Biodiesel Synthesis from High Free-Fatty-Acid Chicken Fat using a Scrap-Tire Derived Solid Acid Catalyst and KOH

Upgrading Pyrolytic Residue from End-of-Life Tires to Efficient Heterogeneous Catalysts for the Conversion of Glycerol to Acetins

Recovered carbon blacks (rCBs) produced from end-of-life tires using pyrolysis were transformed into solid acid catalysts for the synthesis of acetins, i.e., products with a wide spectrum of practical applications. Tuning the chemical properties of the surface of samples and introducing specific functional groups on the rCBs were achieved through carbon functionalization with concentrated H2SO4. The initial and modified rCBs were thoroughly characterized using techniques such as elemental analysis, potentiometric back titration, thermogravimetric technique, scanning and transmission microscopy, X-ray photoelectron spectroscopy, etc. The catalytic activities of the samples were measured via batch mode glycerol acetylation performed at 110 °C and compared to the catalytic performance of the functionalized commercial carbon black. The modified rCBs were found to show a significant catalytic effect in the tested reaction, giving high glycerol conversions (above 95%) and satisfactory combined yields of diacetins and triacetin (~72%) within 4 h; this behavior was attributed to the presence of -SO3H moieties on the surface of functionalized rCBs. The reusability tests indicated that the modified samples were catalytically stable in subsequent acetylation runs. The obtained results evidenced the feasibility of using end-of-life tires for the production of effective acid catalysts for glycerol valorization processes.

Microwave-assisted synthesis of biodiesel by a green carbon-based heterogeneous catalyst derived from areca nut husk by one-pot hydrothermal carbonization

In this study, we have synthesized a solid acid catalyst by areca nut husk using low temperature hydrothermal carbonization method. The fabricated catalyst has enhanced sulfonic actives sites (3.12%) and high acid density (1.88 mmol g^-1) due to -SO₃H, which are used significantly for effective biodiesel synthesis at low temperatures. The chemical composition and morphology of the catalyst is determined by various techniques, such as Fourier transform infrared (FTIR), powder X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET), Scanning electron microscope (SEM), Energy disruptive spectroscopy (EDS), Mapping, Thermogravimetric analysis (TGA), CHNS analyzer, Transmission electron microscopy (TEM), particle size analyzer, and X-ray photoelectron spectroscopy (XPS). Acid-base back titration method was used to determine the acid density of the synthesized material. In the presence of the as-fabricated catalyst, the conversion of oleic acid (OA) to methyl oleate reached 96.4% in 60 min under optimized conditions (1:25 Oleic acid: methanol ratio, 80 °C, 60 min, 9 wt% catalyst dosage) and observed low activation energy of 45.377 kJ mol^-1. The presence of the porous structure and sulfonic groups of the catalyst contributes to the high activity of the catalyst. The biodiesel synthesis was confirmed by gas-chromatography mass spectrometer (GC-MS) and Nuclear magnetic resonance (NMR). The reusability of the catalyst was examined up to four consecutive cycles, yielding a high 85% transformation of OA to methyl oleate on the fourth catalytic cycle.

Utilization of Polymeric Materials toward Sustainable Biodiesel Industry: A Recent Review

The biodiesel industry is expanding rapidly in accordance with the high energy demand and environmental deterioration related to the combustion of fossil fuel. However, poor physicochemical properties and the malperformance of biodiesel fuel still concern the researchers. In this flow, polymers were introduced in biodiesel industry to overcome such drawbacks. This paper reviewed the current utilizations of polymers in biodiesel industry. Hence, four utilizing approaches were discussed, namely polymeric biodiesel, polymeric catalysts, cold-flow improvers (CFIs), and stabilized exposure materials. Hydroxyalkanoates methyl ester (HAME) and hydroxybutyrate methyl ester (HBME) are known as polymeric biodiesel sourced from carbon-enriched polymers with the help of microbial activity. Based on the literature, the highest HBME yield was 70.7% obtained at 10% H2SO4 ratio in methanol, 67 °C, and 50 h. With increasing time to 60 h, HAME highest yield was reported as 68%. In addition, polymers offer wide range of esterification/transesterification catalysts. Based on the source, this review classified polymeric catalysts as chemically, naturally, and waste derived polymeric catalysts. Those catalysts proved efficiency, non-toxicity, economic feasibility, and reusability till the 10th cycle for some polymeric composites. Besides catalysis, polymers proved efficiency to enhance the biodiesel flow-properties. The best effect reported in this review was an 11 °C reduction for the pour point (PP) of canola biodiesel at 1 wt% of ethylene/vinyl acetate copolymers and cold filter plugging point (CFPP) of B20 waste oil biodiesel at 0.08 wt% of EVA copolymer. Polymeric CFIs have the capability to modify biodiesel agglomeration and facilitate flowing. Lastly, polymers are utilized for storage tanks and auto parts products in direct contact with biodiesel. This approach is completely exclusive for polymers that showed stability toward biodiesel exposure, such as polyoxymethylene (POM) that showed insignificant change during static immersion test for 98 days at 55 °C. Indeed, the introduction of polymers has expanded in the biodiesel industry to promote green chemistry.