In-Situ Synthesis and Characterization of Nanocomposites in the Si-Ti-N and Si-Ti-C Systems

In Situ Formation of the TiCN Phase in SiBCN Ceramic Aerogels Enabling Superior Thermal and Structural Stability up to 1800 °C

Ceramic aerogels show excellent thermal insulation and functional performance for their unique nanoporous structure. However, conventional ceramic aerogels often undergo structural collapse and performance deterioration in high-temperature environments due to sintering, crystallization, and/or phase transition. Here, we designed a TiCN/SiBCN ceramic aerogel in which the TiCN phase was in situ formed through a carbothermal reaction during pyrolysis. Benefiting from its unique pearl-necklace-like structure, the TiCN/SiBCN aerogel exhibits a high specific surface area (248 m²/g), a low thermal conductivity (0.08 W/m·K), and a considerable compressive strength (2.2 MPa). The formation of a stable TiCN phase endows the aerogel with significant resistance to thermal decomposition and crystallization up to 1800 °C. Moreover, the TiCN/SiBCN aerogel retains high surface area and low thermal conductivity after thermal treatment, indicative of the stability and reliability of the nanoporous structure. The TiCN/SiBCN ceramic aerogel with superior thermal and structural stability is an ideal candidate for structural and functional applications in high-temperature environments.

Low temperature in situ immobilization of nanoscale fcc and hcp polymorphic nickel particles in polymer-derived Si-C-O-N(H) to promote electrocatalytic water oxidation in alkaline media

We synthesized nickel (Ni) nanoparticles (NPs) in a high specific surface area (SSA) p-block element-containing inorganic compound prepared via the polymer-derived ceramics (PDC) route to dispatch the obtained nanocomposite towards oxygen evolution reaction (OER). The in situ formation of Ni NPs in an amorphous silicon carboxynitride (Si-C-O-N(H)) matrix is allowed by the reactive blending of a polysilazane, NiCl₂ and DMF followed by the subsequent thermolysis of the Ni : organosilicon polymer coordination complex at a temperature as low as 500 °C in flowing argon. The final nanocomposite displays a BET SSA as high as 311 m² g^-1 while the structure of the NPs corresponds to face-centred cubic (fcc) Ni along with interstitial-atom free (IAF) hexagonal close-packed (hcp) Ni as revealed by XRD. A closer look into the compound through FEG-SEM microscopy confirms the formation of pure metallic Ni, while HR-TEM imaging reveals the occurrence of Ni particles featuring a fcc phase and surrounded by carbon layers; thus, forming core-shell structures, along with Ni NPs in an IAF hcp phase. By considering that this newly synthesized material contains only Ni without doping (e.g., Fe) with a low mass loading (0.15 mg cm^-2), it shows promising OER performances with an overpotential as low as 360 mV at 10 mA cm^-2 according to the high SSA matrix, the presence of the IAF hcp Ni NPs and the development of core-shell structures. Given the simplicity, the flexibility, and the low cost of the proposed synthesis approach, this work opens the doors towards a new family of very active and stable high SSA nanocomposites made by the PDC route containing well dispersed and accessible non-noble transition metals for electrocatalysis applications.

Mechanistic Investigation of the Formation of Nickel Nanocrystallites Embedded in Amorphous Silicon Nitride Nanocomposites

Herein, we report the mechanistic investigation of the formation of nickel (Ni) nanocrystallites during the formation of amorphous silicon nitride at a temperature as low as 400 °C, using perhydropolysilazane (PHPS) as a preformed precursor and further coordinated by nickel chloride (NiCl₂); thus, forming the non-noble transition metal (TM) as a potential catalyst and the support in an one-step process. It was demonstrated that NiCl₂ catalyzed dehydrocoupling reactions between Si-H and N-H bonds in PHPS to afford ternary silylamino groups, which resulted in the formation of a nanocomposite precursor via complex formation: Ni(II) cation of NiCl₂ coordinated the ternary silylamino ligands formed in situ. By monitoring intrinsic chemical reactions during the precursor pyrolysis under inert gas atmosphere, it was revealed that the Ni-N bond formed by a nucleophilic attack of the N atom on the Ni(II) cation center, followed by Ni nucleation below 300 °C, which was promoted by the decomposition of Ni nitride species. The latter was facilitated under the hydrogen-containing atmosphere generated by the NiCl₂-catalyzed dehydrocoupling reaction. The increase of the temperature to 400 °C led to the formation of a covalently-bonded amorphous Si₃N₄ matrix surrounding Ni nanocrystallites.