Flexible Investment Casting Wax Patterns for 3D-Printing: Their Rheological and Mechanical Characterizations

Experimental Study on Warpage Phenomenon of Wax Parts Manufactured by Fused Filament Fabrication

Warpage is one of the prominent issues in Fused Filament Fabrication. The cause of this is the rapid cooling of the polymer during extrusion. The residual thermal stresses accumulated within the print part result in a shape distortion and subsequent detachment of the object from the print bed. In this study, both experimental and numerical approaches were used to identify the stresses due to thermal shrinking that occurs in soft polymers such as wax. A temperature sweep test was performed using a rotational rheometer to measure the magnitude of axial forces that are generated due to the thermal shrinking of a thin layer of 3D printable wax. The thermal stresses responsible for warpage were computed analytically and using the FEA. It was found that due to thermal processes, the stress magnitude can reach a value of 1.17 MPa. This value is enough to cause the plastic deformation in the wax part having a thin elongated shape. In addition, Taguchi's robust design has identified two major FFF parameters that impact the warpage in amorphous soft polymers. They are the printing speed and the print bed temperature. To achieve a low level of warpage, it is important to make sure that the layer deposition occurs at medium speeds and the print bed temperature is moderately high according to the findings of this study.

The Effect of Heat Treatment on a 3D-Printed PLA Polymer's Mechanical Properties

Three-dimensional printing is a useful and common process in additive manufacturing nowadays. The advantage of additive polymer technology is its rapidity and design freedom. Polymer materials' mechanical properties depend on the process parameters and the chemical composition of the polymer used. Mechanical properties are very important in product applicability. The mechanical properties of polymers can be enhanced by heat treatment. Additive-manufactured PLA's mechanical properties and structure can be modified via heat treatment after the 3D printing process. The goal of this research was to test the effect of heat treatment on the mechanical and structural parameters of additive-manufactured PLA. This was achieved via the FDM processing of standard PLA tensile test specimens with longitudinal and vertical printing orientations. After printing, the test specimens were heat-treated at 55 °C, 65 °C and 80 °C for 5 h and after being held at 20 °C for 15 h. The printed and heat-treated specimens were tested using tensile tests and microscopy. Based on the test results, we can conclude that the optimal heat treatment process temperature was 65 °C for 5 h. Under the heat treatment, the test specimens did not show any deformation, the tensile strength increased by 35% and the porosity of the PLA structure decreased.