Novel Sustainable Castor Oil-Based Polyurethane Biocomposites Reinforced with Piassava Fiber Powder Waste for High-Performance Coating Floor

Effect of surface treatment on the technological properties of coconut fiber-reinforced plant polyurethane composites

Polymeric composites reinforced with plant fibers have numerous advantages, such as low cost, high raw material availability and good physical, mechanical and thermal properties. Thus, in recent years, they have been studied as thermal insulation substitutes for synthetic polymers in buildings. The aim of this study was to evaluate the technological properties of castor oil-based polyurethane composites reinforced with coconut fibers treated with hot water, alkaline solutions of NaOH and Ca(OH)₂ and corona discharge and without surface treatment as materials for the thermal insulation of buildings. The composites were produced by the hand lay-up method followed by compression; 10% by weight coconut fibers were used to replace the synthetic polymer. Specimens were produced, and physical, mechanical, thermal and microstructural tests were performed. The results showed that the polymer had a thermal conductivity of 0.016 W/(mK), while the composites produced with fibers treated with NaOH had a thermal conductivity of 0.028 W/(mK); therefore, these polymers are considered insulating materials (k = 0.01 to 1.0 W/(mK)). Thus, the composites produced with coconut fibers can be considered as lighter, less expensive and environmentally friendly alternatives to synthetic polymers.

Properties of Luffa Cylindrica Mats Reinforced Castor Oil-Based Polyurethane Composite as an Alternative for Oriented Strand Board

The main objective of this work was to produce and characterize a novel ecofriendly castor oil-based polyurethane (COPU) matrix composite reinforced by Luffa cylindrica mats, luffa for short, to be used as panels, as an alternative to oriented strand board (OSB). To do so, the mechanical behavior was evaluated by tree point flexural, perpendicular o surface tensile, screw pullout, and impact tests that were carried on the novel composite along with the neat matrix. Furthermore, the physical characteristics, the thermomechanical behavior, and the functional groups of the materials were observed by water absorption and thickness swelling tests along with dilatometry and Fourier transform infrared spectroscopy (FTIR). A comparison with commercialized OSB was also performed for control. The luffa/COPU composite was prepared by hand lay-up with 48 vol% of luffa mats incorporated as the maximum allowed by the mold under the available resources for manufacturing. The luffa fibers acted as a good reinforcement for the COPU matrix, where the flexural strength and modulus of elasticity were increased by more than 23 and 10 times, respectively, and the other mechanical properties more than doubled for the composites compared to the neat COPU resin. In general, the composite presented a lower performance compared to the commercial OSB, with the impact results being the exception. The water absorption and thickness swallowing results showed an already-expected behavior for the studied materials, where the better performance was found for the hydrophobic neat resin. The FTIR revealed that there was little interaction between luffa and COPU resin, which can be translated to a weak interface between these materials. However, the mechanical behavior, together with the other results presented by the luffa/COPU composite, confirm it is more than enough to be used as civil construction panels such as OSB.

Thermal and Sliding Wear Properties of Wood Waste-Filled Poly(Lactic Acid) Biocomposites

In our study, the effects of wood waste content (0, 2.5, 5, 7.5, and 10 wt.%) on thermal and dry sliding wear properties of poly(lactic acid) (PLA) biocomposites were investigated. The wear of developed composites was examined under dry contact conditions at different operating parameters, such as sliding velocity (1 m/s, 2 m/s, and 3 m/s) and normal load (10 N, 20 N, and 30 N) at a fixed sliding distance of 2000 m. Thermogravimetric analysis demonstrated that the inclusion of wood waste decreased the thermal stability of PLA biocomposites. The experimental results indicate that wear of biocomposites increased with a rise in load and sliding velocity. There was a 26-38% reduction in wear compared with pure PLA when 2.5 wt.% wood waste was added to composites. The Taguchi method with L₂₅ orthogonal array was used to analyze the sliding wear behavior of the developed biocomposites. The results indicate that the wood waste content with 46.82% contribution emerged as the most crucial parameter affecting the wear of PLA biocomposites. The worn surfaces of the biocomposites were examined by scanning electron microscopy to study possible wear mechanisms and correlate them with the obtained wear results.