Assessment of surface roughness changes on orthodontic acrylic resins by all-in-one spray disinfectant solutions

In Vitro Comparative Evaluation of the Efficacy of Antimicrobial Photodynamic Therapy, Chlorhexidine, Sodium Fluoride, and Hydrogen Peroxide for Acrylic Resin Disinfection

Introduction: Plaque accumulation on the surface of removable orthodontic appliances could lead to dental caries, periodontitis, and fungal infections. This study evaluated the effectiveness of antimicrobial photodynamic therapy (aPDT), chlorhexidine (CHX), sodium fluoride (NaF), and hydrogen peroxide (H2O2) for the disinfection of acrylic resin. Methods: In this in vitro experimental study, 100 acrylic resin specimens were randomly divided into five groups (n=20 each): Enterococcus faecalis, Streptococcus mutans, Streptococcus salivarius, Streptococcus sanguinis, and Lactobacillus acidophilus. Each group was immersed separately in 5 mL of microbial suspension. They were then incubated until biofilm formation on their surface. Of each microorganism, one biofilm sample in phosphate-buffered saline was considered as negative control, and other biofilm samples (n=80) were subjected to aPDT with curcumin, 0.12% CHX (positive control), 1% H2O2, and 0.2% NaF. Finally, the number of colonies was counted. Data were analyzed by the Kruskal-Wallis and Mann-Whitney tests, two-way ANOVA, and Bonferroni adjustment at a significance level of 0.05. Results: The interaction effect of the treatment modality and type of microorganism was significant on the microbial count (effect size: 0.91, P<0.05). Maximum bacterial proliferation was noted in the following combinations: NaF/E. faecalis, H2O2/E. faecalis, and H2O2/S. salivarius. Microorganisms had no or insignificant growth and proliferation in the aPDT and CHX groups. Conclusion: The results supported the optimal antimicrobial efficacy of PDT which was comparable to that of CHX. aPDT showed superior antimicrobial efficacy to NaF and H2O2 for the disinfection of acrylic resin.

Wear Behavior and Surface Quality of Dental Bioactive Ions-Releasing Resins Under Simulated Chewing Conditions

Bioactive materials can reduce caries lesions on the marginal sealed teeth by providing the release of ions, such as calcium, phosphate, fluoride, zinc, magnesium, and strontium. The presence of such ions affects the dissolution balance of hydroxyapatite, nucleation, and epitaxial growth of its crystals. Previous studies mostly focused on the ion-releasing behavior of bioactive materials. Little is known about their wear behavior sealed tooth under mastication. This study aimed to evaluate the wear behavior and surface quality of dental bioactive resins under a simulated chewing model and compare them with a resin without bioactive agents. Three bioactive resins (Activa, BioCoat, and Beautifil Flow-Plus) were investigated. A resin composite without bioactive agents was used as a control group. Each resin was applied to the occlusal surface of extracted molars and subjected to in vitro chewing simulation model. We have assessed the average surface roughness (Ra), maximum high of the profile (Rt), and maximum valley depth (Rv) before and after the chewing simulation model. Vickers hardness and scanning electron microscopy (SEM) also analyzed the final material surface quality). Overall, all groups had increased surface roughness after chewing simulation. SEM analysis revealed a similar pattern among the materials. However, the resin with polymeric microcapsules doped with bioactive agents (BioCoat) showed increased surface roughness parameters. The material with Surface Pre-reacted Glass Ionomer (Beautifil Flow-Plus) showed no differences compared to the control group and improved microhardness. The addition of bioactive agents may influence surface properties, impairing resin composites' functional and biological properties. Future studies are encouraged to analyze bioactive resin composites under high chemical and biological challenges in vitro with pH cycles or in situ models.

An orthodontic acrylic resin containing seaweed Ulva lactuca as a photoactive phytocompound in antimicrobial photodynamic therapy: Assessment of anti-biofilm activities and mechanical properties

BACKGROUND

Uncontrolled accumulation of microbial plaque and formation of biofilm on the surface orthodontic acrylic removable appliances increases the risk of enamel decalcification and periodontal diseases. The purpose of the present study was to evaluate antimicrobial activities, anti-virulence potencies, and mechanical properties of orthodontic acrylic resin containing different concentrations of Ulva lactuca (a green marine macroalga) following photo-activation against Streptococcus mutans.

MATERIALS AND METHODS

Minimum inhibitory concentration (MIC) of U. lactuca was determined against S. mutans. Acrylic resin specimens with different concentrations of U. lactuca (0.2 %, 0.5 %, 1%, 2.5 %, 5%, and 10 % weight/weight) were fabricated. Flexural strength values, antimicrobial effects, and anti-biofilm activities of samples were assessed in comparison with original acrylic resin as the control group. Also, the expression of the virulence-associated genes was assessed by quantitative real-time polymerase chain reaction.

RESULTS

U. lactuca at concentrations of 1-10% significantly reduced the S. mutans growth rate by 20.3%-63.3% in comparison to the control group (P < 0.05). Therefore, the concentration of 1% of U. lactuca was considered as a MIC. The highest and lowest flexural strength values were observed in the control group (43.5 ± 2.4 MPa) and the group with a 10 % concentration of U. lactuca (19.2 ± 1.8 MPa), respectively. Flexural strength values decreased in samples containing 2.5 %, 5%, and 10 % concentrations of U. lactuca in comparison to the control group significantly (P > 0.05). In the disc agar diffusion test, the growth inhabitation zones around samples containing different concentrations of photo-activated U. lactuca ranged from 13 mm to 25 mm in diameter. Interestingly, the anti-biofilm activity of U. lactuca-mediated aPDT against S. mutans was dose-dependent. Additionally, the sub-MIC dose of U. lactuca (0.5 %) following photo-activation could significantly decrease the expression levels of gtfB, gtfC, and gtfD to 4.1-, 5.3-, and 7.4-fold, respectively.

CONCLUSIONS

Adding photo-activated U. lactuca to the orthodontic acrylic resin at a concentration of 1% increases its antibacterial and anti-biofilm activities besides not detrimentally affects its flexural strength.