Polycaprolactone Films Modified by L-Arginine for Mesenchymal Stem Cell Cultivation

Effect of Functionalization of the Polycaprolactone Film Surface on the Mechanical and Biological Properties of the Film Itself

The lack of suitable functional groups for cell adhesion on the surface of Polycaprolactone (PCL) is one of the main limitations in order to use PCL for biomedical applications. The aim of this research is to modify the PCL film surface using arginine, via an aminolysis reaction. In this regard, after PCL films formation by casting method, they were immersed in arginine solutions of various concentration at room temperature or then heated to 40 °C and in the presence of isopropanol or without it. To assess the structure of the modified surface, its wettability, and mechanical properties, methods of measuring the contact angle and the strip tensile test were used, and to compare the degree of attachment and the rate of cell proliferation, the method of fluorescent staining of cultured cells was used. The change in protein synthesis by cells on the modified surface was assessed using Western blotting. The results obtained show that the treatment of PCL films with an aqueous solution of arginine at room temperature for 1 day increases the hydrophilicity of the surface. Wherein surface modification led to a two-fold decrease of mechanical strength and flow stress, but elongation increase by about 30% for PCL films after modification in 0.5 M aqueous arginine solution at room temperature. Moreover, cell attachment and proliferation, as well as collagen synthesis, were significantly enhanced after arginine modification. The proposed simple and effective method for modifying PCL films with arginine significantly expands the possibilities for developing biocompatible scaffolds for tissue engineering.

Collagen Scaffolds Treated by Hydrogen Peroxide for Cell Cultivation

Collagen in the body is exposed to a range of influences, including free radicals, which can lead to a significant change in its structure. Modeling such an effect on collagen fibrils will allow one to get a native structure in vitro, which is important for modern tissue engineering. The aim of this work is to study the effect of free radicals on a solution of hydrogen peroxide with a concentration of 0.006–0.15% on the structure of collagen fibrils in vitro, and the response of cells to such treatment. SEM measurements show a decrease in the diameter of the collagen fibrils with an increase in the concentration of hydrogen peroxide. Such treatment also leads to an increase in the wetting angle of the collagen surface. Fourier transform infrared spectroscopy demonstrates a decrease in the signal with wave number 1084 cm⁻¹ due to the detachment of glucose and galactose linked to hydroxylysine, connected to the collagen molecule through the -C-O-C- group. During the first day of cultivating ASCs, MG-63, and A-431 cells, an increase in cell adhesion on collagen fibrils treated with H₂O₂ (0.015, 0.03%) was observed. Thus the effect of H₂O₂ on biologically relevant extracellular matrices for the formation of collagen scaffolds was shown.

Different Conditions for the Modification of Polycaprolactone Films with L-Arginine

Poly-ε-caprolactone (PCL) is a biodegradable polymer used in regenerative medicine. Mesenchymal stem cells (MSCs) play an important role in the regeneration of different tissues. The hydrophobicity and neutrality of a PCL surface reduce MSCs’ adhesion and proliferation. In this study, PCL films were treated with arginine to improve surface hydrophilicity. The influences of arginine concentration, temperature, and solvent on PCL surface properties were investigated. PCL films treated with a solution of arginine in isopropyl alcohol were found to have the maximum number of amino groups. The greatest number of cells, 2 h after seeding, adhered to such films. It was shown that amino groups affect the interaction of cells with a modified surface and the hydrolysis reaction after treatment with isopropyl alcohol promotes the formation of adhesive focal contacts. Hence, our results illustrate that functional groups on the PCL surface after arginine solution treatment regulate MSC adhesion and focal contact formation.

Functional Polylactide Blend Films for Controlling Mesenchymal Stem Cell Behaviour

Polymer blending is a suitable physical modification method to create novel properties of different polymers. Blending polylactic acid (PLA) and polyethylene glycol (PEG) produces materials with a wide range of properties. This study was the first to investigate the effect of different isomeric forms of PLA and PEG with terminal amino groups to obtain biocompatible films for human mesenchymal stem cell cultivation. It has been shown by scanning electron microscopy that the surface topology changes to the greatest extent when using films obtained on the basis of poly(d,l-lactide) and PEG with high molecular weights (15,000 g/mol). In order to obtain thin films and rapid evaporation of the solvent, PEG is mixed with PLA and does not form a separate phase and is not further washed out during the incubation in water. The presence of PEG with terminal hydroxyl and amino groups in blend films after incubation in water was proven using Fourier transform infrared (FTIR) spectroscopy. Results of fluorescence microscopy demonstrated that blend films formed on PLA and polyethylene glycol diamine (PEG-NH2) are more suitable for cell spreading and focal contact formation compared to cells cultured on the surface of pure PLA films or films made from PLA and PEG.