Physicochemical and Functional Properties of Modified KJ CMU-107 Rice Starches as Pharmaceutical Excipients

Sodium Starch Glycolate (SSG) from Sago Starch (Metroxylon sago) as a Superdisintegrant: Synthesis and Characterization

The characteristics of sago starch exhibit remarkable resemblances to those of cassava, potato, and maize starches. This review intends to discuss and summarize the synthesis and characterization of sodium starch glycolate (SSG) from sago starch as a superdisintegrant from published journals using keywords in PubMed, Scopus, and ScienceDirect databases by Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA 2020). There are many methods for synthesizing sodium starch glycolate (SSG). Other methods may include the aqueous, extrusion, organic solvent slurry, and dry methods. Sago starch is a novel form of high-yield starch with significant development potential. After cross-linking, the phosphorus content of sago starch increases by approximately 0.3 mg/g, corresponding to approximately one phosphate ester group per 500 anhydroglucose units. The degree of substitution (DS) of sodium starch glycolate (SSG) from sago ranges from 0.25 to 0.30; in drug formulations, sodium starch glycolate (SSG) from sago ranges from 2% to 8% w/w. Higher levels of sodium starch glycolate (SSG) (2% and 4% w/w) resulted in shorter disintegration times (within 1 min). Sago starch is more swellable and less enzymatically digestible than pea and corn starch. These investigations demonstrate that sago starch is a novel form of high-yield starch with tremendous potential for novel development as superdisintegrant tablets and capsules.

Fabrication and Characterization of Orodispersible Composite Film from Hydroxypropylmethyl Cellulose-Crosslinked Carboxymethyl Rice Starch

Crosslinked carboxymethyl rice starch (CLCMRS), prepared via dual modifications of native rice starch (NRS) with chloroacetic acid and sodium trimetaphosphate, was employed to facilitate the disintegration of hydroxypropylmethylcellulose (HPMC) orodispersible films (ODFs), with or without the addition of glycerol. Fabricated by using the solvent casting method, the composite films, with the HPMC--LCMRS ratios of 9:1, 7:1, 5:1 and 4:1, were then subjected to physicochemical and mechanical evaluations, including weight, thickness, moisture content and moisture absorption, swelling index, transparency, folding endurance, scanning electron microscopy, Fourier transform infrared spectroscopy, tensile strength, elongation at break, and Young’s modulus, as well as the determination of disintegration time by using the Petri dish method (PDM) and slide frame and bead method (SFM). The results showed that HPMC-CLCMRS composite films exhibited good film integrity, uniformity, and transparency with up to 20% CLCMRS incorporation (4:1 ratio). Non-plasticized composite films showed no significant changes in the average weight, thickness, density, folding endurance (96−122), tensile strength (2.01−2.13 MPa) and Young’s modulus (10.28−11.59 MPa) compared to HPMC film (135, 2.24 MPa, 10.67 MPa, respectively). On the other hand, the moisture content and moisture absorption were slightly higher, whereas the elongation at break (EAB; 4.31−5.09%) and the transparency (4.73−6.18) were slightly lowered from that of the HPMC film (6.03% and 7.03%, respectively). With the addition of glycerol as a plasticizer, the average weight and film thickness increased, and the density decreased. The folding endurance was improved (to >300), while the transparency remained in the acceptable range. Although the tensile strength of most composite films decreased (0.66−1.75 MPa), they all exhibited improved flexibility (EAB 7.27−11.07%) while retaining structural integrity. The disintegration times of most composite films (PDM 109−331, SFM 70−214 s) were lower than those of HPMC film (PDM 345, SFM 229 s). In conclusion, the incorporation of CLCMRS significantly improved the disintegration time of the composite films whereas it did not affect or only slightly affected the physicochemical and mechanical characteristics of the films. The 5:1 and 4:1 HPMC:CLCMRS composite films, in particular, showed promising potential application as a film base for the manufacturing of orodispersible film dosage forms.