Atomistic Simulation of Flow-Induced Microphase Separation and Crystallization of an Entangled Polyethylene Melt Undergoing Uniaxial Elongational Flow and the Role of Kuhn Segment Extension

Chain-Level Analysis of Reinforced Polyethylene through Stretch-Induced Crystallization

Herein, we propose a large-scale simulation approach to perform the stretch-induced crystallization of entangled polyethylene (PE) melts. Sufficiently long (1000 ns) united-atom molecular dynamics (UAMD) simulations for 16000 chains of 1000 consecutive CH2 united-atom particles under periodic boundary conditions were performed to achieve the crystallinity observed in experiments. Before the isothermal crystallization process, we applied uniaxial stretching as pre-elongation to the embedded strain memory on the entangled PE melts. We confirmed significant differences in the morphologies of crystal domains and scattering patterns for pre-elongation ratios of 400% and 800%. The obtained scattering patterns were consistent with the experimental results. Uniaxial stretching MD simulations revealed that the elastic modulus at 800% pre-elongation was stronger than that at 400% pre-elongation. From this observation, we can derive the structure-property relationship, wherein the magnitude of the pre-elongation governs the crystal domain structures and mechanical properties.

Preparation and Characterization of High-Density Polyethylene with Alternating Lamellar Stems Using Molecular Dynamics Simulations

Mechanical recycling is the most efficient way to reduce plastic pollution due to its ability to maintain the intrinsic properties of plastics as well as provide economic benefits involved in other types of recycling. On the other hand, molecular dynamics (MD) simulations provide key insights into structural deformation, lamellar crystalline axis (c-axis) orientations, and reorganization, which are essential for understanding plastic behavior during structural deformations. To simulate the influence of structural deformations in high-density polyethylene (HDPE) during mechanical recycling while paying attention to obtaining an alternate lamellar orientation, the authors examine a specific way of preparing stacked lamella-oriented HDPE united atom (UA) models, starting from a single 1000 UA (C1000) chain of crystalline conformations and then packing such chain conformations into 2-chain, 10-chain, 15-chain, and 20-chain semi-crystalline models. The 2-chain, 10-chain, and 15-chain models yielded HDPE microstructures with the desired alternating lamellar orientations and entangled amorphous segments. On the other hand, the 20-chain model displayed multi-nucleus crystal growth instead of the lamellar-stack orientation. Structural characterization using a one-dimensional density profile and local order parameter {P2(r)} analyses demonstrated lamellar-stack orientation formation. All semi-crystalline models displayed the total density (ρ) and degree of crystallinity (χ) range of 0.90-0.94 g/cm-3 and ≥42-45%, respectively. A notable stress yield (σ_yield) ≈ 100-120 MPa and a superior elongation at break (ε_break) ~250% was observed under uniaxial strain deformation along the lamellar-stack orientation. Similarly, during the MD simulations, the microstructure phase change represented the average number of entanglements per chain (). From the present study, it can be recommended that the 10-chain alternate lamellar-stack orientation model is the most reliable miniature model for HDPE that can mimic industrially relevant plastic behavior in various conditions.