Application of β-Tricalcium Phosphate in Adhesive Dentin Bonding

Advancing dentin remineralization: Exploring amorphous calcium phosphate and its stabilizers in biomimetic approaches

OBJECTIVE

This review elucidates the mechanisms underpinning intrafibrillar mineralization, examines various amorphous calcium phosphate (ACP) stabilizers employed in dentin's intrafibrillar mineralization, and addresses the challenges encountered in clinical applications of ACP-based bioactive materials.

METHODS

The literature search for this review was conducted using three electronic databases: PubMed, Web of Science, and Google Scholar, with specific keywords. Articles were selected based on inclusion and exclusion criteria, allowing for a detailed examination and summary of current research on dentin remineralization facilitated by ACP under the influence of various types of stabilizers.

RESULTS

This review underscores the latest advancements in the role of ACP in promoting dentin remineralization, particularly intrafibrillar mineralization, under the regulation of various stabilizers. These stabilizers predominantly comprise non-collagenous proteins, their analogs, and polymers. Despite the diversity of stabilizers, the mechanisms they employ to enhance intrafibrillar remineralization are found to be interrelated, indicating multiple driving forces behind this process. However, challenges remain in effectively designing clinically viable products using stabilized ACP and maximizing intrafibrillar mineralization with limited materials in practical applications.

SIGNIFICANCE

The role of ACP in remineralization has gained significant attention in dental research, with substantial progress made in the study of dentin biomimetic mineralization. Given ACP's instability without additives, the presence of ACP stabilizers is crucial for achieving in vitro intrafibrillar mineralization. However, there is a lack of comprehensive and exhaustive reviews on ACP bioactive materials under the regulation of stabilizers. A detailed summary of these stabilizers is also instrumental in better understanding the complex process of intrafibrillar mineralization. Compared to traditional remineralization methods, bioactive materials capable of regulating ACP stability and controlling release demonstrate immense potential in enhancing clinical treatment standards.

Fiber post bonding with beta-tricalcium phosphate incorporated root dentin adhesive. SEM, EDX, FTIR, rheometric and bond strength study

The aim was to formulate an experimental adhesive (EA) and added nanoparticles (NPs) of beta-tricalcium phosphate (β-TCP) to see the impact on pushout bond strength (PBS) and other mechanical properties. Three adhesives were prepared, including EA (control, without β-TCP NPs), 2.5%-β-TCP NPs containing adhesive (2.5%-NPA), and 5% β-TCP NPs containing adhesive (5%-NPA). For the characterization of the NPs, scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) spectroscopy was accomplished. For the adhesive's characterization, rheological assessment, and degree of conversion (DC) analysis were performed. PBS of these adhesives against resin fiber post to root dentin, interfacial failure categories, and resin dentin interface analysis were also assessed. The β-TCP NPs were seen as agglomerated asymmetrical particles on SEM. These NPs were composed primarily of calcium (Ca), and phosphorus (P). Rheological evaluation of the adhesive's showed a drop in the viscosity of all adhesives at greater angular frequencies. The greatest DC was detected for the EA group (67.54 ± 7.9) followed by 2.5%-NPA group (45.32 ± 5.1), whereas the lowest DC values were seen for the 5%-NPA group (38.97 ± 6.5). Concerning PBS, the 2.5%-NPA revealed the highest values at the coronal (12.81 ± 3.0) and middle (8.50 ± 2.3) sections, whereas, for the apical section, the highest PBS values were seen for the 5%-NPA (4.9 ± 1.6). Most of the failures for all adhesive groups were seen at the adhesive-dentin interface (cohesive type failures) for all root segments (coronal, middle, and apical). The resin-dentin interface analysis verified hybrid layer and resin tag formation for all adhesives, but the presence of dispersed β-TCP NPs was only seen in the two NP-reinforced adhesives. The adding of β-TCP NPs in the adhesive could be beneficial as it could improve its PBS. Suitable rheological properties and dentin interaction were also observed for NP-reinforced adhesives. A reduced DC was seen for both β-TCP NP-containing adhesives as compared to the EA. RESEARCH HIGHLIGHTS: Experimental adhesives were reinforced with beta-tricalcium phosphate (β-TCP) nanocrystals. The β-TCP NPs were seen as agglomerated asymmetrical particles on SEM. These NPs were composed primarily of calcium (Ca), and phosphorus (P). β-TCP adhesives demonstrated superior pushout bond strength and a drop in the adhesive viscosity at greater angular frequencies compared to control adhesive. The greatest DC was detected for the EA group followed by 2.5%- β-TCP group, whereas the lowest DC values were for the 5%- β-TCP group.

Influence of Concentration Levels of β-Tricalcium Phosphate on the Physical Properties of a Dental Adhesive

Our study assessed the influence of integrating 5% and 10% tricalcium phosphate (β-TCP-Ca₃(PO₄)₂.) nanoparticles into a dental adhesive on the adhesive’s bonding. To evaluate the filler nanoparticles, scanning electron microscopy (SEM), Energy Dispersive X-Ray (EDX) spectroscopy, Fourier-transform infrared (FTIR) spectroscopy, and micro-Raman spectroscopy techniques were used. Shear Bond strength (SBS) testing, degree of conversion (DC) analysis, investigation of the adhesive–dentin interface, and biofilm experiments were conducted. The SEM micrographs revealed non-uniform agglomerates, while the EDX demonstrated the existence of oxygen ‘O’ (24.2%), phosphorus ‘P’ (17.4%) and calcium ‘Ca’ (60.1%) in the β-TCP nanoparticles. The FTIR and micro-Raman spectra indicated characteristic bands for β-TCP containing materials. The 10 wt.% β-TCP adhesive presented the highest SBS values (NTC-10 wt.% β-TCP: 33.55 ± 3.73 MPa, TC-10 wt.% β-TCP: 30.50 ± 3.25 MPa), followed by the 5 wt.% β-TCP adhesive (NTC-5 wt.% β-TCP: 32.37 ± 3.10 MPa, TC-5 wt.% β-TCP: 27.75 ± 3.15 MPa). Most of the detected failures after bond strength testing were adhesive in nature. The β-TCP adhesives demonstrated suitable dentin interaction by forming a hybrid layer (with few or no gaps) and resin tags. The β-TCP adhesives (10 wt.%) revealed lower DC values compared to control. The incorporation of 5 and 10 wt.% concentrations of β-TCP particles resulted in an increase in SBS values. A linear decline in DC values was witnessed when the nanoparticle concentration was increased. Further research focusing on exploring the influence of higher filler concentrations on adhesive’s properties is recommended.