Biofilm Formation on the Surfaces of CAD/CAM Dental Polymers

Changes in the surface texture of pre-polymerized acrylic resin pediatric crowns following acidulated phosphate fluoride application

This study aimed to investigate the effect of acidulated phosphate fluoride (APF) application on filler-free polymethyl methacrylate (PMMA)-based resin blocks for computer-aided design/computer-aided manufacturing (CAD-CAM), focusing on their use in pediatric crowns. Three types of PMMA-based blocks for CAD-CAM were evaluated, and a composite resin block for CAD-CAM was used as a control. Statistical analysis (p<0.05) of the data revealed that all PMMA-based blocks showed significantly higher gloss levels than the composite resin blocks. Two PMMA-based blocks also demonstrated significantly lower Ra and Sa values. SEM images showed no irregular changes in the surface properties of the PMMA-based blocks compared to those of the composite resin block. These results are significant in meeting the increasing demand for esthetic restorative treatments in pediatrics, where APF is commonly used for caries prevention. PMMA-based resin blocks for CAD-CAM are an effective alternative to prevent esthetic degradation from gloss reduction and plaque accumulation.

Evaluation of early bacterial adhesion on CAD/CAM dental materials: an in situ study

The aim of this research was to determine if there are differences in early bacterial adhesion among CAD/CAM dental materials after 24 h exposure in the oral environment. One hundred twenty specimens were prepared according to the manufacturer's recommendations and divided into six groups: RBC (resin-based composite), PMMA (polymethyl methacrylate), PEEK (polyether ether ketone), ZP (zirconia polished), ZG (zirconia glazed), and cobalt-chromium alloy (CoCr alloy). Twenty healthy participants were instructed to carry an intraoral device with six specimens, one per group, for 24 h. Thereafter, real-time polymerase chain reaction (qPCR) and scanning electron microscopy (SEM) analyses enabled quantification and 2D view of biofilm formed on the specimens' surfaces. Kruskal-Wallis test and Dunn's post hoc analysis were used for inter-group comparison and data were presented as median (minimum-maximum). RBC specimens accumulated less bacteria, in comparison with ZG (p = 0.017) and PEEK specimens (p = 0.030), that dominated with the highest amount of adhered bacterial biofilm. PMMA, CoCr, and ZP specimens adhered more bacteria than RBC (p > 0.05), and less than ZG (p > 0.05) and PEEK (p > 0.05). The bacterial number varied considerably among participants. The obtained results enable a closer view into the susceptibility of CAD/CAM materials to microorganisms during the presence in the oral environment, which can be beneficial for a proper selection of these materials for a variety of dental restorations.

Considerations about Cytotoxicity of Resin-Based Composite Dental Materials: A Systematic Review

The dental material industry is rapidly developing resin-based composites (RBCs), which find widespread use in a variety of clinical settings. As such, their biocompatibility has gained increasing interest. This literature review presents a summary of research into the cytotoxicity of methacrylate-based composites published from 2017 to 2023. Subject to analysis were 14 in vitro studies on human and murine cell lines. Cytotoxicity in the included studies was measured via MTT assay, LDH assay, and WST-1 assay. The QUIN Risk of Bias Tool was performed to validate the included studies. Included studies (based entirely on the results of in vitro studies) provide evidence of dose- and time-dependent cytotoxicity of dental resin-based composites. Oxidative stress and the depletion of cellular glutathione (GSH) were suggested as reasons for cytotoxicity. Induction of apoptosis by RBCs was indicated. While composites remain the golden standard of dental restorative materials, their potential cytotoxicity cannot be ignored due to direct long-term exposure. Further in vitro investigations and clinical trials are required to understand the molecular mechanism of cytotoxicity and produce novel materials with improved safety profiles.

Bonding Characteristics of Silane Coupling Agent and MMA-Containing Primer to Various Composite CAD/CAM Blocks

This study evaluated the bonding characteristics of a silane coupling agent (SCA) and a methyl methacrylate (MMA)-containing primer (MCP) for 11 types of commercial composite blocks (CBs) for sandblasted and non-sandblasted surfaces. The shear bond strength (SBS) was measured according to ISO 29022: Notched-edge shear bond strength test. The SBS results demonstrated statistically significant differences between the CBs under all identical conditions. For the non-sandblasted groups, the SBSs of MCP-treated specimens were significantly higher than those of SCA-treated specimens for all but two CBs. Comparing the two treatments in sandblasted groups, the SBS was significantly higher for seven out of 11 MCP-treated RCB specimens, in contrast with three cases for the SCA-treated group. Two-way ANOVA for SBS showed the interaction effect between sandblasting and primer type for specific CBs, indicating that the sandblasting treatment improved SBS more effectively for SCA-treated specimens. Moreover, the effect of the SCA treatment was more material-dependent compared to that of the MCP treatment, which did not achieve a strong bond in all CBs but proved more effective than the SCA treatment, especially for non-sandblasted surfaces.