The Formation of a Highly Oriented Structure and Improvement of Properties in PP/PA6 Polymer Blends during Extrusion-Stretching

Scalable Continuous Manufacturing Process of Stereocomplex PLA by Twin-Screw Extrusion

A scalable continuous manufacturing method to produce stereocomplex PLA was developed and optimized by melt-blending a 1:1 blend of high molecular weight poly(L-lactide) (PLLA) and high molecular weight poly(D-lactide) (PDLA) in a co-rotating twin-screw extruder. Thermal characteristics of stereocomplex formation were characterized via DSC to identify the optimal temperature profile and time for processing stereocomplex PLA. At the proper temperature window, high stereocomplex formation is achieved as the twin-screw extruder allows for alignment of the chains; this is due to stretching of the polymer chains in the extruder. The extruder processing conditions were optimized and used to produce >95% of stereocomplex PLA conversion (melting peak temperature Tpm = 240 °C). ATR-FTIR depicts the formation of stereocomplex crystallites based on the absorption band at 908 cm-1 (β helix). The only peaks observed for stereocomplex PLA's WAXD profile were at 2θ values of 12, 21, and 24°, verifying >99% of stereocomplex formation. The total crystallinity of stereocomplex PLA ranges from 56 to 64%. A significant improvement in the tensile behavior was observed in comparison to the homopolymers, resulting in a polymer of high strength and toughness. These results lead us to propose stereocomplex PLA as a potential additive/fiber that can reinforce the material properties of neat PLA.

The Entangled Conductive Structure of CB/PA6/PP MFCs and Their Electromechanical Properties

In this work, carbon black (CB)/polyamide 6 (PA6)/polypropylene (PP) microfibrillar composites (MFCs) were fabricated through an extrusion (hot stretching) heat treatment process. The CB-coated conductive PA6 microfibrils with high aspect ratio were in situ generated as a result of the selective accumulation of CB at the interface. At the proper temperature, a 3D entangled conductive structure was constructed in the PP matrix, due to topological entanglement between these conductive microfibrils. This unique conductive structure provided the PP composites with a low electrical conductivity percolation threshold. Moreover, the electromechanical properties of conductive MFCs were investigated for the first time. A great stability, a high sensitivity and a nice reproducibility were achieved simultaneously for CB/PA6/PP MFCs. This work provides a universal and low-cost method for the conductive polymer composites’ (CPCs) fabrication as sensing materials.