Welding and Riveting Hybrid Bonding of 6061 Al and Carbon Fiber Reinforced Composites

Process Characterizations of Ultrasonic Extruded Weld-Riveting of AZ31B Magnesium Alloy to Carbon Fiber-Reinforced PA66

Traditional metal-plastic dissimilar welding methods directly heat the metal workpiece, which may cause potential thermal damage to the metal workpiece. Ultrasonic extruded weld-riveting (UEWR) is a relatively new method for dissimilar joining of carbon fiber-reinforced thermoplastic (CFRTP) and metal. In this method, the CFRTP workpiece is melted using the ultrasonic effect and is squeezed into prefabricated holes in the metal workpiece to form a rivet structure. In this method, the metal workpiece is not directly heated, and potential high-temperature losses can be avoided. This paper investigates the process characterizations of UERW of AZ31B magnesium alloy to carbon fiber-reinforced PA66. The process parameters are optimized by the Taguchi method. The joint formation process is analyzed based on the fiber distribution in the cross-sections of joints. The effects of welding parameters on the joint microstructure and fracture surface morphology are discussed. The results show that a stepped amplitude strategy (40 μm amplitude in the first stage and 56 μm amplitude in the second stage) could balance the joint strength and joint appearance. Insufficient (welding energy < 2600 J or amplitude-A < 50%) or excessive (welding energy > 2800 J or amplitude-A > 50%) welding parameters lead to the formation of porous defects. Three fracture modes are identified according to the fracture surface analysis. The maximum tensile shear strength of joints at the optimal parameters is about 56.5 ± 6.2 MPa.

Study on the SPCC and CFRTP Hybrid Joint Performance Produced with Additional Nylon-6 Interlayer by Ultrasonic Plastic Welding

Due to the high degree of dissimilarity in physicochemical properties between metal and carbon fiber, it presents a tremendous challenge to join them directly. In this paper, cold rolled steel (SPCC) and carbon fiber reinforced thermoplastic (CFRTP) chopped sheet hybrid joints were produced with the addition of Nylon 6 (PA6) thermoplastic film as an intermediate layer by the ultrasonic plastic welding method. The effect of ultrasonic welding energy and preheating temperature on the hybrid joint microstructure and mechanical behavior was well investigated. The suitable joining parameters could obtain a strong joint by adding the PA6 film as an intermediate layer between the SPCC and bare carbon fibers. Microstructural analysis revealed that the interface joining condition between the PA6 film and the SPCC component is the primary reason for the joint strength. The crevices generated at the interface were eliminated when the preheating temperature arrived at 200 °C, and the joint strength thus significantly increased. The lap shear test results under quasi-static loading showed that the welding energy and preheating temperature synergistically affect the joint performances. At 240 °C, the joint strength value reached the maximum. Through the analysis of the microstructure morphology, mechanical performance, and the failure mechanism of the joint, the optimized joining process window for ultrasonic plastic welding of SPCC-CFRTP by adding an intermediate layer, was obtained.

Laser Joining of Continuous Carbon Fiber-Reinforced PEEK and Titanium Alloy with High Strength

The generation of high-performance heterojunctions between high-strength resin matrix composites and metals is of great significance for lightweight applications in fields such as aerospace and automobile engineering. Herein, we explored the feasibility of employing a laser joining process to achieve high-strength heterojunctions between continuous carbon fiber-reinforced PEEK (CCF30/PEEK) composites and titanium alloy (Ti6Al4V). A joint strength of over 50 MPa was achieved through constructing mechanical interlocking structures between CCF30/PEEK and Ti6Al4V. Tensile tests revealed that the fracture of joints was mainly ascribed to the detachment of carbon fibers from the resin matrix and the breakage of carbon fibers. The structures with different orientations and dimensions were confirmed to significantly influence the formation of interlocking structures near the joining interface and the resultant fracture strength of joints. It is believed that the results presented in this study provide a strong foundation for the production of high-performance heterojunctions.