Properties and Interfacial Bonding Enhancement of Oil Palm Bio-Ash Nanoparticles Biocomposites

Properties Enhancement Nano Coconut Shell Filled in Packaging Plastic Waste Bionanocomposite

Plastic waste recycling has been proposed as a long-term solution to eliminate land and marine deposit. This study proposed a new approach to fabricate biocomposites of nano-sized fillers and low matrix compositions with a great performance by using plastic packaging waste different from the conventional biocomposite. Coconut shell, an agricultural waste, wasbonded with waste plastic to form a biocomposite with a coupling agent. The optimum percentage composition and the effect of coconut shell ball milling time on the properties of the biocomposite were studied with density, thickness swelling, porosity flexural strength, flexural modulus, compressive strength, thermogravimetric analysis, differential scanning calorimetry, scanning electron microscope (SEM), and atomic force microscopy (AFM). The results showed that the optimum performance of biocomposite was obtained at 30/70 (wt.%) plastic waste to coconut shell ratio, where 70 wt.% was the highest coconut shell composition that can be achieved. Furthermore, for 30 wt.% of polypropylene (low matrix), the performance of biocomposite improved significantly with milling time due to enhanced interaction between filler and matrix. As the milling time was increased from 0 to 40 h, the density increased from 0.9 to 1.02 g/cm3; thickness swelling decreased from 3.4 to 1.8%; porosity decreased from 7.0 to 3.0%; flexural strength increased from 8.19 to 12.26 MPa; flexural modulus increased from 1.67 to 2.87 GPa, and compressive strength increased from 16.00 to 27.20 MPa. The degradation temperature of biocomposite also increased as the milling duration increased from 0 to 40 h. The melting temperature increased significantly from 160 to 170 °C as the milling duration increased from 0 to 40 h. The depolymerisation occurred at 350 °C, which also increased with milling duration. This study revealed that the performance of biocomposite improved significantly with a lower percentage matrix and fillernanoparticle rather than increasing the percentage of the matrix. The nanocomposite can be used as a panelboard in industrial applications.

Bionanocarbon Functional Material Characterisation and Enhancement Properties in Nonwoven Kenaf Fibre Nanocomposites

Bionanocarbon as a properties enhancement material in fibre reinforced nanobiocomposite was investigated for sustainable material applications. Currently, an extensive study using the micro size of biocarbon as filler or reinforcement materials has been done. However, poor fibre-matrix interface results in poor mechanical, physical, and thermal properties of the composite. Hence in this study, the nanoparticle of biocarbon was synthesised and applied as a functional material and properties enhancement in composite material. The bionanocarbon was prepared from an oil palm shell, an agriculture waste precursor, via a single-step activation technique. The nanocarbon filler loading was varied from 0, 1, 3, and 5% as nanoparticle properties enhancement in nonwoven kenaf fibre reinforcement in vinyl ester composite using resin transfer moulding technique. The functional properties were evaluated using TEM, particle size, zeta potential, and energy dispersion X-ray (EDX) elemental analysis. While the composite properties enhancement was evaluated using physical, mechanical, morphological, thermal, and wettability properties. The result indicated excellent nanofiller enhancement of fibre-matrix bonding that significantly improved the physical, mechanical, and thermal properties of the bionanocomposite. The SEM morphology study confirmed the uniform dispersion of the nanoparticle enhanced the fibre-matrix interaction. In this present work, the functional properties of bionanocarbon from oil palm shells (oil palm industrial waste) was incorporated in nanaobiocomposite, which significantly enhance its properties. The optimum enhancement of the bionanocomposite functional properties was obtained at 3% bionanocarbon loading. The improvement can be attributed to homogeneity and improved interfacial interaction between nanoparticles, kenaf fibre, and matrix.

Propionic Anhydride Modification of Cellulosic Kenaf Fibre Enhancement with Bionanocarbon in Nanobiocomposites

The use of chemical modification of cellulosic fibre is applied in order to increase the hydrophobicity, hence improving the compatibility between the fibre and matrix bonding. In this study, the effect of propionic anhydride modification of kenaf fibre was investigated to determine the role of bionanocarbon from oil palm shell agricultural wastes in the improvement of the functional properties of bionanocomposites. The vinyl esters reinforced with unmodified and propionic anhydride modified kenaf fibres bio nanocomposites were prepared using 0, 1, 3, 5 wt% of bio-nanocarbon. Characterisation of the fabricated bionanocomposite was carried out using FESEM, TEM, FT-IR and TGA to investigate the morphological analysis, surface properties, functional and thermal analyses, respectively. Mechanical performance of bionanocomposites was evaluated according to standard methods. The chemical modification of cellulosic fibre with the incorporation of bionanocarbon in the matrix exhibited high enhancement of the tensile, flexural, and impact strengths, for approximately 63.91%, 49.61% and 54.82%, respectively. The morphological, structural and functional analyses revealed that better compatibility of the modified fibre–matrix interaction was achieved at 3% bionanocarbon loading, which indicated improved properties of the bionanocomposite. The nanocomposites exhibited high degradation temperature which signified good thermal stability properties. The improved properties of the bionanocomposite were attributed to the effect of the surface modification and bionanocarbon enhancement of the fibre–matrix networks.