Research on Friction and Wear Properties of Rubber Composites by Adding Glass Fiber during Mixing

Effects of the etching process on the surface, friction and wear characteristics of silicone rubber coated with micro-sized ceramic particles

This study investigates the friction and wear characteristics of silicone rubber used in hydraulic systems, focusing on surface properties achieved through coating strategies. Silicone rubber specimens with varying surface characteristics, prepared by coating with micro-sized ceramic particles and employing etching processes, were examined. Surface morphology, roughness, water droplet contact angles, and friction and wear characteristics were evaluated. The silicone rubber was coated with ceramic particles (average size: 16 μm) and subsequently etched for different durations (1, 5, 10, 30, and 60 minutes). The results revealed that longer etching times led to increased surface roughness, while shorter etching times resulted in improved wear characteristics. The friction coefficient demonstrated a discernible reduction with escalating etching durations, with Etching-60M showing approximately 50% lower friction coefficient compared to Etching-1M. Wear rates ranged from 2.47 × 10-7 to 1.43 × 10-6 mm3 N-1 mm-1, indicating an increasing trend with longer etching times. Distinct wear mechanisms were observed between non-etched and etched specimens, with the latter exhibiting more pronounced wear tracks. Finite element analysis highlighted variations in stress behavior during contact sliding, indicating that surface modifications significantly impact wear resistance. While longer etching times improved friction characteristics, shorter etching times yielded superior wear characteristics. Further research is recommended to explore optimal etching conditions considering various variables.

Assessment of the Influence of Protective Polymer Coating on Panda Fiber Performance Based on the Results of Multivariant Numerical Simulation

This article considers the deformation behavior of Panda optical fiber using different models of material behavior for the tasks of predicting residual stresses after drawing when cooling from 2000 °C to room temperature (23 °C) and indenting the fiber into an aluminum half-space at different parameters. These studies were conducted for single- and double-layer protective coatings (PCs), at different values of external load and thickness of single-layer PC. This paper determined the fields of residual stresses in the fiber formed during the drawing process. They are taken into account in modeling the fiber performance in the further process of this research. This article investigated two variants of PC behavior. The influence of behavior models and the number of covering layers on the deformation of the "fiber-half-space" system was analyzed. This paper establishes qualitative and quantitative regularities of the influence of the external load magnitude and relaxation properties of PCs on the deformation and optical characteristics of Panda optical fiber.