Development of Quebracho (Schinopsis balansae) Tannin-Based Thermoset Resins

Optimization of Starch-Tannin Adhesives for Solid Wood Gluing

Bio-based solutions for solid timber gluing have always been a very sensitive topic in wood technology. In this work, we optimize the gluing conditions of a starch-tannin formulation, which allows high performance in dry conditions and resistance to water dipping for 3 h, allowing for the D2 classification to be reached according to EN 204. It was observed that the starch-tannin formulations enhanced their performance by increasing the heating temperature, achieving satisfactory results at 140 °C for 13 min. The proportion of polyphenols in the mixture enhances the water resistance but is only tolerated until 20-30%. In particular, the addition of 10% tannin-hexamine enhances the water-resistant properties of starch for both quebracho and chestnut extract. The application of the jet of cold atmospheric plasma allows for good results with more viscous formulations, increasing their penetration in wood. Solid-state 13C-NMR analysis was also performed, and the spectroscopic information suggests establishing a coordination complex between starch and tannin.

Comparing Condensed and Hydrolysable Tannins for Mechanical Foaming of Furanic Foams: Synthesis and Characterization

This study examined the potential of hydrolysable tannin in comparison to condensed tannins for the production of furanic foams. The results indicate that chestnut tannin presents lower reactivity and requires a stronger acid for the polymerization. Additionally, foamability and density were found to be dependent on both surfactant concentration and tannin type, allowing lower densities for mimosa tannin and lower thermal conductivities for chestnut-based foams. Mimosa tannin was found to have the highest compression strength, followed by quebracho and chestnut, promising thermal conductivity of around 50 mW/m·K for 300 kg/m³ foams, which suggests that chestnut foams have the potential to performing highly when the density is reduced. Chemical analysis revealed that the methylene moieties of the furanics are non-specific and produces new covalent bonds with nucleophilic substrates: -OH groups and free-positions in the flavonoids. Overall, this study opens new perspectives for the application of hydrolysable tannins in polymer and material science.

Quebracho Tannin Bio-Based Adhesives for Plywood

Wood-based products are traditionally bonded with synthetic adhesives. Resources availability and ecological concerns have drawn attention to bio-based sources. The use of tannin-based adhesives for engineered wood products has been known for decades, however, these formulations were hardly used for the gluing of solid wood because their rigidity involved low performance. In this work, a completely bio-based formulation consisting of Quebracho (Schinopsis balancae) extract and furfural is characterized in terms of viscosity, gel time, and FT-IR spectroscopy. Further, the usability as an adhesive for beech (Fagus sylvatica) plywood with regard to press parameters (time and temperature) and its influence on physical (density and thickness) and mechanical properties (modulus of elasticity, modulus of rupture and tensile shear strength) were determined. These polyphenolic adhesives presented non-Newtonian behavior but still good spreading at room temperature as well as evident signs of crosslinking when exposed to 100 °C. Within the press temperature, a range of 125 °C to 140 °C gained suitable results with regard to mechanical properties. The modulus of elasticity of five layered 10 mm beech plywood ranged between 9600 N/mm² and 11,600 N/mm², respectively, with 66 N/mm² to 100 N/mm² for the modulus of rupture. The dry state tensile shear strength of ~2.2 N/mm² matched with other tannin-based formulations, but showed delamination after 24 h of water storage. The proposed quebracho tannin-furfural formulation can be a bio-based alternative adhesive for industrial applicability for special plywood products in a dry environment, and it offers new possibilities in terms of recyclability.

Quebracho-Based Wood Preservatives: Effect of Concentration and Hardener on Timber Properties

Tannin polyphenols are produced by plants to protect themselves against natural decay. It is expected that impregnating low-durable timber with tannin extracts of more durable species such as quebracho (Schinopsis balansae) will enhance the durability of the specimens. This biomimetic approach combined with the in situ polymerization of quebracho–hexamine formulations can be a valid alternative to synthetic wood preservatives. In this work, we aim to evaluate the impregnation mechanism as well as the impact of tannin and hardener concentration on the mechanical and leaching resistance properties of treated wood. Compression resistance, surface hardness and leaching resistance of four different common non-durable wood species: spruce (Picea abies), pine (Pinus spp.), poplar (Populus alba) and beech (Fagus sylvatica) impregnated with different concentrations of extract and hexamine are presented. The results show that the mechanical properties of tannin-impregnated timber are enhanced, especially for timber with lower densities. Tannin and hardener concentrations tendentially do not contribute significantly to further increase MOE (modulus of elasticity), MOR (modulus of rupture) and Brinell hardness. Similar results are also obtained when the specimens are tested against leaching: tannin is significantly more water-resistant when cured with hexamine, but higher amounts of hardener do not further improve its water resistance. These findings suggest that quebracho tannin–hexamine formulations are already effective at low concentrations (5 to 10% extract with 2.5 to 5% hexamine).