Evaluation of single liquid primers with organic sulfur compound for bonding between indirect composite material and silver-palladium-copper-gold alloy

Dental Alloy Adhesive Primers and Bond Strength at Alloy-Resin Interface: A Systematic Review and Meta-analyses

AIM

The present systematic review aimed to report the studies concerning the primers in improving bond strength and identifying pertinent primers for a particular dental alloy by adhering to PRISMA precepts.

MATERIALS AND METHODS

PubMed and Semantic Scholar databases were scoured for articles using 10 search terms. In vitro studies satisfying the inclusion criteria were probed which were meticulously screened and scrutinized for eligibility adhering to the 11 exclusion criteria. The quality assessment tool for in vitro studies (QUIN Tool) containing 12 criteria was employed to assess the risk of bias (RoB).

RESULTS

A total of 48 studies assessing shear bond strength (SBS) and 15 studies evaluating tensile bond strength (TBS) were included in the qualitative synthesis. Concerning SBS, 33.4% moderate and 66.6% high RoB was observed. Concerning TBS, 26.8% moderate and 73.2% high RoB was discerned. Seventeen and two studies assessing SBS and TBS, respectively, were included in meta-analyses.

CONCLUSIONS

Shear bond strength and TBS increased for the primed alloys. Cyclic disulfide primer is best-suited for noble alloys when compared with thiol/thione primers. Phosphoric acid- and phosphonic acid ester-based primers are opportune for base alloys.

CLINICAL SIGNIFICANCE

The alloy-resin interface (ARI) would fail if an inappropriate primer was selected. Therefore, the selection of an appropriate alloy adhesive primer for an alloy plays a crucial role in prosthetic success. This systematic review would help in the identification and selection of a congruous primer for a selected alloy.

Bonding performance of a thiohydantoin-methacrylate monomer on noble metal alloys

This study assessed the effect of a primer containing 10-methacryloyloxydecyl-(2-thiohydantoin-4-yl)propionate (MDTHP) on the bonding of noble metal alloys to an acrylic resin. Three noble metal alloys were selected as adherends, and V-Primer containing 6-(4-vinylbenzyl-n-propyl)amino-1,3,5-triazine-2,4-dithione was used as a comparative control. The disk specimens of each noble metal alloy were wet-ground and divided into three conditions: specimens primed with MDTHP primer or V-Primer, and specimens without priming. An acrylic resin was bonded to each specimen, and the specimens were performed the shear bond test. The MDTHP primer showed higher shear bond strength than the V-Primer for all specimens. X-ray photoelectron spectroscopic analysis showed that MDTHP was adsorbed on the Au-Pt-Pd alloy surface even after acetone cleaning. MDTHP binds not only with Cu but also with Au and Ag, promoting the bond strength of noble metal alloys. The effectiveness of MDTHP on dental noble metal alloys was suggested.

Chemical alteration of Ag-Pd-Cu-Au alloy surface by alumina air-abrasion and its effect on bonding to resin cement

The goal of this study was to investigate the chemical alteration of a dental alloy surface by alumina air-abrasion and its effect on bonding to resin cement. Alumina air-abrasion was carried out on an Ag-Pd-Cu-Au alloy. The surface morphology and chemical state of the abraded alloy were characterized. The effect of the air-abrasion on the shear bond strength between the alloy and a methyl methacrylate/tri-n-butyl borane (MMA/TBB) resin cement with some primers was evaluated. The surface characterization revealed that the alumina air-abrasion mechanically roughened and chemically altered the surface. The chemical alterations had two effects: (1) abraded alumina particles remained on the alloy surface and (2) copper ions were oxidized in the alloy surface. As the result, the shear bond strength test indicated that 10-methacryloyloxydecyl dihydrogen phosphate (MDP) contained primer worked with the abraded alloy surface, whereas it did not work with the non-abraded alloy surface.

Effect of thione primers on adhesive bonding between an indirect composite material and Ag-Pd-Cu-Au alloy

The current study evaluated the effect of primers on the shear bond strength of an indirect composite material joined to a silverpalladium-copper-gold (Ag-Pd-Cu-Au) alloy (Castwell). Disk specimens were cast from the alloy and were air-abraded with alumina. Eight metal primers were applied to the alloy surface. A light-polymerized indirect composite material (Solidex) was bonded to the alloy. Shear bond strength was determined both before and after the application of thermocycling. Two groups primed with Metaltite (thione) and M. L. Primer (sulfide) showed the greatest post-thermocycling bond strength (8.8 and 6.5 MPa). The results of the X-ray photoelectron spectroscopic (XPS) analysis suggested that the thione monomer (MTU-6) in the Metaltite primer was strongly adsorbed onto the Ag-Pd-Cu-Au alloy surface even after repeated cleaning with acetone. The application of either the thione (MTU-6) or sulfide primer is effective for enhancing the bonding between a composite material and Ag-Pd-Cu-Au alloy.