Influence of Carbon Black and Silica Fillers with Different Concentrations on Dielectric Relaxation in Nitrile Butadiene Rubber Investigated by Impedance Spectroscopy

Hydroxyapatite-Filled Acrylonitrile-Butadiene Rubber Composites with Improved Cure Characteristics and Reduced Flammability

The goal of this work was to develop acrylonitrile-butadiene (NBR) elastomer composites filled with hydroxyapatite (HAP) characterized by improved cure characteristics and resistance to burning. Silane, i.e., (3-aminopropyl)-triethoxysilane, ionic liquid, i.e., 1-decyl-3-methylimidazolium bromide and surfactant, i.e., cetyltrimethylammonium bromide, were used to improve the filler's dispersibility in the elastomer matrix and to reduce the time and temperature of vulcanization. The effects of HAP and dispersants on the cure characteristics, crosslink density and physico-chemical properties of NBR composites were explored. The additives used, especially the ionic liquid and surfactant, effectively improved the dispersion of HAP in the NBR matrix. The amount of HAP and the dispersant used strongly affected the cure characteristics and crosslink density of NBR. The optimal vulcanization time significantly increased with HAP content and was pronouncedly reduced when ionic liquid and surfactant were applied. In addition, ionic liquid and surfactant significantly lowered the onset vulcanization temperature and improved the crosslink density and hardness of the vulcanizates while impairing their elasticity. HAP and dispersants did not significantly affect the damping properties or chemical resistance of NBR vulcanizates. Above all, application of HAP considerably enhanced the resistance of vulcanizates to thermo-oxidative aging and reduced their flammability compared with the unfilled NBR.

Direct visualization of carbon black aggregates in nitrile butadiene rubber by THz near-field microscope

The use of filling agents for rubber reinforcement is beneficial in various industrial applications, and several experimental methods have been used to study the effect of fillers on rubber. However, due to the lack of a suitable imaging technique, filler dispersion and distribution in rubber cannot be easily displayed. Thus, we utilize the THz near-field microscope (THz-NFM) to directly visualize the distribution of carbon black (CB) aggregates in nitrile butadiene rubber (NBR). The THz time-domain spectroscopy (THz-TDS) was used to evaluate the optical properties of the NBR specimens. Results revealed significant indices contrast between CB and NBR at the THz regime, which was attributed to the variation in electrical conductivities. The micrographs of NBR in the THz-NFM revealed the distribution of CB aggregates. The area fraction (AF) of the CB aggregates was calculated using a binary thresholding algorithm to compare with the transmission electron microscope method. Both methods yielded comparable AF values, suggesting, for the first time, that CB can be detected in the NBR without preprocessing the specimens.

Effect of Functional Fillers on Tribological Characteristics of Acrylonitrile Butadiene Rubber after High-Pressure Hydrogen Exposures

In a high-pressure hydrogen environment, the sealing rubber material is swelled by hydrogen, and the mechanical and tribological properties are reduced, causing various problems in the sealing performance. The focus of this study was the effect of the filler type and content on the tribological characteristics of rubber after exposure to high-pressure hydrogen. Acrylonitrile butadiene rubber specimens were exposed to high-pressure hydrogen at 96.6 MPa, and the change in the amount of wear with time after exposure was observed. The wear test was performed using a pin-on-disc ball tip to measure the amount of wear before and after hydrogen exposure of the materials under fixed revolutions per minute and normal load. Scanning electron microscopy was used to observe the wear track and cross section of the specimen to examine the changes in the wear mechanism after hydrogen exposure and to analyze the wear mechanism for each filler. The results of this study are expected to contribute to the evaluation of the tribological properties of the sealing materials used in hydrogen environments.

Filler Effects on H2 Diffusion Behavior in Nitrile Butadiene Rubber Blended with Carbon Black and Silica Fillers of Different Concentrations

Filler effects on H2 diffusion in nitrile butadiene rubbers (NBRs) blended with carbon black and silica fillers of different concentrations are first investigated by employing a volumetric analysis. Total uptake, solubility, and diffusivity of hydrogen for ten filled-NBR, including neat NBR, are determined in an exposed pressure range of 1.3 MPa~92.6 MPa. Filler dependence on hydrogen uptake and diffusion is distinctly observed in the NBRs blended with high abrasion furnace (HAF) carbon black (CB) fillers compared to NBRs blended with medium thermal furnace (MT) CB and silica filler, which is related to the specific surface area of carbon black and interface structure. The HAF CB filled-NBR follows dual sorption behavior combined with Henry's law and the Langmuir model, responsible for two contributions of solubility from polymer and filler. However, a single gas sorption behavior coming from the polymer is observed satisfying Henry's law up to 92.6 MPa for NBR blended with MT CB filled-NBR and silica filled-NBR. Diffusion demonstrates Knudsen and bulk diffusion behavior below and above, respectively, at certain pressures. With increasing pressure, the filler effect on diffusion is reduced, and diffusivity converges to a value. The correlation observed between diffusivity and filler content (or crosslink density) is discussed.