Restoring the Reactivity of Organic Acid Solution Used for Silver Recovery from Solar Cells by Fractional Distillation

Studies on Polybenzimidazole and Methanesulfonate Protic-Ionic-Liquids-Based Composite Polymer Electrolyte Membranes

In the present work, different methanesulfonate-based protic ionic liquids (PILs) were synthesized and their structural characterization was performed using FTIR, ¹H, and ¹³C NMR spectroscopy. Their thermal behavior and stability were studied using DSC and TGA, respectively, and EIS was used to study the ionic conductivity of these PILs. The PIL, which was diethanolammonium-methanesulfonate-based due to its compatibility with polybenzimidazole (PBI) to form composite membranes, was used to prepare proton-conducting polymer electrolyte membranes (PEMs) for prospective high-temperature fuel cell application. The prepared PEMs were further characterized using FTIR, DSC, TGA, SEM, and EIS. The FTIR results indicated good interaction among the PEM components and the DSC results suggested good miscibility and a plasticizing effect of the incorporated PIL in the PBI polymer matrix. All the PEMs showed good thermal stability and good proton conductivity for prospective high-temperature fuel cell application.

Recovery of copper, zinc and lead from photovoltaic panel residue

The increase in photovoltaic panel installations in Europe will generate vast amounts of waste in the near future. Therefore, it is important to develop new technologies that allow the recycling of end-of-life photovoltaic panels. This material can serve as a secondary resource, not only for precious metals (e.g. silver), but also for base metals. In this work, the extraction and recovery of the base metals copper, zinc and lead from a copper-rich photovoltaic panel residue was investigated. The material was first leached at 80 °C under microwave irradiation with a mixture of hydrochloric acid, sodium chloride and hydrogen peroxide solutions. Based on the Box-Behnken factorial design optimization, it was possible to extract 81.2% of Cu, 96.4% of Zn and 77.6% of Pb, under the following leaching conditions: [HCl] = 0.5 mol L-1, [NaCl] = 200 g L-1, [H2O2] = 7.5 wt% and t = 60 min. Cementation with iron powder at a 1.2 iron-to-copper stoichiometric ratio allowed the recovery of copper nearly quantitatively (99.8%) as a copper-iron sediment. The gas-liquid separation technique of ion flotation was employed to separate lead and zinc from the dilute copper-free leachate. Cetyltrimethylammonium bromide (CTAB), a cationic surfactant, selectively recovered lead (99.4%) over zinc as lead(ii) tetrachloro cetyltrimethylammonium colloid, after eight ion flotation stages and [CTAB]total = 7.2 mmol L-1. The zinc that remained in the solution after the ion flotation step was recovered by precipitation and by adding sodium sulfide at 110% of the stoichiometric amount after removing iron as ferric hydroxide by slowly raising the pH to 3.7.