Effect of Autoclaving Cycles on the Cyclic Fatigue Resistance of Race and Race Evo Nickel-Titanium Endodontic Rotary Files: An In Vitro Study

Effect of simulated clinical use and sterilization on the cyclic fatigue resistance of nickel titanium files

Aim

Assess the effect of simulated clinical use and sterilization on the cyclic fatigue resistance of Race Evo and Tia Tornado Blue nickel titanium (NiTi) files.

Materials and Methods

For this study, a total of sixty-four NiTi files were selected, with thirty-two files each from two different manufacturers. Files from each manufacturer were subdivided into four subgroups (n = 8) based on the test parameters. The control groups included files that were neither used nor sterilized. Files from the test groups were used to prepare the root canals of extracted mandibular premolars and then sterilized. This procedure was repeated once, twice, or thrice, depending on the test group. All files were then subjected to a cyclic fatigue test. Data was statistically analyzed using the Kruskal-Wallis and Mann-Whitney U tests.

Results

No significant difference was observed in the number of cycles to failure (NCF) among the subgroups for both types of files (P = 0.869 for Tia Tornado Blue, P = 0.626 for Race Evo). Tia Tornado Blue files displayed significantly higher NCF values in the control (P = 0.021), once (P = 0.027), and thrice (P = 0.031) usage groups when compared to Race Evo files.

Conclusions

Repeated clinical use and sterilization for up to three cycles did not affect the cyclic fatigue resistance of Race Evo and Tia Tornado Blue files.

Evaluation of cyclic fatigue behavior of RACE EVO rotary Files: In-vitro comparative study

Introduction

Comparative evaluation of the newly introduced; RACE EVO file system to the currently well-performing file systems like HyFlex EDM OneFile, Vortex Blue, ProTaper Gold (PTG) with regards to the cyclic fatigue resistance.

Materials

&Methods.The endodontic rotary files under evaluation were segregated into four groups as follows:; RACE EVO, PTG, Vortex Blue, and HyFlex EDM OneFile. A detailed physical analysis of the cyclic fatigue resistance was performed in 15 files of each type (n = 60). Under the test conditions of 37 °C the test samples were subjected to continuous motion at the manufacturer recommended speed within an artificial curved canal until it fractured. For all the test samples, with the recording of time of fracture, calculation was done for number of cycles to fracture (NCF). In addition, the length of the fractured segment was determined. The fractured surface was further evaluated with scanning electron microscopic (SEM) images.

Results

Highest significance for NCF was seen in HyFlex EDM OneFile followed by the Vortex Blue, PTG, and; RACE EVO (p < 0.05) by analyzing the data statistically. Significant differences among the lengths of the fractured segments were evident among tested files, ranging between 4.73 and 6.3 mm (p < 0.05) with HyFlex EDM OneFile uniquely differentiating from the others showing the fracture at 6.3 mm. The common features of cyclic fatigue failure was further substantiated by SEM images.

Conclusions

Compared to the HyFlex EDM OneFile, Vortex Blue, and PTG files; RACE EVO demonstrated significantly lower resistance to cyclic fatigue.

Advancing Nitinol: From heat treatment to surface functionalization for nickel–titanium (NiTi) instruments in endodontics

Nickel-titanium (NiTi) alloy has been extensively researched in endodontics, particularly in cleaning and shaping the root canal system. Research advances have primarily focused on the design, shape, and geometry of the NiTi files as well as metallurgy and mechanical properties. So far, extensive investigations have been made surrounding surface and thermomechanical treatments, however, limited work has been done in the realm of surface functionalization to augment its performance in endodontics. This review summarizes the unique characteristics, current use, and latest developments in thermomechanically treated NiTi endodontic files. It discusses recent improvements in nano-engineering and the possibility of customizing the NiTi file surface for added functionalization. Whilst clinical translation of this technology has yet to be fully realized, future research direction will lie in the use of nanotechnology.

•

Nitinol (Nickel Titanium alloy) is widely used to clean/shape root canal system in endodontics.

