Biobased Waterborne Polyurethane-Ureas Modified with POSS-OH for Fluorine-Free Hydrophobic Textile Coatings

Preparation and Properties of GMS/HTSF-Modified Waterborne Polyurethane Fluorine-Free Waterproof and Breathable Film

Developing a fluorine-free, durable, high-performance waterproof breathable film for fabrics remains a formidable challenge. In this paper, a strategy for the preparation of fluorine-free, durable, and high-efficiency fabric waterproof and breathable membranes using glyceryl monostearate (GMS)/double-ended hydroxy silicone oil (HTSF)-modified waterborne polyurethane was proposed. The orderly orientation of GMS and HTSF gives the fabric excellent water-repellent properties, and the polyurethane macromolecular chain ensures strong adhesion of long-chain alkanes and silicones to the fabric surface. In this paper, the effects of different GMS contents on the stability, chemical structure, particle size, viscosity, water absorption performance, surface morphology, and XPS of a waterborne polyurethane fluorine-free waterproof and breathable membrane (GHWPU) were studied. At the same time, the application properties of GHWPU-treated fabrics, such as waterproof performance, antifouling performance, surface energy, morphology, and air permeability, were discussed. Through the analysis of SEM and XPS, it was found that the folds on the surface of the film were more and more orderly with the increasing content of GMS, and this orderly distribution of water-repellent groups endowed the film with excellent water-repellent ability. When the GMS content was 28 wt %, the finished fabrics had excellent comprehensive properties such as static contact angle of 141.6°, hydrostatic pressure of 96.7 KPa, resistance to more than 30 washes, and air permeability of 119.3 mm/s.

Hybrid Hemp Particles as Functional Fillers for the Manufacturing of Hydrophobic and Anti-icing Epoxy Composite Coatings

The development of hydrophobic composite coatings is of great interest for several applications in the aerospace industry. Functionalized microparticles can be obtained from waste fabrics and employed as fillers to prepare sustainable hydrophobic epoxy-based coatings. Following a waste-to-wealth approach, a novel hydrophobic epoxy-based composite including hemp microparticles (HMPs) functionalized with waterglass solution, 3-aminopropyl triethoxysilane, polypropylene-graft-maleic anhydride, and either hexadecyltrimethoxysilane or 1H,1H,2H,2H-perfluorooctyltriethoxysilane is presented. The resulting epoxy coatings based on hydrophobic HMPs were cast on aeronautical carbon fiber-reinforced panels to improve their anti-icing performance. Wettability and anti-icing behavior of the prepared composites were investigated at 25 °C and -30 °C (complete icing time), respectively. Samples cast with the composite coating can achieve up to 30 °C higher water contact angle and doubled icing time than aeronautical panels treated with unfilled epoxy resin. A low content (2 wt %) of tailored HMPs causes an increase of ∼26% in the glass transition temperature of the coatings compared to pristine resin, confirming the good interaction between the hemp filler and epoxy matrix at the interphase. Finally, atomic force microscopy reveals that the HMPs can induce the formation of a hierarchical structure on the surface of casted panels. This rough morphology, combined with the silane activity, allows the preparation of aeronautical substrates with enhanced hydrophobicity, anti-icing capability, and thermal stability.

Highly Efficient Cationic Polymerization of β-Pinene, a Bio-Based, Renewable Olefin, with TiCl4 Catalyst from Cryogenic to Energy-Saving Room Temperature Conditions

