Mono-Doped and Co-Doped Nanostructured Hematite for Improved Photoelectrochemical Water Splitting

Evaluation of the Efficiency of Photoelectrochemical Activity Enhancement for the Nanostructured LaFeO3 Photocathode by Surface Passivation and Co-Catalyst Deposition

Perovskite-type lanthanum iron oxide, LaFeO₃, is a promising photocathode material that can achieve water splitting under visible light. However, the performance of this photoelectrode material is limited by significant electron-hole recombination. In this work, we explore different strategies to optimize the activity of a nanostructured porous LaFeO₃ film, which demonstrates enhanced photoelectrocatalytic activity due to the reduced diffusion length of the charge carriers. We found that surface passivation is not an efficient approach for enhancing the photoelectrochemical performance of LaFeO₃, as it is sufficiently stable under photoelectrocatalytic conditions. Instead, the deposition of a Pt co-catalyst was shown to be essential for maximizing the photoelectrochemical activity both in hydrogen evolution and oxygen reduction reactions. Illumination-induced band edge unpinning was found to be a major challenge for the further development of LaFeO₃ photocathodes for water-splitting applications.

Facile Zn and Ni Co-Doped Hematite Nanorods for Efficient Photocatalytic Water Oxidation

In this work, we report the effect of zinc (Zn) and nickel (Ni) co-doping of hydrothermally synthesized hematite nanorods prepared on fluorine-doped tin oxide (FTO) substrates for enhanced photoelectrochemical (PEC) water splitting. Seeded hematite nanorods (NRs) were facilely doped with a fixed concentration of 3 mM Zn and varied concentrations of 0, 3, 5, 7, and 9 mM Ni. The samples were observed to have a largely uniform morphology of vertically aligned NRs with slight inclinations. The samples showed high photon absorption within the visible spectrum due to their bandgaps, which ranged between 1.9-2.2 eV. The highest photocurrent density of 0.072 mA/cm2 at 1.5 V vs. a reversible hydrogen electrode (RHE) was realized for the 3 mM Zn/7 mM Ni NRs sample. This photocurrent was 279% higher compared to the value observed for pristine hematite NRs. The Mott-Schottky results reveal an increase in donor density values with increasing Ni dopant concentration. The 3 mM Zn/7 mM Ni NRs sample produced the highest donor concentration of 2.89 × 1019 (cm-3), which was 2.1 times higher than that of pristine hematite. This work demonstrates the role of Zn and Ni co-dopants in enhancing the photocatalytic water oxidation of hematite nanorods for the generation of hydrogen.

Large Two-Magnon Raman Hysteresis Observed in a Magnetically Uncompensated Hematite Coating across the Morin Transition

A temperature-dependent Raman experiment between 80 and 600 K was performed in a nanoparticulated coating of single-phase hematite grown on a silica substrate. In that range, a thermal Raman shift hysteresis was identified in the vibrational modes that accompanies the Morin transition, observing large effects in the two-magnon Raman frequency position and in its relative intensity. Interestingly, no decrease in coercivity occurs when the hematite crosses the Morin transition below 230 K. The spin-flop processes produced in the coating leads to a strong decompensation of the surface spins, generating a ferromagnetic component over the whole temperature range studied. Such unusual effects might be promoted by a certain degree of structural disorder and the stresses produced by the nanoparticulation growth approach of the hematite coating. As a result, a high stability of the two-magnon excitation is obtained over a wide temperature range and considerable advances are made for the development of spintronic devices based on semiconductor antiferromagnetic materials.