Effect of Lead and Zinc Impurities in Ironmaking and the Corresponding Removal Methods: A Review

Volatilisation Behaviour and Mechanism of Lead-Containing Slag during Physical Property Tests

According to physical property tests of lead-containing slag, the volatilisation behaviour of lead slag will have adverse impacts on test accuracy and further affect the control of chemical reactions, solidification and removal of inclusions during smelting. To analyse the volatilisation characteristics of lead slag, in this paper, four kinds of lead slags from lead direct reduction smelting with different PbO and ZnO content are taken. thermogravimetry, ISP-TOF were used. Additionally, the changes in volatiles and slag composition and phases were analysed with XRD and ICPS, and the volatilisation reaction mechanism was discussed. The results indicated that the volatilisation of lead slag can lead to a big weight loss of about to the slag with higher PbO content. The weight loss increases with the PbO content in slag increases. The volatile corresponding to the weight loss above 900 °C is mainly PbO and less ZnO. The higher the temperature is, the stronger the volatilisation is. With the increase in temperature and keeping time, most of the PbO can be evaporated and leaves little PbO in the residual slag. This will has great effect to physico-chemical property measurement of the slag with higher PbO content, especially to the property measurement that be kept at high temperature for a long time. Because the volatiles is trend to condense with the temperature decrease, mass spectrometer is limited by the condensation of volatiles, i.e., PbO, ZnO and so on, in the connection pipeline. The device should be modified for this use.

Mineralogical and Chemical Changes after Reduction Roasting of Xinjiang Iron Ore, China

The mineralogical and chemical changes in Chinese Xinjiang iron ore containing impurities, lead, and zinc as a result of reduction roasting were studied via chemical analysis, optical microscopy, X-ray fluorescence (XRF), electron probe microanalysis (EPMA), and energy-dispersive spectroscopy (EDS). Analysis showed that hematite was the main iron-bearing mineral, with small amounts of magnetite and iron silicate; lead impurities were mainly lead oxide and lead–iron alum, while zinc oxide was the main zinc impurity. X-ray fluorescence analysis for raw samples indicated the presence of quartz, hematite, magnetite, chlorite, calcite, and dolomite. The results of the analysis of roasted samples showed an increase in hematite at temperatures of 750 °C and 950 °C, while the elemental iron increased at a temperature of 1200 °C, along with the conversion of galena to lead oxide and sphalerite to zinc oxide, with a stable quartz ratio. The chemical analysis of the raw sample showed that the TFe grade of the sample was 47.04%, while the contents of harmful Pb and Zn impurities were 0.39% and 0.30%, respectively, both of which exceed the index (less than 0.10%) required by the iron industry for raw materials. The content of harmful sulfur impurities was also high, at 1.19%, which needs to be eliminated or reduced. The results of EPMA and EDS analysis of pre-roasting raw samples showed that chemical compositions vary in different locations in the hematite, magnetite, sphalerite, and galena micro-zones. It has also been observed that quartz is mostly diffused with magnetite and hematite, and sulfur appears in small quantities in most regions. The analysis after roasting showed that the percentages of lead, zinc, and sulfur impurities decreased by a large rate. It is clear that the roasting process plays a major role in removing impurities such as sulfur, which appears in a small percentage after the roasting process, and also helps in oxidizing the impurities of lead and zinc, which helps in removing them.