Innovative and Cost-Efficient BiOI Immobilization Technique on Ceramic Paper-Total Coverage and High Photocatalytic Activity

Effects of high pressure on the lattice structure and electrical transport properties of BiOI

To reveal the pressure effects on BiOX semiconductors, we performed in-situ Raman spectroscopy and electrical transport measurements on BiOI up to 26.1 GPa and 19.2 GPa. BiOI showed good structural stability, while the electron conduction characteristics maintained dominance throughout the pressure range. The influence of grain boundary conduction disappeared at pressures above 9.2 GPa. With pressure elevation, the pressure-induced lattice fragmentation and grain refinement introduced a large number of relevant levels in the energy gap and resulted in a significant increase in the conductivity of BiOI under compression. The conductivity increased by 10⁶ at 19.2 GPa from the initial value and maintained an increase of 10² after depressurization until ambient conditions were attained. At the same time, the space charge polarization of the crystal interface layer became weaker with pressure elevation resulting in a decrease in the relative permittivity of BiOI. The calculation results of the complex permittivity showed that the frequency of orientation polarization response decreases with pressure elevation, and the complex permittivity becomes constant in the high-frequency region. Our work proves that pressure could significantly increase the carrier concentration and mobility, thus effectively improving the conductivity of BiOX semiconductors.

The boosted activity of AgI/BiOI nanocatalyst: a RSM study towards Eriochrome Black T photodegradation

Nowadays, critical environmental pollution needs some novel, simple, effective, and cost-effective catalysts with high efficiency in the visible region of the light. Thus, the AgI/BiOI coupled nanocatalyst sample (CS) was prepared and briefly characterized. The pH_pzc values of 6.2, 5.4, and 4.5 were estimated for AgI, BiOI, and AgI/BiOI samples. Based on the PXRD results, average crystallite sizes of 35.2, 34.7, and 34.1 nm were obtained for AgI, BiOI, and AgI/BiOI samples from the Scherrer formula and 38.3, 25.6, and 25.6 nm by the Williamson-Hall formula. SEM image confirmed a sheet-like BiOI morphology covered by AgI nanoparticles. The simultaneous interactions of the influencing variables on the boosted photocatalytic activity of CS sample towards Eriochrome Black T (EBT) were evaluated by response surface methodology (RSM) (under 100-W tungsten lamp irradiation with 230 mW/m².nm irradiance). The goodness of the model was confirmed by the significance of the model (F value of 65.68 > F_{0.05, 14, 13} = 2.55) and a non-significant LOF (F value of 0.97 < F_{0.05, 10, 3} = 8.79) at a 95% confidence interval obtained in ANOVA analysis of the results. The center point runs have the following conditions: catalyst dose: 0.68 g/L; pH: 7.5; C_EBT: 7.25 mg/L; and irradiation time: 53.5 min, while the optimal run included the following conditions: catalyst dose: 1.0 g/L; pH: 4; C_EBT: 10 mg/L; and irradiation time: 80 min. About 95% of EBT molecules were degraded in the optimal conditions.

A readily synthesized bismuth oxyiodide/attapulgite for the photodegradation of tetracycline under visible light irradiation

Bismuth oxyiodide and attapulgite have proven to be potential materials for the removal of emerging contaminants in wastewater.