created. Pure water flux, BSA flux, and BSA rejection were calculated to evaluate the mixed-matrix membrane's efficiency. Bovine serum albumin (BSA) solution was employed in this study to examine the protein rejection ability. Increases in hydrophilicity, viscosity, and flux in pure water and BSA solution were achieved using PVP and PEG additives. The PVDF membrane's hydrophilicity was raised with the addition of TiO₂, showing an increased contact angle to 71°. The results show that the PVDF-PVP-TiO₂ membrane achieved its optimum water flux of 97 L/(m²h) while the PVDF-PEG-TiO₂ membrane rejected BSA at a rate greater than 97%. The findings demonstrate that use of a support or additive improved filtration performance compared to a pristine polymeric membrane by increasing its hydrophilicity.

Influence of Dispersed TiO2 Nanoparticles via Steric Interaction on the Antifouling Performance of PVDF/TiO2 Composite Membranes

Herein, the influence of various contents of polyethylene glycol (PEG) on the dispersion of TiO2 nanoparticles and the comprehensive properties of PVDF/TiO2 composite membranes via the steric hindrance interaction was systematically explored. Hydrophilic PEG was employed as a dispersing surfactant of TiO2 nanoparticles in the pre-dispersion process and as a pore-forming additive in the following membrane preparation process. The slight overlap shown in the TEM image and low TSI value (<1) of the composite casting solution indicated the effective dispersion and stabilization under the steric interaction with a PEG content of 6 wt.%. Properties such as the surface pore size, the development of finger-like structures, permeability, hydrophilicity and Zeta potential were obviously enhanced. The improved antifouling performance between the membrane surface and foulants was corroborated by less negative free energy of adhesion (about −42.87 mJ/m2), a higher interaction energy barrier (0.65 KT) and low flux declination during the filtration process. The high critical flux and low fouling rate both in winter and summer as well as the long-term running operation in A/O-MBR firmly supported the elevated antifouling performance, which implies a promising application in the municipal sewage treatment field.