Fabrication and Performance of Composite Microencapsulated Phase Change Materials with Palmitic Acid Ethyl Ester as Core

Preparation of High Thermo-Stability and Compactness Microencapsulated Phase Change Materials with Polyurea/Polyurethane/Polyamine Three-Composition Shells through Interfacial Polymerization

In the preparation of microencapsulated phase change materials (MicroPCMs) with a three-composition shell through interfacial polymerization, the particle size, phase change behaviors, core contents, encapsulation efficiency morphology, thermal stability and chemical structure were investigated. The compactness of the MicroPCMs was analyzed through high-temperature drying and weighing. The effect of the core/shell ratio and stirring rate of the system was studied. The results indicated that the microcapsules thus-obtained possessed a spherical shape and high thermal stability and the surfaces were intact and compact. Furthermore, in the emulsification stage, the stirring speed had a significant influence on the microcapsules' particle size, and smaller particles could be obtained under the higher stirring speed, and the distributions were more uniform in these cases. When the core/shell ratio was lower than 4, both the core content and the encapsulation efficiency was high. Additionally, when the core/shell ratio was higher than 4, the encapsulation efficiency was decreased significantly. The three-composition shell greatly increased the compactness of microcapsules, and when the core/shell ratio was adjusted to 3, the mass loss of the MicroPCMs was lower than 6% after drying at 120 °C for 1 h. After the microencapsulation, double exothermic peaks appeared on the crystallization curve of the MicroPCMs, the crystallization mechanism was changed from the heterogeneous nucleation to the homogeneous nucleation and the super cooling degree was enhanced.

Methods for Determining the Thermal Transfer in Phase-Changing Materials (PCMs)

A very important issue that needs to be solved as simply and correctly as possible is how to establish the thermal performance of phase-changing materials (PCM). The undertaken researches have analyzed the values of the thermal performances of the PCM taking into account the method of finite elements and the experimental research, respectively, based on a modern measurement system that was designed and implemented. Butyl stearate which has been encapsulated through complex coacervation in polymethyl methacrylate has been used as a PCM. Samples were made containing 10%, 20%, 30% and 40% PCM, respectively, within their structure. The research has established that at both the hot plate and the cold plate interface, the evolution of the temperature over time, established by both the finite element method (FEM) and experimental research, are quite close, and the best results have been obtained for the P30 sample. A very important thing observed during the finite element method (FEM) is that the simulated thermal flow variation extends between 2700-3110W/m² being small enough not to influence the temperature measurement at the interface of hot or cold plates. Thus, the use of the FEM or the experimental research method can be applied with good results, provided that the correct initial conditions are used in the finite element method and that the experimental research is performed using the best possible apparatus.

Rheological Issues of Phase Change Materials Obtained by the Complex Coacervation of Butyl Stearate in Poly Methyl Methacrylate Membranes

The research started from the fact that the coacervation process represents the process of formation of macromolecular aggregates after separation from the phase that takes place in a homogeneous polymer solution as a result of the addition of a non-solvent. This process is very complex, and takes place in several stages of emulsification technology. The first step of the research created a sample through an encapsulation process of complex coacervation, followed by the creation of three different samples with specific emulsification technologies. Each resulting sample and step of emulsification went through rheological analysis, including the development of evolutions of the complex viscosity, loss module and respective storage module. When we analyzed the rheological properties of each sample at different emulsification stages, we reached the conclusion that, at the moment when the polymerization reaction develops the methyl methacrylate (MMA), the loss modules of the samples were stronger than the storage modules. In this context, the emulsification technology strongly influenced the process of forming the polymethyl methacrylate (PMMA) layer over the butyl stearate particles. In addition, in order to obtain the corresponding microcapsules, it was preferable for the butyl stearate particles covered with MMA to be vigorously stirred in a short period of time, under 250 s, because after that the polymerization process of the MMA on the surface of the particles begins. When producing microcapsules, it is very important that the whole process of emulsification be accompanied by rigorous stirring.