Nicula LM, Manea DL, Simedru D, Cadar O, Dragomir ML, Ardelean I, Corbu O. Potential Role of GGBS and ACBFS Blast Furnace Slag at 90 Days for Application in Rigid Concrete Pavements. MATERIALS (BASEL, SWITZERLAND) 2023; 16:5902. [PMID: 37687595 PMCID: PMC10488527 DOI: 10.3390/ma16175902] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 07/31/2023] [Revised: 08/24/2023] [Accepted: 08/25/2023] [Indexed: 09/10/2023]
Abstract
Incorporating blast furnace slag into the composition of paving concrete can be one of the cost-effective ways to completely eliminate by-products from the pig iron production process (approximately 70% granulated slag and 30% air-cooled slag). The possibility to reintroduce blast furnace slag back into the life cycle will provide significant support to current environmental concerns and the clearance of tailings landfills. Especially in recent years, granulated and ground blast furnace slag (GGBS) as a substitute for cement and air-cooled blast furnace slag (ACBFS) aggregates as a substitute for natural aggregates in the composition of concretes have been studied by many researchers. But concrete compositions with large amounts of incorporated blast furnace slag affect the mechanical and durability properties through the interaction between the slag, cement and water depending on the curing times. This study focuses on identifying the optimal proportions of GGBS as a supplementary cementitious material (SCM) and ACBFS aggregates as a substitute to natural sand such that the performance at 90 days of curing the concrete is similar to that of the control concrete. In addition, to minimize the costs associated with grinding GGBS, the hydration activity index (HAI) of the GGBS, the surface morphology, and the mineral components were analyzed via X-ray diffraction, scanning electron microscopy (SEM), energy dispersive spectrometry (EDX), and nuclear magnetic resonance relaxometry (NMR). The flexural strength, the basic mechanical property of road concretes, increased from 28 to 90 days by 20.72% and 20.26% for the slag concrete but by 18.58% for the reference concrete. The composite with 15% GGBS and 25% ACBFS achieved results similar to the reference concrete at 90 days; therefore, they are considered optimal percentages to replace cement and natural sand in ecological pavement concretes. The HAI of the slag powder with a specific surface area equivalent to that of Portland cement fell into strength class 80 at the age of 28 days, but at the age of 90 days, the strength class was 100. The results of this research present three important benefits: the first is the protection of the environment through the recycling of two steel industry wastes that complies with European circular economy regulations, and the second is linked to the consequent savings in the disposal costs associated with wastefully occupied warehouses and the savings in slag grinding.
Collapse
Affiliation(s)
- Liliana Maria Nicula
- Faculty of Civil Engineering, Technical University of Cluj-Napoca, 28, Memorandumului, 400114 Cluj-Napoca, Romania; (D.L.M.); (M.L.D.)
- Faculty of Construction, Cadastre and Architecture, University of Oradea, 4, B.S. Delavrancea Street, 410058 Oradea, Romania
| | - Daniela Lucia Manea
- Faculty of Civil Engineering, Technical University of Cluj-Napoca, 28, Memorandumului, 400114 Cluj-Napoca, Romania; (D.L.M.); (M.L.D.)
| | - Dorina Simedru
- Research Institute for Analytical Instrumentation Subsidiary, National Institute for Research and Development for Optoelectronics INOE 2000, 67 Donath Street, 400293 Cluj-Napoca, Romania; (D.S.); (O.C.)
| | - Oana Cadar
- Research Institute for Analytical Instrumentation Subsidiary, National Institute for Research and Development for Optoelectronics INOE 2000, 67 Donath Street, 400293 Cluj-Napoca, Romania; (D.S.); (O.C.)
| | - Mihai Liviu Dragomir
- Faculty of Civil Engineering, Technical University of Cluj-Napoca, 28, Memorandumului, 400114 Cluj-Napoca, Romania; (D.L.M.); (M.L.D.)
| | - Ioan Ardelean
- Department of Physics and Chemistry, Technical University of Cluj-Napoca, 28, Memorandum Street, 400114 Cluj-Napoca, Romania;
| | - Ofelia Corbu
- Faculty of Civil Engineering, Technical University of Cluj-Napoca, 28, Memorandumului, 400114 Cluj-Napoca, Romania; (D.L.M.); (M.L.D.)
- Research Institute for Construction Equipment and Technology, ICECON S.A. Bucharest, 266, Pantelimon Road, 2nd District, CP 3-33, 021652 Bucharest, Romania
| |
Collapse
|
2
|
Effects of Temperature on the Leaching Behavior of Pb from Cement Stabilization/Solidification-Treated Contaminated Soil. SEPARATIONS 2022. [DOI: 10.3390/separations9120402] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 12/03/2022] Open
Abstract
Solidification/stabilization (S/S) is one of the most widely used techniques in the disposal of heavy-metal-contaminated soil, though the long-term effectiveness of S/S technology remains implicit. Temperature is an important factor affecting the leaching behavior of heavy metals and the long-term effectiveness of S/S treatment. This study systematically explored the influence of temperature on the leaching behavior of lead in an S/S monolith through semi-dynamic leaching test at different temperatures. The results showed that an increase in temperature could accelerate the leaching concentration and cumulative leaching amount of lead ions in the S/S monolith. The cumulative leaching amount of lead ions in the S/S monolith after 11 days at 55 °C was about 5.8 times that at 25 °C. The leaching rate of lead ions in the S/S monolith increased with the increase in temperature. The leaching index of lead ions was larger than 9, which met the requirements for “controlled utilization” in the environment. The leaching mechanism of lead ions was diffusion control and did not change in the temperature range of 25–55 °C. These findings indicate that temperature affects the leaching behavior and the long-term effectiveness of S/S treatment, and temperature variation should be considered in the effectiveness evaluation of S/S treatment.
Collapse
|