Riowruangsanggoon D, Riddhabhaya A, Niyomtham N, Sirisoontorn I. Shear Bond Strength of Polypropylene Fiber in Orthodontic Adhesive on Glazed Monolithic Zirconia.
Polymers (Basel) 2022;
14:4627. [PMID:
36365620 PMCID:
PMC9658274 DOI:
10.3390/polym14214627]
[Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 10/11/2022] [Revised: 10/23/2022] [Accepted: 10/24/2022] [Indexed: 11/06/2022] Open
Abstract
This study aims to compare shear bond strength (SBS) and mode of failure (MOF) between ceramic and metal orthodontic brackets on glazed monolithic zirconia using non-woven polypropylene fiber adhesive. Sixty glazed and sintered zirconia blocks were divided into six groups and attached with orthodontic brackets as follows: CS, ceramic bracket with silane; CB, ceramic bracket with bonding agent; CBS, ceramic bracket with bonding agent and silane; MS, metal bracket with silane; MB, metal bracket with bonding agent; and MBS, metal bracket with bonding agent and silane. There was a statistically significant difference in mean SBS values (p < 0.001). The CS group showed the highest SBS value (23.42 ± 3.88 MPa). On the other hand, the lowest was found in the MB group, which was not statistically different from the CB group (3.26 ± 0.76 and 5.09 ± 1.50 MPa, respectively). The MS, MBS, and CBS groups showed no statistical difference compared to each other (15.57 ± 4.01, 13.23 ± 5.47, and 12.77 ± 4.43 MPa, respectively). SBS is highest when a ceramic bracket with silane is bonded to glazed monolithic zirconia.
Collapse