Is Gutta-Percha Still the “Gold Standard” among Filling Materials in Endodontic Treatment?

Tensile Strength and Elastic Modulus of Gutta-percha Cones Disinfected with Sodium Hypochlorite at Different Immersion Times: An In Vitro Comparative Study

Aim

The tensile strength and modulus of elasticity of gutta-percha cones can be chemically altered due to disinfectant solutions. Therefore, the aim of the present study was to compare tensile strength and elastic modulus of gutta-percha cones subjected to sodium hypochlorite (NaOCl) disinfection at different times.

Materials and Methods

This in vitro and longitudinal experimental study consisted of 45 gutta-percha cones, divided equally into three groups: Group 1 (disinfection with 2.5% NaOCl), Group 2 (disinfection with 5.25% NaOCl), and control group. All groups were subdivided according to immersion times for 1, 5, and 10 minutes. Tensile strength and elastic modulus were measured with a universal testing machine. For comparing more than two independent groups, parametric analysis of variance test with Sheffe's post hoc was used and for multivariate analysis, and multivariate analysis of variance test based on Pillai's Trace was used. In all statistical analysis, a significance level P ≤ 0.05 was considered.

Results

When comparing the tensile strength of gutta-percha cones, no significant differences were observed after being immersed at 1, 5, and 10 minutes in NaOCl 2.5% (P = 0.715) and 5.25% (P = 0.585). Regarding the elastic modulus, a significant decrease (P < 0.05) was observed in those that were immersed in NaOCl 2.5% and 5.25% for 1, 5, and 10 minutes. Furthermore, increased NaOCl concentration significantly reduced the elastic modulus (P < 0.001). However, there were no significant differences in tensile strength (P > 0.05) and elastic modulus (P > 0.05), when evaluating the interaction between NaOCl concentration and time.

Conclusion

Increasing NaOCl concentration significantly reduced the modulus of elasticity without affecting the tensile strength of gutta-percha cones, regardless of immersion time. Furthermore, the interaction of time and NaOCl concentration did not significantly affect the tensile strength and elastic modulus.

Use of micro-CT to examine effects of heat on coronal obturation

PURPOSE

The aim of this study was to categorize the effects of heat on coronal obturation with gutta-percha and sealer using X-ray micro-computed tomography (micro-CT).

METHODS

Ten single-rooted, extracted human teeth were shaped using ProTaper NEXT files to size X5 (#50/Taper 6%) with 2.5% NaOCl irrigation. A single ProTaper NEXT X5 gutta-percha point was then inserted with epoxy resin (AH Plus) or tricalcium silicate (EndoSequence BC) sealer (n = 5/group), and cut at the cemento-enamel junction. The teeth were scanned using micro-CT (SkyScan1272) to obtain 11 sagittal 2-D images. Three calibrated raters categorized the coronal 0.5 mm of the images into four categories: "swirled sealer and/or gutta-percha without voids" (I), "uniform voids and sealer/gutta-percha" (II), "non-uniform voids and sealer/gutta-percha" (III), and "swirled sealer and/or gutta-percha with voids" (IV). Intra-rater and inter-rater reliability were then calculated. Chi-square tests were conducted to determine the significance of differences in each category between sealers.

RESULTS

The intra-class correlation coefficient was 0.55 (same rater/two different times) and Fleiss' kappa (different raters/same image) was 0.34. Categories I, II, III, and IV accounted for 16.4%, 4.2%, 30.3%, and 49.1% for AH Plus, and 6.7%, 4.2%, 27.3%, and 61.8% for EndoSequence BC, respectively.

CONCLUSION

Category IV was most common and Category II the least common. Significant differences were evident between sealers for Category I (P < 0.01).

Coronal and apical leakage among five endodontic sealers

PURPOSE

The aim of this study was to use dye penetration to measure apical and coronal leakage simultaneously in single-canal teeth that had been treated endodontically using a single-cone obturation technique.

METHODS

One hundred single-canal, extracted human teeth were cleaned and shaped with ProTaper NEXT rotary files to size-X5 (50/.06), then randomly assigned to five sealer groups for single-cone gutta-percha obturation. The teeth were soaked in 0.6% rhodamine B at 37°C for seven days, then the roots were ground mesiodistally and the maximum apical and coronal dye penetration was measured. Differences in leakage among the sealer groups were examined using the Kruskal-Wallis test. Pairwise comparisons were made using the Mann-Whitney test with Bonferroni correction.

RESULTS

The mean values (mm) of dye penetration for AH Plus, Pulp Canal Sealer, NeoSEALER Flo, EndoSequence BC, and Super-Bond RC Sealer were 0.200, 0.300, 0.675, 0.850, and 0.900 apically, whereas 1.675, 2.075, 4.800, 6.500, and 4.125 coronally. Pairwise comparisons showed significant apical differences between AH Plus/Super-Bond RC Sealer (P = 0.047) and significant coronal differences between AH Plus/NeoSEALER Flo (P = 0.001), AH Plus/EndoSequence BC (P < 0.01), AH Plus/Super-Bond RC Sealer (P < 0.01), Pulp Canal Sealer/NeoSEALER Flo (P = 0.010), Pulp Canal Sealer/EndoSequence BC (P < 0.01), and Pulp Canal Sealer/Super-Bond RC Sealer (P < 0.01).

