Influence of Conventional Polymer, Hybrid Polymer and Zinc Phosphate Luting Agents on the Bond Strength of Customized Zirconia Post in Premolars-An In-Vitro Evaluation

PEEK and glass fiber post pushout bond strength and vickers hardness of canal disinfected with curcumin photosensitizer activated by microbubble emulsion and sodium-hypochlorite with EDTA

AIMS

Impact of different post-space disinfectants (Saline, Sodium hypochlorite (NaOCl) followed by ethylene-diamine-tetra-acetic acid (EDTA) and curcumin activated by microbubble emulsion (MBE) on the Vickers hardness (VH) of root canal dentin and extrusion bond strength (EBS) of Glass fiber post (GFP) and PEEK post.

METHODS

Ninety maxillary central incisors having fully formed roots were included. After the specimen's disinfection, root canal treatment was completed. Post space was prepared by removing gutta-percha using gates glidden drills. Teeth were then arbitrarily allocated into three groups based on the methods of disinfection regime used. Group 1: Saline, Group 2: NaOCl+ EDTA and Group 3: Curcumin activated by MBE (n = 30). Analysis of VH of radicular dentin was performed using a micro-Vickers tester on ten samples from each group. After post-space disinfection, twenty specimens from each group were further divided into two subgroups (n = 10) In group-1A 2A, and 3A, GFP was used. Whereas, prefabricated PEEK posts were used in 1B, 2B, and 3B subgroups. The PBS and failure modes were performed using a universal testing machine and stereomicroscope respectively. Data was analyzed using ANOVA and Tukey post hoc test to identify significant variations among groups concerning the MH and EBS of the different posts used (p = 0.05).

RESULTS

Group 2 (5.25 % NaOCl + 17 % EDTA) (0.15 ± 0.02 GPa) treated specimens presented lowest scores of VH. However, Group 1 (Saline) irrigated canals displayed the highest scores of surface hardness (0.25 ± 0.07 GPa). Additionally, a cervical third of 3A (CP activated by MBE + GFP) (11.22 ± 0.79 MPa) presented the highest scores of bond integrity. Whereas Group 1B (Saline + PEEK post) treated specimens presented the lowest scores of PBS (4.15 ± 0.15 MPa).

CONCLUSION

Curcumin activated by microbubble emulsion for disinfection of canal dentin demonstrated favorable VH. Similarly, glass fiber post-cemented in radicular walls disinfected with curcumin activated with MBE showed promising post-bond integrity to the canal dentin.

Canal disinfection using Nd: YAG Laser, synchronized microbubble-photodynamic activation, and carbon quantum dots on microhardness, smear layer removal, and extrusion bond strength of zirconia post to canal dentin. An invitro scanning electron microscopic analysis

Evaluation of the impact of the latest root canal disinfectant, that is carbon quantum dots (CQDs), synchronized microbubble-photodynamic activation (SYMPA), and Nd: YAG laser along with ethylenediaminetetraacetic acid (EDTA) as a final irrigant on the Marten hardness (MH), smear layer (SL) removal, and extrusion bond strength (EBS) of zirconia post to the canal dentin. Eighty intact single-rooted premolars were obtained and disinfected using 0.5% chloramine-T solution. Root canal preparation was performed using ProTaper files followed by obturation. The post space was prepared for prefabricated zirconia post and all the teeth were randomly divided into four groups based on the disinfection used (n = 20 each) Group 1: 5.25% NaOCl + 17% EDTA (Control), Group 2: Nd: YAG laser + 17% EDTA, Group 3: SYMPA + 17% EDTA, and Group 4: CQDs + 17% EDTA. MH, SL removal, and EBS of zirconia post-bonded to root dentin were performed using a microhardness tester, scanning electron microscope (SEM), and universal testing machine, respectively. Both intragroup and intergroup comparisons were performed using one-way analysis of variance (ANOVA) and posthoc-Tukey test for significant difference (p < .05). Group 2 samples (Nd: YAG laser + 17% EDTA) (0.24 ± 0.06 GPa) exhibited highest values of MH. Samples in group 3 (SYMPA + 17% EDTA) treated teeth unveiled the lowest MH scores (0.13 ± 0.02 GPa). Moreover, the coronal third of Group 3 specimens (SYMPA and 17% EDTA) (1.54 ± 0.31) eliminated SL from the canal with the greatest efficacy as well as presented the highest EBS (10.13 ± 0.69 MPa). However, the apical third of Group 1 samples (5.25% NaOCl + 17% EDTA) (2.95 ± 0.33) exhibited the least efficient elimination of SL from the radicular dentin as well as the lowest bond strength (5.11 ± 0.19 MPa) of zirconia post to the dentin. The SYMPA technique with 17% EDTA proved highly effective in removing the SL from canal dentin and enhancing the EBS of zirconia posts. The least preferable method for SL removal and MH improvement was found to be 5.25% NaOCl + 17% EDTA. CQDs and Nd: YAG laser demonstrated satisfactory smear layer removal properties from the canal, along with achieving appropriate bond strength of zirconia posts. RESEARCH HIGHLIGHTS: Nd: YAG laser and 17% EDTA as canal disinfectant exhibited the highest values of MH. Specimens irrigated with SYMPA and 17% EDTA eliminated SL from the canal with the greatest efficacy. The coronal third of Group 3 (SYMPA + 17% EDTA) samples unveiled the highest zirconia post-bond integrity score to the canal dentin. Cohesive failure was a dominant failure type among different experimental groups.

