Ultra-Stable Potassium Ion Storage of Nitrogen-Doped Carbon Nanofiber Derived from Bacterial Cellulose

Design of reduced graphene oxide coating carbon sub-microspheres hierarchical nanostructure for ultra-stable potassium storage performance

The development of high-performance carbon-based anode materials is still a significant challenge for K-ion storage. In our work, we designed reduced graphene oxide coating carbon sub-microspheres hierarchical nanostructure (CS@RGO) hierarchical nanostructure via a simple freeze-drying and subsequent pyrolysis as anode for K-ion batteries (KIBs), which presented an excellent electrochemical performance for K-ion storage, with a reversible specific capacity of 295 mAh g^-1 after 100 cycles at 100 mAh g^-1. Even at a high current density of 1 A g^-1, our CS@RGO still achieves ultra-stable K-ion storage of 200 mAh g^-1 at 1 A g^-1 after 5000 cycles almost without capacity fade. According to the galvanostatic intermittent titration technique result, the CS@RGO hybrid receives a high average diffusion coefficient of 7.35 × 10^-8 cm² s^-1, contributing to the rapid penetration of K-ion, which facilitates the enhancement of electrochemical performance for KIBs. Besides, we also use Raman spectra to investigate the electrochemical behavior of our CS@RGO hybrid for K-ion storage and confirm the reaction process. We believe that our work will offer the opportunity to enable ultra-stable carbon-based materials by the structure design in the K-ion battery field.

Insight into a Nitrogen-Doping Mechanism in a Hard-Carbon-Microsphere Anode Material for the Long-Term Cycling of Potassium-Ion Batteries

To investigate the alternatives to lithium-ion batteries, potassium-ion batteries have attracted considerable interest due to the cost-efficiency of potassium resources and the relatively lower standard redox potential of K⁺/K. Among various alternative anode materials, hard carbon has the advantages of extensive resources, low cost, and environmental protection. In the present study, we synthesize a nitrogen-doping hard-carbon-microsphere (N-SHC) material as an anode for potassium-ion batteries. N-SHC delivers a high reversible capacity of 248 mAh g⁻¹ and a promoted rate performance (93 mAh g⁻¹ at 2 A g⁻¹). Additionally, the nitrogen-doping N-SHC material also exhibits superior cycling long-term stability, where the N-SHC electrode maintains a high reversible capacity at 200 mAh g⁻¹ with a capacity retention of 81% after 600 cycles. DFT calculations assess the change in K ions’ absorption energy and diffusion barriers at different N-doping effects. Compared with an original hard-carbon material, pyridinic-N and pyrrolic-N defects introduced by N-doping display a positive effect on both K ions’ absorption and diffusion.

O-Doping Configurations Reduce the Adsorption Energy Barrier of K-Ions to Improve the Electrochemical Performance of Biomass-Derived Carbon

In recent years, atomic-doping has been proven to significantly improve the electrochemical performance of biomass-derived carbon materials, which is a promising modification strategy. Among them, there are relatively few reports about O-doping. Here, porous carbon derived from orange peel was prepared by simple carbonization and airflow-annealing processes. Under the coordination of microstructure and surface groups, the derived carbon had excellent electrochemical performance for the K-ion batteries’ anode, including a high reversible specific capacity of 320.8 mAh/g, high rate performance of 134.6 mAh/g at a current density of 2000 mA/g, and a retention rate of 79.5% even after 2000 long-term cycles, which shows great application potential. The K-ion storage mechanisms in different voltage ranges were discussed by using various characterization techniques, that is, the surface adsorbed of K-ionswas in the high-potential slope area, and the intercalation behavior corresponded to the low-potential quasi-plateau area. In addition, the density functional theory calculations further confirmed that O-doping can reduce the adsorption energy barrier of K-ions, change the charge density distribution, and promote the K-ion storage. In particular, the surface Faraday reaction between the C=O group and K-ions plays an important role in improving the electrochemical properties.

Polydopamine Doping and Pyrolysis of Cellulose Nanofiber Paper for Fabrication of Three-Dimensional Nanocarbon with Improved Yield and Capacitive Performances

Biomass-derived three-dimensional (3D) porous nanocarbons have attracted much attention due to their high surface area, permeability, electrical conductivity, and renewability, which are beneficial for various electronic applications, including energy storage. Cellulose, the most abundant and renewable carbohydrate polymer on earth, is a promising precursor to fabricate 3D porous nanocarbons by pyrolysis. However, the pyrolysis of cellulosic materials inevitably causes drastic carbon loss and volume shrinkage. Thus, polydopamine doping prior to the pyrolysis of cellulose nanofiber paper is proposed to fabricate the 3D porous nanocarbons with improved yield and volume retention. Our results show that a small amount of polydopamine (4.3 wt%) improves carbon yield and volume retention after pyrolysis at 700 °C from 16.8 to 26.4% and 15.0 to 19.6%, respectively. The pyrolyzed polydopamine-doped cellulose nanofiber paper has a larger specific surface area and electrical conductivity than cellulose nanofiber paper that without polydopamine. Owing to these features, it also affords a good specific capacitance up to 200 F g⁻¹ as a supercapacitor electrode, which is higher than the recently reported cellulose-derived nanocarbons. This method provides a pathway for the effective fabrication of high-performance cellulose-derived 3D porous nanocarbons.