Strand-Morphology-Based Process Optimization for Extrusion-Based Silicone Additive Manufacturing

X-ray CT Analysis of the Cross-Section of a 3D-Printed Deformed Layer

In this study, we experimentally analyzed the deformation shape of stacked layers developed using three-dimensional (3D) printing technology. The nozzle traveling speed was changed to 80, 90, 100, and 110 mm/s when printing the layers to analyze its effect on layer deformation. Furthermore, the cross-sectional area and the number of layers were analyzed by printing five layers with overall dimensions of 1000 (w) × 2200 (l) × 50 (h) mm (each layer was 10 mm high) using Vernier calipers. Moreover, we analyzed the interface and cross-sectional area of layers that are difficult to confirm visually using X-ray computed tomography (X-ray CT) analysis. As a result of measuring the deformation at the center of the layer, it was confirmed that the deformation was greater for lower nozzle traveling speeds. Consequently, the X-ray CT analysis verified that the layer had the same cross-sectional area irrespective of the layer printing order at the same nozzle travel speed, even if the layer was deformed.