Evolution of Mechanical Twinning during Cyclic Deformation of Mg-Zn-Ca Alloys

On the Corrosion Fatigue of Magnesium Alloys Aimed at Biomedical Applications: New Insights from the Influence of Testing Frequency and Surface Modification of the Alloy ZK60

Magnesium alloys are contemporary candidates for many structural applications of which medical applications, such as bioresorbable implants, are of significant interest to the community and a challenge to materials scientists. The generally poor resistance of magnesium alloys to environmentally assisted fracture, resulting, in particular, in faster-than-desired bio-corrosion degradation in body fluids, strongly impedes their broad uptake in clinical practice. Since temporary structures implanted to support osteosynthesis or healing tissues may experience variable loading, the resistance to bio-corrosion fatigue is a critical issue that has yet to be understood in order to maintain the structural integrity and to prevent the premature failure of implants. In the present communication, we address several aspects of the corrosion fatigue behaviour of magnesium alloys, using the popular commercial ZK60 Mg-Zn-Zr alloy as a representative example. Specifically, the effects of the testing frequency, surface roughness and metallic coatings are discussed in conjunction with the fatigue fractography after the testing of miniature specimens in air and simulated body fluid. It is demonstrated that accelerated environmentally assisted degradation under cyclic loading occurs due to a complicated interplay between corrosion damage, stress corrosion cracking and cyclic loads. The occurrence of corrosion fatigue in Mg alloys is exaggerated by the significant sensitivity to the testing frequency. The fatigue life or strength reduced remarkably with a decrease in the test frequency.

High Performance Fine-Grained Biodegradable Mg-Zn-Ca Alloys Processed by Severe Plastic Deformation

The tensile strength, fatigue, and corrosion fatigue performance of the magnesium alloy ZX40 benefit strongly from hybrid deformation processing involving warm equal-channel angular pressing (ECAP) at the first step and room temperature rotary swaging at the second. The general corrosion resistance improved as well, though to a lesser extent. The observed strengthening is associated with a combined effect of substantial microstructure refinement down to the nanoscale, reducing deformation twinning activity, dislocation accumulation, and texture transformation. The ultimate tensile strength and the endurance limit in the ultrafine-grained material reached or exceeded 380 and 120 MPa, respectively, which are remarkable values for this nominally low strength alloy.