•

To enhance its performance, various thermo-mechanical and nano-engineering modifications have been performed.

•

This comprehensive review summarizes the latest advances and future trends relating to functionalized NiTi endodontic files.

Cyclic fatigue resistance of EdgeTaper Platinum, Protaper Gold, and TruNatomy Prime rotary files before and after autoclave sterilization

Background

This in vitro investigation aimed to determine the influence of multiple autoclave cycles on the cyclic fatigue resistance of three heat-treated nickel-titanium (NiTi) files: EdgeTaper Platinum (ETP), ProTaper Gold (PTG), and TruNatomy Prime (TN).

Materials

Sixty NiTi files, twenty of each NiTi file type: ETP 25/.06, PTG 25/.08, and TN 26/.04 were randomly divided into four equal subgroups (n = 5). The files for the control group were left un-autoclaved. Different autoclave sterilization cycles (one, five, and ten) were used for the other three groups. The files were then placed in a metal canal block and rotated according to the manufacturer's instructions until fracture. The length of the broken segment and the time taken for fracture were measured. The fractured surfaces were subsequently subjected to SEM imaging. The Kruskal-Wallis test was used to analyze the data, followed by Dunn-Bonferroni pairwise comparisons. Statistical significance was set at p < 0.05.

Results

ETP showed significantly greater resistance to cyclic fatigue than TN in all autoclave groups and PTG after five autoclave cycles (p = 0.014). Fatigue resistance was not affected by the number of autoclaving cycles, except for ETP. After the first and tenth autoclaving cycles, they required significantly more rotations to failure than the non-sterilized files (p = 0.039 and p = 0.021, respectively). The fractured segments of the ETP files in these two groups were also longer than those in the control group (p = 0.010).

Conclusion

The cyclic fatigue resistance of ETP was greater than that of TN in all tested conditions. Repeated autoclave cycles of sterilization improved the cyclic fatigue resistance of the ETP files only and did not affect the cyclic fatigue resistance of TN and PTG. However, the ETP files separated at a longer distance from the tip with increased autoclaving cycles.

Undergraduate Endodontic Training and Its Relation to Contemporary Practice: Multicenter Cross-Sectional Study in Saudi Arabia

MATERIALS AND METHODS

An online questionnaire was developed and emailed to all dental schools in Saudi Arabia. This questionnaire was answered by the endodontic undergraduate program director. The data collected were analysed using descriptive statistics.

RESULTS

The response rate was 96.15%, which means twenty-five out of twenty-six dental schools participated in the study. The majority of the academic supervisors was endodontists (92%). The use of magnification and ultrasonic tips was not required by 84% and 76% of the dental schools, respectively. The main endodontic treatment techniques were the step-back technique and gates glidden for cleaning and shaping (76%) and cold lateral compaction for obturation (92%).

CONCLUSIONS

The dental students were supervised by endodontic specialists and trained to use traditional endodontic methods. Encouraging dental educators to train students to use modern technology and equipment would probably improve their graduate clinical skills and performance.

New heat-treated vs electropolished nickel-titanium instruments used in root canal treatment: Influence of autoclave sterilization on surface roughness

Nickel-titanium (NiTi) instruments used to treat root canal infections are affected by autoclave sterilization in various ways. The aim of this study was to compare the effect of autoclave sterilization on two NiTi rotary instruments that undergo different manufacturing treatments: The electro-polished Race and the heat-treated Race Evo, using scanning electron microscope analysis. In this in-vitro study, Race and Race-Evo instruments were subjected to a number of autoclaving cycles (0, 1, 3, 5, and 10). Scanning electron microscopy images were obtained at 3 mm from the tip of the file at 450x and 1000x magnifications. Surface roughness parameters were measured using ImageJ software. The results showed that autoclave sterilization caused a significant decrease in conventional NiTi Race surface roughness. While in Race Evo, surface roughness increased following the first autoclaving cycle. After 10 autoclaving cycles, surface roughness significantly decreased for both Race and Race Evo files.