Dental Resin-Based Luting Materials-Review

As cementation represents the last stage of the work involved in making various indirect restorations (metal ceramic crowns and bridges, full ceramic crowns and bridges, inlays, onlays, and fiber posts), its quality significantly contributes to the clinical success of the therapy performed. In the last two decades, the demand for ceramic indirect restorations in everyday dental practice has considerably increased primarily due to the growing significance of esthetics among patients, but also as a result of hypersensitivity reactions to dental alloys in some individuals. In this context, it is essential to ensure a permanent and reliable adhesive bond between the indirect restoration and the tooth structure, as this is the key to the success of aesthetic restorations. Resin-based luting materials benefit from excellent optical (aesthetic) and mechanical properties, as well as from providing a strong and durable adhesive bond between the restoration and the tooth. For this reason, resin cements are a reliable choice of material for cementing polycrystalline ceramic restorations. The current dental material market offers a wide range of resin cement with diverse and continually advancing properties. In response, we wish to note that the interest in the properties of resin-based cements among clinicians has existed for many years. Yet, despite extensive research on the subject and the resulting continued improvements in the quality of these materials, there is still no ideal resin-based cement on the market. The manuscript authors were guided by this fact when writing the article content, as the aim was to provide a concise overview of the composition, properties, and current trends, as well as some future guidelines for research in this field that would be beneficial for dental practitioners as well as the scientific community. It is extremely important to provide reliable and succinct information and guidelines for resin luting materials for dental dental practitioners.

Bond strength of various post-core restorations with different lengths and diameters following cycle loading

PURPOSE

This in vitro study aims to evaluate the bonding strengths of Polyether ether ketone (PEEK), Polyether ketone (PEKK), Fiber, and Zirconia (ZrO₂) post-core restorations with posts in different diameter and length following chewing simulator.

MATERIALS AND METHODS

Endodontic treatment was performed on 256 intact maxillary central teeth. The test specimens were prepared in four groups according to the types of materials: Glass fiber post-composite core (FB-n:64), Zirconia post-core (Zr-n:64), PEEK post-core (PE-n:64), and PEKK post-core (PK-n:64). The groups were divided into four subgroups according to diameter and length (n:16): Group 1: 10 mm length 1.75 mm diameter, Group 2: 10 mm length 1.5 mm diameter, Group 3: 7 mm length 1.75 mm diameter, Group 4: 7 mm length 1.5 mm diameter. Custom PEKK, PEEK, Zirconia post-cores, and Zirconia crowns were milled on the CAD/CAM. The post-cores and crowns were cemented to the teeth with dual-cure resin cement. After that, all subgroups were divided into control and cyclic loading groups. During the cycling, the control test group was kept in distilled water at 37±1^oC before the push-out test. Half of the specimens were loaded with 250,000 cycles and 50 N with a chewing simulator. All test specimens had 1.5 mm sections taken from their roots. Then, the push-out test was applied to these sections for bond strength. Data were analyzed by Mann-Whitney U test, Shapiro-Wilk, Kruskal-Wallis's test, and Chi-Square. The statistical significance level was determined as 0.05.

RESULTS

The bond strength of all test groups decreased after the cycling loading. The bond strength values of zirconia posts showed a statistically significant difference (p < 0.05). The 10 mm length 1.75 mm diameter posts made of Zirconium had the highest bond strength observed in all control and cyclic loading groups of test specimens (9.74 MPa-6.25 MPa). The PEEK test specimens with a 7 mm length and 1.75 mm diameter showed the weakest bond strength in all control and cyclic loading groups (5.44 MPa-3.37 MPa). The average of the cervical region's bond strength values was statistically significantly higher than the apical region (p < 0.05).

CONCLUSION

Within the limitations of this study, one-piece custom-milled Zirconia post-cores appear promising, as they perform well under functional forces, especially in the anterior region. In addition, custom-milled PEKK post-cores might be considered a suitable alternative to prefabricated fiber-reinforced posts.