Hydrogenation of ZnFe2O4 Flat Films: Effects of the Pre-Annealing Temperature on the Photoanodes Efficiency for Water Oxidation

Nature of Charge Carrier Recombination in CuWO4 Photoanodes for Photoelectrochemical Water Splitting

CuWO4 is a ternary semiconductor oxide with excellent visible light harvesting properties up to 550 nm and stability at high pH values, which make it a suitable material to build photoanodes for solar light conversion to hydrogen via water splitting. In this work, we studied the photoelectrochemical (PEC) performance of transparent CuWO4 electrodes with tunable light absorption and thickness, aiming at identifying the intrinsic bottlenecks of photogenerated charge carriers in this semiconductor. We found that electrodes with optimal CuWO4 thickness exhibit visible light activity due to the absorption of long-wavelength photons and a balanced electron and hole extraction from the oxide. The PEC performance of CuWO4 is light-intensity-dependent, with charge recombination increasing with light intensity and most photogenerated charge carriers recombining in bulk sites, as demonstrated by PEC tests performed in the presence of sacrificial agents or cocatalysts. The best-performing 580 nm thick CuWO4 electrode delivers a photocurrent of 0.37 mA cm-2 at 1.23 VSHE, with a 7% absorbed photon to current efficiency over the CuWO4 absorption spectrum.

Nanostructured ZnFe2O4: An Exotic Energy Material

More people, more cities; the energy demand increases in consequence and much of that will rely on next-generation smart materials. Zn-ferrites (ZnFe₂O₄) are nonconventional ceramic materials on account of their unique properties, such as chemical and thermal stability and the reduced toxicity of Zn over other metals. Furthermore, the remarkable cation inversion behavior in nanostructured ZnFe₂O₄ extensively cast-off in the high-density magnetic data storage, 5G mobile communication, energy storage devices like Li-ion batteries, supercapacitors, and water splitting for hydrogen production, among others. Here, we review how aforesaid properties can be easily tuned in various ZnFe₂O₄ nanostructures depending on the choice, amount, and oxidation state of metal ions, the specific features of cation arrangement in the crystal lattice and the processing route used for the fabrication.

Rational design of interface refining through Ti4+/Zr4+ diffusion/doping and TiO2/ZrO2 surface crowning of ZnFe2O4 nanocorals for photoelectrochemical water splitting

The interplay between diffusion/doping and surface passivation of TZF NCs exhibits a breakthrough photocurrent density of 0.73 mA cm⁻² (1.23 V vs. RHE) with 98% stability over 10 h in the TZF/Al₂O₃/CoO_x photoanode.

Stability of Non-Flexible vs. Flexible Inverted Bulk-Heterojunction Organic Solar Cells with ZnO as Electron Transport Layer Prepared by a Sol-Gel Spin Coating Method

In this research, inverted bulk heterojunction organic solar cells (BHJ OSC) with poly(3-hexylthiophene-2,5-diyl): (6,6)-phenyl C61 butyric acid methyl (P3HT:PCBM) as the active layer were fabricated by a sol-gel spin coating method using flexible PET and non-flexible glass as substrates. The power conversion efficiency (PCE) and the stability of the cells were investigated. According to the results, the non-flexible device showed higher short circuit current (Jsc) as well as open-circuit voltage (Voc) as compared to the flexible one so that 2.52% and 0.67% PCE for non-flexible and flexible cells were obtained, respectively. From the stability point of view, the non-flexible device maintained 51% of its initial efficiency after six weeks in a dark atmosphere, while it was about 19% for the flexible cell after four weeks. The most important reason for the higher PCE with the higher stability in the non-flexible cell can be attributed to its higher shunt resistance (Rsh) and better interlayer connections at the electron collector side.