Tailoring the Performance of Graphene Aerogels for Oil/Organic Solvent Separation by 1-Step Solvothermal Approach

Ultralight, Mechanically Enhanced, and Thermally Improved Graphene-Cellulose-Polyethyleneimine Aerogels for the Adsorption of Anionic and Cationic Dyes

Graphene-cellulose-polyethyleneimine aerogels (GA-MCC-PEI) were prepared using a simple, environmentally friendly method to remove anionic and cationic dyes in water. Graphene-cellulose hydrogels were prepared using a hydrothermal method and then immersed in a polyethyleneimine aqueous solution for 48 h to obtain graphene-cellulose-polyethyleneimine hydrogels, which were then freeze-dried. The light and porous composite aerogels had a good compression resistance, and the maximum allowable pressure of the graphene-cellulose-polyethyleneimine aerogel with a cellulose content of 43% was 21.76 kPa, which was 827 times its weight. Adsorption of the anionic dye amaranth and the cationic dye methylene blue by the graphene-cellulose-polyethyleneimine aerogel was satisfactorily modeled using the Langmuir isothermal equation, indicating monolayer adsorption. When the cellulose content was 39%, the equilibrium adsorption capacities of the composite aerogel for amaranth and methylene blue were 369.37 mg/g and 237.33 mg/g, respectively. This graphene-cellulose-polyethyleneimine aerogel can be used to remove dye pollutants in water to maintain ecological balance, thus broadening the application space of aerogel materials, that is, as adsorbents in different environments.

Hydrothermal-Freeze-Casting of Poly(amidoamine)-Modified Graphene Aerogels towards CO2 Adsorption

This article presents novel poly(amidoamine) (PAMAM) dendrimer-modified with partially-reduced graphene oxide (rGO) aerogels, obtained using the combined solvothermal synthesis-freeze-casting approach. The properties of modified aerogels are investigated with varying synthesis conditions, such as dendrimer generation (G), GO:PAMAM wt. ratio, solvothermal temperature, and freeze-casting rate. Scanning electron microscopy, Fourier Transform Infrared spectroscopy, Raman spectroscopy, X-ray photoelectron spectroscopy are employed to characterize the aerogels. The results indicate a strong correlation of the synthesis conditions with N content, N/C ratio, and nitrogen contributions in the modified aerogels. Our results show that the best CO₂ adsorption performance was exhibited by the aerogels modified with higher generation (G7) dendrimer at low GO:PAMAM ratio as 2:0.1 mg mL⁻¹ and obtained at higher solvothermal temperature and freeze-casting in liquid nitrogen. The enclosed results are indicative of a viable approach to modify graphene aerogels towards improving the CO₂ capture.

Review on synthesis of three-dimensional graphene skeletons and their absorption performance for oily wastewater

Water pollution is a global environmental problem that affects the ecosystem severely. Treatment of oily wastewater and organic pollutants is a major challenge that waits to be solved as soon as possible. Adsorbing is one of the most effective strategies to deal with this problem. Three-dimensional (3D) porous adsorbents made of graphene or graphene-based nanomaterials skeletons had attracted more attention in wastewater treatment because of their large surface area, high porosity, low density, high chemical/thermal stability, and steady mechanical properties, which allow different pollutants to easily access and diffuse into 3D networks of adsorbents. This work presents an extensive summarization of recent progress in the synthesis methodologies and microstructures of 3D graphene foams and 3D graphene-based foams and highlights their adsorption performance for oils and organic solvents. Advantages and disadvantages of various preparation strategies are compared and the corresponded structures of these skeletons are studied in detail. Furthermore, the effects of the structures on oil-adsorption properties are analyzed and some data and parameters of the oil-adsorption properties are listed and studied for easier comparison. At last, the future research directions and technical challenges are prospected, which is hoped that the researchers will be inspired to develop the new graphene-based adsorbents.

From 2D Graphene Nanosheets to 3D Graphene-based Macrostructures

The combination of exceptional functionalities offered by 3D graphene-based macrostructures (GBMs) has attracted tremendous interest. 2D graphene nanosheets have a high chemical stability, high surface area and customizable porosity, which was extensively researched for a variety of applications including CO₂ adsorption, water treatment, batteries, sensors, catalysis, etc. Recently, 3D GBMs have been successfully achieved through few approaches, including direct and non-direct self-assembly methods. In this review, the possible routes used to prepare both 2D graphene and interconnected 3D GBMs are described and analyzed regarding the involved chemistry of each 2D/3D graphene system. Improvement of the accessible surface of 3D GBMs where the interface exchanges are occurring is of great importance. A better control of the chemical mechanisms involved in the self-assembly mechanism itself at the nanometer scale is certainly the key for a future research breakthrough regarding 3D GBMs.

Highly elastic, electroconductive, immunomodulatory graphene crosslinked collagen cryogel for spinal cord regeneration

Novel amino-functionalized graphene crosslinked collagen based nerve conduit having appropriate electric (3.8 ± 0.2 mSiemens/cm) and mechanical cues (having young modulus value of 100-347 kPa) for stem cell transplantation and neural tissue regeneration was fabricated using cryogelation. The developed conduit has shown sufficiently high porosity with interconnectivity between the pores. Raman spectroscopy analysis revealed the increase in orderliness and crosslinking of collagen molecules in the developed cryogel due to the incorporation of amino-functionalized graphene. BM-MSCs grown on graphene collagen cryogels have shown enhanced expression of CD90 and CD73 gene upon electric stimulation (100 mV/mm) contributing towards maintaining their stemness. Furthermore, an increased secretion of ATP from BM-MSCs grown on graphene collagen cryogel was also observed upon electric stimulation that may help in regeneration of neurons and immuno-modulation. Neuronal differentiation of BM-MSCs on graphene collagen cryogel in the presence of electric stimulus showed an enhanced expression of MAP-2 kinase and β-tubulin III. Immunohistochemistry studies have also demonstrated the improved neuronal differentiation of BM-MSCs. BM-MSCs grown on electro-conductive collagen cryogels under inflammatory microenvironment in vitro showed high indoleamine 2,3 dioxygenase activity. Moreover, macrophages cells grown on graphene collagen cryogels have shown high CD206 (M2 polarization marker) and CD163 (M2 polarization marker) and low CD86 (M1 polarization marker) gene expression demonstrating M2 polarization of macrophages, which may aid in tissue repair. In an organotypic culture, the developed cryogel conduit has supported cellular growth and migration from adult rat spinal cord. Thus, this novel electro-conductive graphene collagen cryogels have potential for suppressing the neuro-inflammation and promoting the neuronal cellular migration and proliferation, which is a major barrier during the spinal cord regeneration.