Preparation of Molded Fiber Products from Hydroxylated Lignin Compounded with Lewis Acid-Modified Fibers Its Analysis

Sustainable Materials from Organosolv Fibers and Lignin, Kraft Fibers, and Their Blends

The aim of this study was to investigate new materials from organosolv fibers, organosolv lignin, kraft fibers, and their blends. The organosolv fibers showed reprecipitated lignin on the surface, a comparably low fiber length of 0.565 mm on average, and a high fines content of 82.3%. Handsheets were formed and thermopressed at 175 °C and 50 MPa, yielding dense materials (1050-1100 kg/m3) with properties different to that of regular paper products. The thermopressing of organosolv fibers alone produced materials with similar or better tensile strength (σb = 18.6 MPa) and stiffness (E* = 2.8 GPa) to the softwood Kraft reference pulp (σb = 14.8 MPa, E* = 1.8 GPa). The surface morphology was also smoother with fewer cavities. As a result, the thermopressed organosolv fibers exhibited higher hydrophobicity (contact angle > 95°) and had the lowest overall water uptake. Combinations of Kraft fibers with organosolv fibers or organosolv lignin showed reduced wetting and a higher density than the Kraft fibers alone. Furthermore, the addition of organosolv lignin to Kraft fibers greatly improved tensile stiffness and strength (σb = 23.8 MPa, E* = 10.5 GPa), likely due to the lignin acting as a binder to the fiber network. In conclusion, new thermopressed materials were developed and tested, which show promising potential for sustainable fiber materials with improved water resistance.

Organosolv Lignin as a Green Sizing Agent for Thermoformed Pulp Products

The purpose of this study was to investigate the use of organosolv lignin as a sizing agent for thermoformed pulp products as a sustainable material with improved water resistance. For this purpose, an in-house-produced organosolv lignin from softwood (Norway Spruce) was mixed with bleached and unbleached chemi-thermomechanical pulp fibers. In addition, the isolated organosolv lignin was characterized by ATR-FTIR spectroscopy, size-exclusion chromatography, and thermogravimetric analysis. The analysis showed that organosolv lignin was of a high purity and practically ash-free, exhibiting low molecular weight, a glass transition temperature below the thermoforming temperature, and a high content of phenolic OH groups. The mechanical properties and water resistance of the organosolv lignin-sized thermoformed pulp materials were measured. A small decrease in strength and an increase in stiffness and density were observed for the lignin-sized thermoformed materials compared to the reference, that is, unsized materials. The addition of organosolv lignin decreased the wettability and swelling of the thermoformed product. These results are due to the distribution of organosolv lignin on the surface, filling in the pores and cavities, and providing a tighter fit within the thermoformed materials. In conclusion, the results from our study encourage the use of organosolv lignin as a sizing additive to thermoformed products, which can improve the water resistance to use it in sustainable packaging applications.

A Mini-Review on Preparation of Functional Composite Fibers and Their Based Devices

Composite fibers are composed of two or more different components by functionating, coating or direct spinning, enabling unique characteristics, such as design ability, high strength, and high- and low-temperature resistance. Due to their ability to be directly woven into or stitched onto textiles to prepare flexible electronic devices, stretchable composite fibers have drawn great attention, enabling better wearability and integrality to wearable devices. Fiber or fiber-based electronic film or textiles represent a significant component in wearable technology, providing the possibility for portable and wearable electronics in the future. Herein, we introduce the composite fiber together with its preparation and devices. With the advancement of preparation technology, the as-prepared composite fibers exhibit good performance in various applications closely related to human life. Moreover, a simple discussion will be provided based on recent basic and advanced progress on composite fibers used in various devices.