Combination of Slag, Limestone and Sedimentary Apatite in Columns for Phosphorus Removal from Sludge Fish Farm Effluents

Environmental and Geotechnical Assessment of the Steel Slags as a Material for Road Structure

Slags are the final solid wastes from the steel industry. Their production from waste and associated materials is a proper implementation of the basic objectives and principles of the waste management. This study aims to investigate the chemical and selected significant geotechnical parameters of steel slag as the alternative materials used in road construction. These investigations are strongly desired for successful application in engineering. Young’s modules E, and resilient modules M_r showed that their values corresponding with requirements for subbase (principal or auxiliary) and riding surface as well. Tested mechanical properties were conducted in soaked and un-soaked (optimal moisture content) conditions. The designated high content of chromium and zinc are strongly associated with the internal crystal structure of steel slag. The results do not lead to threats when they are applied in roads’ structures. Mechanical characterization was obtained by performing California bearing ratio (CBR) tests for steel slag in fixed compaction and moisture content conditions. Moreover, cyclic loading of steel slag was conducted with the application of cyclic California bearing ratio (cCBR) apparatus to characterization of this material as a controlled low-strength material. Finally, field studies that consist of static load plate VSS tests were presented.

Chemical techniques for pretreating and regenerating active slag filters for improved phosphorus removal

Active slag filters are an emerging technology for removing phosphorus (P) from wastewaters. Recent research revealed that adsorption onto Fe oxides/oxyhydroxides at near-neutral pH and oxidizing Eh is the key mechanism of P removal by melter slag filters. Currently, filter lifespan is limited by available adsorption sites. This study examined whether the performance and longevity of active filters could be improved via chemical treatment to create additional reactive sites as well as regenerate exhausted ones. Fresh original melter slag as well as slag from an exhausted full-scale filter was tested. Chemical reagents that could manipulate the pH/Eh of the slag granule surfaces and potentially activate them for further P removal were used, namely hydrochloric acid (HCI), sodium hydroxide (NaOH) and sodium dithionite (Na2S2O4). Waste stabilization pond effluent was then applied to the treated slag to assess the effectiveness of the treatments at improving P removal. Fresh slag treated with Na2S204 and HCl, respectively, retained 1.9 and 1.4 times more P from the effluent than the untreated fresh slag. These reagents were even more effective at regenerating the exhausted slag, increasing total retained P by a factor of 13 and six, respectively, compared with untreated slag. Sodium hydroxide was ineffective at increasing P removal. The higher P retention by the 'treated exhausted slag' compared with the 'treated fresh media' indicates that adsorption sites on melter slag filters become increasingly reactive with time. This research is the first study to provide evidence that P retention by active slag filters can be increased by both (1) chemical pre treatment and (2) chemical post-treatment once their P removal is exhausted, thereby potentially transforming them from a single use system to a more viable, reusable treatment technology.