One-Pot Preparation of Hydrophilic Polylactide Porous Scaffolds by Using Safe Solvent and Choline Taurinate Ionic Liquid

Wetting of Superhydrophobic Polylactic Acid Micropillared Patterns

Superhydrophobic (SH) polylactic acid (PLA) surfaces were previously produced by various methods and used especially in biomedical applications and oil/water separation processes after 2008. However, the wettability of SH-PLA patterns containing micropillars has not been investigated before. In this study, PLA patterns having regular microstructured pillars with 12 different pillar diameters and pillar-to-pillar distances were prepared by hot pressing pre-flattened PLA sheets onto preformed polydimethylsiloxane (PDMS) soft molds having micro-sized pits. PDMS templates were previously prepared by photolithography using SU-8 molds. Apparent, advancing, and receding water contact angle measurements were carried out on the PLA patterns containing micropillars, and the morphology of the patterns was examined by optical and SEM microscopy. The largest contact angle obtained without the surface modification of the pure PLA pattern was 139°. Then, PLA micropatterns were hydrophobized using three types of silanes via chemical vapor deposition method, and SH-PLA patterns were obtained having θs of up to 167°. It was found that the highest θ values could be obtained when PLA pattern samples were coated with a silane containing a fluorine atom in its chemical structure. Washing and service life stability tests were also performed on the coated pattern samples and all of the silane coatings on the PLA patterns were found to be resistant over a 6 month period.

Synthesis of Novel Hyaluronic Acid Sulfonated Hydrogels Using Safe Reactants: A Chemical and Biological Characterization

Here, we present a one-pot procedure for the preparation of hyaluronic acid (HA) sulfonated hydrogels in aqueous alkaline medium. The HA hydrogels were crosslinked using 1,4-butanedioldiglycidyl ether (BDDE) alone, or together with N-bis(2-hydroxyethyl)-2-aminoethanesulfonic acid (Bes), as a safe sulfonating agent. Conditions for the simultaneous reaction of HA with BDDE and Bes were optimized and the resulting hydrogels were characterized under different reaction times (24, 72, and 96 h). The incorporation of sulfonic groups into the HA network was proven by elemental analysis and FTIR spectroscopy and its effect on water uptake was evaluated. Compared with the non-sulfonated sample, sulfonated gels showed improved mechanical properties, with their compressive modulus increased from 15 to 70 kPa, higher stability towards hyaluronidase, and better biocompatibility to 10T1/2 fibroblasts, especially after the absorption of collagen. As main advantages, the procedure described represents an easy and reproducible methodology for the fabrication of sulfonated hydrogels, which does not require toxic chemicals and/or solvents.