Polymers based on renewable monomers are projected to have a significant role in the sustainable economy, even in the near future. Undoubtedly, the cationically polymerizable β-pinene, available in considerable quantities, is one of the most promising bio-based monomers for such purposes. In the course of our systematic investigations related to the catalytic activity of TiCl4 on the cationic polymerization of this natural olefin, it was found that the 2-chloro-2,4,4-trimethylpentane (TMPCl)/TiCl4/N,N,N′,N′-tetramethylethylenediamine (TMEDA) initiating system induced efficient polymerization in dichloromethane (DCM)/hexane (Hx) mixture at both −78 °C and room temperature. At −78 °C, 100% monomer conversion was observed within 40 min, resulting in poly(β-pinene) with relatively high Mn (5500 g/mol). The molecular weight distributions (MWD) were uniformly shifted towards higher molecular weights (MW) in these polymerizations as long as monomer was present in the reaction mixture. However, chain–chain coupling took place after reaching 100% conversion, i.e., under monomer-starved conditions, resulting in considerable molecular weight increase and MWD broadening at −78 °C. At room temperature, the polymerization rate was lower, but chain coupling did not occur. The addition of a second feed of monomer in the polymerization system led to increasing conversion and polymers with higher MWs at both temperatures. 1H NMR spectra of the formed polymers indicated high in-chain double-bond contents. To overcome the polarity decrease by raising the temperature, polymerizations were also carried out in pure DCM at room temperature and at −20 °C. In both cases, rapid polymerization occurred with nearly quantitative yields, leading to poly(β-pinene)s with Mns in the range of 2000 g/mol. Strikingly, polymerization by TiCl4 alone, i.e., without any additive, also occurred with near complete conversion at room temperature within a few minutes, attributed to initiation by adventitious protic impurities. These results convincingly prove that highly efficient carbocationic polymerization of the renewable β-pinene can be accomplished with TiCl4 as catalyst under both cryogenic conditions, applied widely for carbocationic polymerizations, and the environmentally benign, energy-saving room temperature, i.e., without any additive and cooling or heating. These findings enable TiCl4-catalyzed eco-friendly manufacturing of poly(β-pinene)s, which can be utilized in various applications, and in addition, subsequent derivatizations could result in a range of high-added-value products.

Modifications of Textile Materials with Functional Silanes, Liquid Silicone Softeners, and Silicone Rubbers-A Review

General information concerning different kinds of chemical additives used in the textile industry has been described in this paper. The properties and applications of organofunctional silanes and polysiloxanes (silicones) for chemical and physical modifications of textile materials have been reviewed, with a focus on silicone softeners, silane, and silicones-based superhydrophobic finishes and coatings on textiles composed of silicone elastomers and rubbers. The properties of textile materials modified with silanes and silicones and their practical and potential applications, mainly in the textile industry, have been discussed.

Role of Macrodiols in the Synthesis and Thermo-Mechanical Behavior of Anti-Tack Water Borne Polyurethane Dispersions

The texture and molecular weight of polymer drastically affect the adhesion or tack strength. Waterborne polyurethane dispersions (WBPU) have been prepared using two different macrodiols of hydroxyl terminated polybutadiene (HTPB; Mn = 2912 g/mol⁻¹) and four compositions of Polypropylene glycol (PPG Mn = 425, 1000, 2000, 2700 g/mol⁻¹). The contents of the macrodiols have been varied using HTPB as 5, 10 and 15 mol%. The prepolymer of HTPB and Poly propylene glycol (PPG) have been developed using 4,4-Methylene bis(cyclohexyl isocyanate) (H₁₂MDI) which is extended using 1, 4 butanediol (BD) followed by the dispersion of polymers in deionized water. Fourier Transform Infra-red spectroscopy (FTIR) is used to confirm the desired PU linkage. The probe tack graphs for tack analysis have not shown any plateau indicating absence of fibrillation. Two different values of glass transition temperature (Tg) have been observed for each dispersion using Differential Scanning Calorimetry(DSC). Storage modulus (E′) up to 3.97 MPa and (tanδ/E′) from 0.01–0.30 MPa⁻¹ has been observed via Dynamic Mechanical Analysis (DMA). Introducing the HTPB has resulted in a decrease in the values of (tanδ/E′). No adhesion favorable parameters have been retrieved, indicating the molar variation a key factor in the development of anti-tack dispersions.