Effect of Pressure and Particle Size During Aluminum Oxide Air Abrasion on the Flexural Strength of Disperse-Filled Composite and Polymer-Infiltrated Ceramic Network Materials

Air-Abrasion in Dentistry: A Short Review of the Materials and Performance Parameters

The selection of abrasive material and parameters of the Air-Abrasion device for a particular application is a crucial detail. However, there are no standard recommendations or manuals for choosing these details; the operator must depend on his experience and knowledge of the procedure to select the best possible material and set of parameters. This short review attempts to identify some of the effects that the selection of material and parameters could have on the performance of the Air-Abrasion procedure for a particular application. The material and parameter data are collected from various studies and categorized according to the most popular materials in use right now. These studies are then analyzed to arrive at some inferences on the performance of Air-Abrasion materials and parameters. This review arrives at a few conclusions on the effectiveness of a material and parameter set, and that there is potential for developments in the area of standardizing parameter selection; also, there is scope for further studies on Bio-Active Glass as an alternative to the materials currently used in Air-Abrasion.

Effect of airborne particle abrasion treatment of two types of 3D-printing resin materials for permanent restoration materials on flexural strength

OBJECTIVES

This study aimed to assess the effects of airborne-particle abrasion (APA) on the flexural strength of two types of 3D-printing resins for permanent restoration.

METHODS

Two types of 3D printing resins (urethane dimethacrylate oligomer; UDMA, ethoxylated bisphenol-A dimethacrylate; BEMA) constituting different components were printed. The specimen surfaces were subjected to APA using 50 and 110 µm alumina particles under different pressures. The three-point flexural strength was measured for each surface treatment group, and a Weibull analysis was performed. Surface characteristics were analyzed via surface roughness measurements and scanning electron microscopy. Dynamic mechanical analysis and nano-indentation measurements were limited to the control group.

RESULTS

The three-point flexural strength according to the surface treatment was significantly lower in the UDMA group for large particle sizes and at high pressures; the BEMA group demonstrated low flexural strength for large particle sizes regardless of the pressure. After thermocycling, the flexural strengths of UDMA and BEMA significantly decreased in the group subjected to surface treatment. The Weibull modulus and characteristic strength of UDMA were higher than those of BEMA under different APA and thermocycling conditions. As the abrasion pressure and particle size increased, a porous surface formed, and the surface roughness increased. Compared with BEMA, UDMA featured a lower strain, greater strain recovery, and a negligible increase in modulus according to strain.

SIGNIFICANCE

Thus, surface roughness increased with the sandblasting particle size and pressure of the 3D-printing resin. Hence, a suitable surface treatment method to improve adhesion can be determined by considering physical property changes.

The effect of sandblasting versus acid etching on the surface roughness and biaxial flexural strength of CAD/CAM resin-matrix ceramics (In vitro study)

BACKGROUND

CAD/CAM resin matrix ceramics are one of the materials used in dental offices. The long-term success of the restoration depends on the bond strength of the restoration to the tooth and other materials; thus, surface treatment of the restoration is necessary to achieve this. But such treatment may affect the restoration strength. The purpose of this study is to assess the impact of various surface treatments on the surface roughness (Ra) and the biaxial flexural strength of two CAD-CAM resin-matrix ceramics.

METHODS

Thirty-six-disc-shaped specimens, each measuring 1.2 mm in thickness and 12 mm in diameter, were machined from two resin-matrix ceramic blocks (Lava Ultimate and Cerasmart) (n = 18). Based on the surface treatments, each material was divided into 3 groups: control (no treatment), 50-μm Al₂O₃ sandblasting, or 9% hydrofluoric acid etching (n = 6). The surface roughness (Ra) was evaluated by the 3D laser scanning microscope. Then, specimens were aged by thermal cycling (5000 cycles) and tested for biaxial flexural strength using a universal testing machine at a crosshead speed of 1.0 mm/min.

RESULTS

No significant differences in flexural strength or Ra were found for Lava Ultimate among the surface treatment groups. For Cerasmart, only the sandblasting group showed significantly higher Ra values than the control group. Also, the Ra values for the sandblasting group were significantly higher than those for the acid etching group. The flexural strengths of the sandblasting and acid etching groups for Cerasmart were statistically similar, and both were significantly lower than the control group.

CONCLUSIONS

Although all of the applied surface conditioning techniques improved Ra, they had a negative impact on the flexural strength of resin-matrix ceramics. Thus, clinicians should utilize the appropriate surface treatment techniques, taking into account their effects on the surface roughness and mechanical properties of resin-matrix ceramics.

Influence of surface treatment and ageing on the bond strength of resin cement to hybrid and glass-ceramic CAD/CAM materials

The influence of different surface treatments and ageing on the shear bond strength (SBS) of computer-aided design/computer-aided manufacturing (CAD/CAM) materials is still contentious. Therefore, this study evaluated the effect of surface treatments and ageing on the SBS of resin cement to polymer-infiltrated ceramic network (PICN) and zirconia-reinforced lithium silicate (ZLS) CAD/CAM materials. Specimens of PICN (n=10) and ZLS (n=10) were submitted to four surface treatment groups: 1) 5% hydrofluoric acid etching (HF) + silanisation (SI); 2) Air abrasion (AB)+HF+SI; 3) HF + universal adhesive (UA); 4) AB+HF+SI+UA. The treated specimens were bonded with resin cement cylinders and tested in SBS after 24 h and one year of water storage. Data were assessed by "analysis of variance" (ANOVA) and Tukey test (α=0.05) and failure modes were classified. No significant differences were observed among treatments at each evaluation time (p>0.05). SBS decreased after one year of storage, except for PICN treated with HF+UA (p=0.068). Air-abraded groups displayed a lower SBS reduction for ZLS. PICN and ZLS exhibited predominantly adhesive and mixed failures, but at one year, PICN cohesive failures increased. In conclusion, HF+UA is an effective surface treatment for PICN, while the combination AB+HF+SI+UA was more appropriate for ZLS. The water storage for one year reduced the SBS for most groups.

Effect of Sintering and Infiltration Conditions on Nanoscale Dual Network SiO2/Polymethyl Metacrylate Composites Mimicking Human Enamel

OBJECTIVE

The aim of this study was to achieve facile sintering conditions and rapid penetration of organic substances into the structure of sintered silica network on the nano-scale in order to prepare polymer infiltrated ceramic network mimicking human enamel.

METHODS

Stepwise temperature programming (stepwise isothermal firing) was used to create a cohesive ceramic network containing interconnected pores, which is essential to provide polymer/ceramic dual networks. Liquid phase self-penetration, ultrasonic irradiation assisted liquid phase penetration and vapor phase penetration routes were used to infiltrate methyl methacrylate monomers and benzoyl peroxide reagent into the porous silica blocks.

RESULTS

The use of stepwise isothermal firing route, in comparison with high temperature sintering methods, significantly reduces the time and temperature required for the preliminary preparation of the SiO₂ samples and reaching the appropriate interconnected porous structure. The most appropriate method for monomer and oxidant reagents infiltration is to use liquid phase infiltration assisted by ultrasound irradiation of pre-sintered nano-silica blocks. It was found that the amount of infiltrated monomer and oxidizing agent, degree of conversion of the monomer to the polymer and surface hardness of the samples strongly depend on the infiltration route.

CLINICAL SIGNIFICANCE

The use of inexpensive silica nanoparticles and low temperature sintering and the use of ultrasound waves to quickly and effectively penetrate methyl methacrylate monomers and increase the polymerization efficiency lead to the preparation of composites with a transparent appearance and mechanical properties similar to human tooth enamel.