CONCLUSION

Coronal leakage was worse than apical leakage for all sealers. AH Plus exhibited the least leakage apically and coronally; Super-Bond RC Sealer showed the most leakage apically, and EndoSequence BC showed the most leakage coronally.

Nitinol Type Alloys General Characteristics and Applications in Endodontics

A very extensive literature review presents the possibilities and needs of using, in endodontics, the alloys commonly known as nitinol. Nitinol, as the most modern group of engineering materials used to develop root canals, is equilibrium nickel and titanium alloys in terms of the elements’ atomic concentration, or very similar. The main audience of this paper is engineers, tool designers and manufacturers, PhD students, and students of materials and manufacturing engineering but this article can also certainly be used by dentists. The paper aims to present a full material science characterization of the structure and properties of nitinol alloys and to discuss all structural phenomena that determine the performance properties of these alloys, including those applied to manufacture the endodontic tools. The paper presents the selection of these alloys’ chemical composition and processing conditions and their importance in the endodontic treatment of teeth. The results of laboratory studies on the analysis of changes during the sterilization of endodontic instruments made of nitinol alloys are also included. The summary of all the literature analyses is an SWOT analysis of strengths, weaknesses, opportunities, and threats, and is a forecast of the development strategy of this material in a specific application such as endodontics.

Development Strategy of Endodontic Filling Materials Based on Engineering and Medical Approaches

This article is a literature review aimed at presenting the general state of knowledge in manufacturing engineering and materials engineering to develop engineering materials applied for endodontic treatment as filling materials. Particular attention was paid to theoretical analyses concerning the selection of methods for developing and obturating root canals and discussing the results of experimental studies available in the literature. These activities aimed to compare the importance of the most commonly used endodontic filling materials based on gutta-percha or polymeric polyester materials, commonly known as resilon, respectively. The motivation to take up this complex, multi-faceted topic in this paper is the extent of caries, periodontal disease, and other oral diseases in 3 to 5 billion people, often affecting toothlessness and contributing to an increase in the index of disability-adjusted life years (number). Endodontics is an important element of the authors’ concept of Dentistry Sustainable Development (DSD) > 2020. The principles of qualifying patients for endodontic treatment are discussed. The introduction of rotary tools, especially manufactured from Nitinol alloy, to develop root canals and the latest thermohydraulic and condensation techniques for obturation guarantee progress in endodontics. The “Digital Twins” methodology was used, rooted in the idea of Industry 4.0 and the resulting idea of Dentistry 4.0, as well as knowledge management methods, to perform experimental research in virtual space, concerning methods of developing and obturating the root canal and assessing the tightness of fillings. Microscopic visualization methods were also used. Significant factors determining the effectiveness of endodontic obturation are the selection of the filling material and the appropriate obturation method. The generalized dendrological matrix of endodontic filling materials considers the criteria of mechanical strength influencing the potential root fracture and the quality of root canal filling. The results of the SWOT point analysis (strengths and weaknesses, opportunities, threats) were also compared. For both filling materials, the weaknesses are much less than the strengths, while the threats are slightly less than the opportunities for the gutta-percha-based material, while for resilon the opportunities are much smaller than the threats. It requires the application of an appropriate development strategy, i.e., MAXI-MAXI in the case of a filling material based on gutta-percha and MAXI-MINI in the case of resilon. Therefore, the analysis of these experimental data does not indicate the real competitiveness of resilon for the gutta-percha-based material. This material deservedly maintains its strong position as the “Gold Standard of Endodontics”.

What Are the Chances of Resilon to Dominate the Market Filling Materials for Endodontics?

This paper is a literature review with additional virtual analyses of the authors’ own experimental research results. Knowledge from various areas was synergistically combined, appropriately for concurrent engineering, presenting several possible methodological approaches used in research, optimizing the selection of engineering materials and the conditions of their application with particular application in endodontics. Particular attention was paid to the theoretical aspects of filling material strengths, weaknesses, opportunities, and threats SWOT analysis. Attention was paid to the original concepts of Sustainable Dentistry Development in conjunction with Dentistry 4.0, which includes endodontics as an important element. The dentists’ actions, among others, in conservative dentistry, along with endodontics, requires close cooperation with engineers and the enginering sciences. Methods of root canal preparation were described, together with selected tools, including those made of nitinol. Principles concerning the process of cleaning and shaping the pulp complex are presented. The importance of obturation methods, including the Thermo-Hydraulic-Condensation THC technique, and the selection of filling materials with the necessary sealants for the success of endodontic treatment are discussed. The experimental studies were carried out in vitro on human teeth removed for medical reasons, except for caries, for which two groups of 16 teeth were separated. After the root canal was prepared, it was filled with studs and pellets of a filling material based on polyester materials, which has gained the common trade name of resilon or, less frequently, RealSeal (SybronEndo) with an epiphany sealant. The teeth for the first group were obturated by cold lateral condensation. In the second case the obturation was performed using the Thermo-Hydraulic-Condensation technique using System B and Obtura III. The experimental leakage testing was done using a scanning electron microscope SEM and a light stereoscopic microscope LSM, as typical research tools used in materialography. The research results, in a confrontation with the data taken from the literature studies, do not indicate the domination of resilon in endodontics.