Structure of Coal-Derived Metal-Supported Few-Layer Graphene Composite Materials Synthesized Using a Microwave-Assisted Catalytic Graphitization Process

Fabrication and Microwave Absorption Properties of Core-Shell Structure Nanocomposite Based on Modified Anthracite Coal

Microwave-absorbing materials have attracted extensive attention due to the development of electronic countermeasures. In this study, novel nanocomposites with core-shell structures based on the core of Fe-Co nanocrystals and the shell of furan methylamine (FMA)-modified anthracite coal (Coal-F) were designed and fabricated. The Diels-Alder (D-A) reaction of Coal-F with FMA creates a large amount of aromatic lamellar structure. After the high-temperature treatment, the modified anthracite with a high degree of graphitization showed an excellent dielectric loss, and the addition of Fe and Co effectively enhanced the magnetic loss of the obtained nanocomposites. In addition, the obtained micro-morphologies proved the core-shell structure, which plays a significant role in strengthening the interface polarization. As a result, the combined effect of the multiple loss mechanism promoted a remarkable improvement in the absorption of incident electromagnetic waves. The carbonization temperatures were specifically studied through a setting control experiment, and 1200 °C was proved to be the optimum parameter to obtain the best dielectric loss and magnetic loss of the sample. The detecting results show that the 10 wt.% CFC-1200/paraffin wax sample with a thickness of 5 mm achieves a minimum reflection loss of -41.6 dB at a frequency of 6.25 GHz, indicating an excellent microwave absorption performance.

Biomass derived reduced-graphene-oxide supported α-Fe2O3/ZnO S-scheme heterostructure: Robust photocatalytic wastewater remediation

The emergence of new diseases and the unplanned industrialization of cities have led to new diseases and the subsequent use of antibiotics. Hence the remediation of wastewater containing antibiotics and their severe pollution has raised serious concerns in recent years. Herein coral-shaped α-Fe₂O₃/ZnO/reduced graphene oxide (r-GO)-like carbon heterojunction in-situ were prepared from basil seed as a sustainable biomass resource and applied for the photodegradation of the oxytetracycline (OTC) as a typical antibiotic in a helical plug flow photoreactor (HPFPR) via persulfate activation under visible light irradiation. Spectroscopy and electrochemical results confirmed the tunable band structure and quick light absorption, superior charge separation and transfer, satisfactory charge carrier lifetime, and long-term stability for the prepared photocatalyst. The 98% degradation efficiency was achieved for OTC within 90 min fitted by a first-order kinetic model with the rate constant of 0.1248 min^-1. The finding proves that HPFPR exhibited a higher degradation rate of OTC by 2.3 times compared to the batch reactor. The 3D computational fluid dynamics (CFD) model confirmed the outstanding performance of the HPFPR. Scavenging experiments integrated with mott Schottky and DRS results revealed that rGO intensifies the S-scheme charge carrier transfer and built-in electric field and reduces the recombination. Finally, this work has substantial potential for the in-situ synthesis of environmental-friendly and large-scale metal oxide heterojunctions in natural carbon supports as well as scale-up and gives novel insights from molecular and engineering points of view into the wastewater remediation processes and clean water production.

Study on Structural Evolution of Synthetic Graphite Derived from Lignite Prepared by High Temperature–High Pressure Method

Abundant and cheap lignite is regarded as inferior fuel due to its disadvantages such as low heat and high moisture. In order to realize the high value and clean, non-fuel utilization of lignite, we used lignite as precursor to prepare high-quality synthetic graphite through graphitization treatment using the high temperature–high pressure (HTHP) method, and afterwards characterized the samples by XRD, Raman, FTIR, SEM-EDS, and HRTEM, and systematically analyzed the effect of P-T conditions on the structure evolution of lignite. Our results demonstrated that temperature dominates the graphitization of lignite, and high pressure accelerates the graphitization process of lignite. Under HTHP treatment, the aromatic layer of lignite accelerates directional rearrangement; the ordered domain increases rapidly, and the ductility and stacking degree of the carbon sheets of the lignite sample are greatly enhanced. Compared with the traditional high-temperature graphitization method, the HTHP method greatly reduces the graphitization temperature and shortens the graphitization time. Remarkably, the as-prepared graphite with a graphitization degree of 91.87% superior to graphite fabricated by the conventional high-temperature processing were rapidly prepared from lignite at 6 GPa and 1300 °C in 20 min. This study demonstrates that the HTHP method is a feasible and effective method to realize the green, efficient, and high value utilization of lignite.

Structural Investigation of the Synthesized Few-Layer Graphene from Coal under Microwave

This study focused on the structural investigation of few-layer graphene (FLG) synthesis from bituminous coal through a catalytic process under microwave heat treatment (MW). The produced FLG has been examined by Raman spectroscopy, XRD, TEM, and AFM. Coal was activated using the potassium hydroxide activation process. The FLG synthesis processing duration was much faster requiring only 20 min under the microwave radiation. To analyse few-layer graphene samples, we considered the three bands, i.e., D, G, and 2D, of Raman spectra. At 1300 °C, the P10% Fe sample resulted in fewer defects than the other catalyst percentages sample. The catalyst percentages affected the structural change of the FLG composite materials. In addition, the Raman mapping showed that the catalyst loaded sample was homogeneously distributed and indicated a few-layer graphene sheet. In addition, the AFM technique measured the FLG thickness around 4.5 nm. Furthermore, the HRTEM images of the P10% Fe sample contained a unique morphology with 2–7 graphitic layers of graphene thin sheets. This research reported the structural revolution with latent feasibility of FLG synthesis from bituminous coal in a wide range.

Microwave-Assisted Coal-Derived Few-Layer Graphene as an Anode Material for Lithium-Ion Batteries

A few-layer graphene (FLG) composite material was synthesized using a rich reservoir and low-cost coal under the microwave-assisted catalytic graphitization process. X-ray diffraction, Raman spectroscopy, transmission electron microscopy, and X-ray photoelectron spectroscopy were used to evaluate the properties of the FLG sample. A well-developed microstructure and higher graphitization degree were achieved under microwave heating at 1300 °C using the S5% dual (Fe-Ni) catalyst for 20 min. In addition, the synthesized FLG sample encompassed the Raman spectrum 2D band at 2700 cm-1, which showed the existence of a few-layer graphene structure. The high-resolution TEM (transmission electron microscopy) image investigation of the S5% Fe-Ni sample confirmed that the fabricated FLG material consisted of two to seven graphitic layers, promoting the fast lithium-ion diffusion into the inner surface. The S5% Fe-Ni composite material delivered a high reversible capacity of 287.91 mAhg-1 at 0.1 C with a higher Coulombic efficiency of 99.9%. In contrast, the single catalyst of S10% Fe contained a reversible capacity of 260.13 mAhg-1 at 0.1 C with 97.96% Coulombic efficiency. Furthermore, the dual catalyst-loaded FLG sample demonstrated a high capacity-up to 95% of the initial reversible capacity retention-after 100 cycles. This study revealed the potential feasibility of producing FLG materials from bituminous coal used in a broad range as anode materials for lithium-ion batteries (LIBs).