Tribological Performance and Thermal Stability of Nanorubber-Modified Polybenzoxazine Composites for Non-Asbestos Friction Materials

High Performance Composites Based on Highly Filled Glass Fiber-Reinforced Polybenzoxazine for Post Application

Glass fiber post based on the new polymeric material, polybenzoxazine, is prepared and the effects of glass fiber contents on mechanical and thermal properties are evaluated. The mechanical response to externally applied loads of tooth restored with glass fiber-reinforced polybenzoxazine composite posts is also simulated by finite element analysis of a tridimensional model and compared with the response to that of a natural tooth. The reinforcing of glass fiber can help improve the mechanical and thermal properties of the polybenzoxazine influenced by the interfacial adhesion between the glass fiber and polybenzoxazine matrix, except for the relatively high mechanical property of the glass fiber. The mechanical data, i.e., elastic modulus under flexure load or flexural modulus by three-point bending test of the glass fiber-reinforced polybenzoxazine composites are agreed with the elastic modulus of dentin and then used in the finite element model. The restoration using the glass fiber-reinforced polybenzoxazine composite post provided the maximum von Mises equivalent stress at the cervical third area of the endodontically treated tooth model as similarly observed in the natural tooth. In addition, the maximum von Mises equivalent stress of the tooth restored with the glass fiber-reinforced polybenzoxazine composite post is also quietly like that of the natural tooth. The finding of this work provided the essential properties of the glass fiber-reinforced polybenzoxazine composite for dental restorations and appliances.

Effects of Automotive Test Parameters on Dry Friction Fiber-Reinforced Clutch Facing Surface Microgeometry and Wear

Wear and surface microgeometry aspects of fiber-reinforced hybrid composite dry friction clutch facings are revealed in a novel way: after different, real life automotive tests during their lifetime. This study examines and reveals the tribological response of friction material surfaces to real life application conditions with two different facing diameters and in two directions. Along the increasing activation energy scale, wear values increased according to two different trends, sorting tests into two main groups, namely 'clutch killer' and 'moderate'. Wear results also highlighted the influence of mileage and test conditions, with clutch killer tests also creating considerable wear-more than 0.1 mm-at inner diameters: 1% higher wear was generated by 90% higher mileage; another 1% increment could be caused by insufficient cooling time or test bench-specific conditions. Surface roughness values trends varied accordingly with exceptions revealing effects of facing size, friction diameter and directions and test conditions: small (S) facings produced significantly decreased Rmax roughness, while large (L) and medium (M) size facings had increased roughness values; Rmax results showed the highest deviations among roughness values in radial direction; tests run with trailer and among city conditions resulted in more than 2% thickness loss and a 40-50% roughness decrease.

Radiation Graft-Copolymerization of Ultrafine Fully Vulcanized Powdered Natural Rubber: Effects of Styrene and Acrylonitrile Contents on Thermal Stability

Graft copolymers, deproteinized natural rubber-graft-polystyrene (DPNR-g-PS) and deproteinized natural rubber-graft-polyacrylonitrile (DPNR-g-PAN), were prepared by the grafting of styrene (St) or acrylonitrile (AN) monomers onto DPNR latex via emulsion copolymerization. Then, ultrafine fully vulcanized powdered natural rubbers (UFPNRs) were produced by electron beam irradiation of the graft copolymers in the presence of di-trimethylolpropane tetra-acrylate (DTMPTA) as a crosslinking agent and, subsequently, a fast spray drying process. The effects of St or AN monomer contents and the radiation doses on the chemical structure, thermal stability, and physical properties of the graft copolymers and UFPNRs were investigated. The results showed that solvent resistance and grafting efficiency of DPNR-g-PS and DPNR-g-PAN were enhanced with increasing monomer content. SEM morphology of the UFPNRs showed separated and much less agglomerated particles with an average size about 6 μm. Therefore, it is possible that the developed UFPNRs grafted copolymers with good solvent resistance and rather high thermal stability can be used easily as toughening modifiers for polymers and their composites.