Effect of temperature on the mass and color stability of additional photoinitiatorcontaining composite resins

Can sterilization methods influence surface properties of resin composites? A purpose for previewing bias in laboratory bacterial adhesion tests

This study aimed to evaluate the influence of sterilization methods on conventional and bulk-fill resin composites' (BFRCs) surface properties in an attempt to preview bias in laboratory bacterial adhesion tests. Two regular viscosity conventional resin composites [Filtek Z350 XT™ (Z350) and IPS Empress Direct™ (ED)] and two regular viscosity BFRCs [Filtek Bulk Fill™ (FILT) and Tetric N-Ceram Bulk Fill IVA™ (TBF)] were used. The materials were characterized by Scanning Electron Microscopy (SEM), surface roughness (SR), and wettability (W) after sterilization with hydrogen peroxide gas plasma (HPGP) and steam sterilization (SS). Nonsterilized samples served as a control group (n = 5). Statistical analysis was performed using two-way analysis of variance (ANOVA) and Tukey post hoc test (p <  0.05). For SR, there were no statistically significant differences among the groups (p > .05). SS method decreased the contact angle for FILT and Z350 (p < .01). The SS promoted more exposition of filler particles, while the HPGP method did not alter the tested materials' morphology. Therefore, sterilization methods affected the resin composites tested selectively. HPGP seems to be the most recommended method to sterilize the tested resin composites before laboratory bacterial adhesion tests.

Retentive Force of Glass-Ceramic Soldered Customized Zirconia Abutment Copings with Prefabricated Titanium Bases

Two-piece abutments consisting of customized zirconia abutment copings and prefabricated titanium bases are popular due to their biological and esthetic advantages. Glass-ceramic solder (GS) is an alternative biocompatible connective agent. This in vitro study evaluated the retentive force of GS in comparison to classical resin composite cements (RC) after artificial aging and autoclaving. Ninety specimens consisting of prefabricated titanium bases and zirconia abutment copings were fabricated. The two parts of each specimen were fixed either by RC (n = 30) or GS with a luting space of either 30 µm (n = 30) or 100 µm (n = 30). Ten specimens of each group underwent autoclaving before artificial aging (water storage, thermocycling). Twenty specimens (including the 10 autoclaved specimens) of each group were exposed to a mechanical load. The retentive force between the zirconia and titanium in all specimens was determined. A fractographic analysis was performed to analyze the fracture surfaces of the GS specimens. The RC- and GS-connected two-piece abutments showed no relevant differences, independent of the luting space. RC appears to be more vulnerable to the thermal and mechanical loads than GS. Thus, GS may be an appropriate alternative to RC for two-piece abutments, especially for patients with enhanced biocompatibility requirements.

The Effect of Simulated Field Storage Conditions on Dental Restorative Materials for Military Field Use

INTRODUCTION

Dental readiness, one critical component of medical readiness, is adversely impacted by dental emergencies. Many dental emergencies require restorative materials such as glass ionomers, resins, and zinc oxide eugenols to remedy them. The Authorized Dental Allowance List (ADAL) and Authorized Medical Allowance List (AMAL) contain the equipment and materials used by Navy dentists to treat Sailors and Marines. These supplies are subjected to harsh storage conditions on deployments. Much is known about how materials behave when stored at room temperature, but less is known about how their properties are affected after exposure to high temperatures and humidity. We subjected five dental restorative materials to storage in aggravated conditions, and then tested them to determine which products are more robust.

MATERIALS AND METHODS

Unopened packages of Fuji Triage, Fuji IX GP (both GC America Inc., Alsip, Illinois), TPH Spectra ST Low Viscosity, Intermediate Restorative Material (both Dentsply Sirona, York, Pennsylvania), and Herculite XRV (Kerr Corporation, Orange, California) were exposed to 0, 5, or 10 days' storage at 30-60°C with 95% relative humidity. After storage in these aggravated conditions, we tested the compressive strength, hardness, elastic modulus, flexural strength, flexural modulus, sorption, and solubility of each material.

RESULTS

The physical properties of all materials were affected by storage in aggravated conditions, though the properties of some materials degraded more than others. Both glass ionomers, Fuji Triage (P = 0.0012) and Fuji IX GP (P = 0.0031), and the composite Herculite XRV (P = 0.0253) lost compressive strength after 5 or 10 days in aggravated conditions. The hardness values for all materials were affected (P < 0.05) by the aggravated conditions, though the elastic modulus of TPH Spectra was not affected (P > 0.05). None of the materials lost flexural strength (P > 0.05) or had changes in their flexural modulus (P > 0.05). The water sorption behavior of Fuji Triage (P = 0.0426) and Fuji IX GP (P = 0.0201) changed after 10 days of aggravated storage, and the solubility of all materials was altered by the harsh conditions.

CONCLUSION

Some materials degrade more than others in aggravated conditions. Both resin composite materials were more resistant to high temperatures and humidity levels than the glass ionomers tested. These changes in physical characteristics should be considered when reviewing or optimizing the ADAL/AMAL for different projected operational environments.

Effect of vulcanization temperature and dental stone colour on colour degradation of maxillofacial silicone elastomers

Background

Colour degradation is a major problem in maxillofacial silicone elastomers. Recent studies have focused on colour stability and the mechanical properties of the silicone elastomers. A colour match is also essential for the acceptance of the prosthesis by the patient. The aim of this study is to assess the colour degradation of the silicone elastomer after being moulded in different colours of dental stones at two different vulcanization temperatures.

Methods

Five different colours of dental stones were used to fabricate a total of 120 silicone blocks using a Cosmesil M511 maxillofacial silicone elastomer. Vulcanization was completed at two different temperatures (25 and 100° Celsius). Colour measurements were obtained with a Conica Minolta spectrophotometer. The CIEDE2000 formula was used to calculate the colour differences (∆E00). Two-way ANOVA, one-way ANOVA with Bonferroni corrected post-hoc p values and independent samples t-test were used for the statistical analyses.

Results

High temperature vulcanization causes lightening of the maxillofacial silicone elastomers without regard to the dental stone colour (p = 0.001). Specimens moulded in green stone lightened least at room temperature (p = 0.999). Compared to the control group, at high temperature, all specimens moulded in coloured dental stones darkened significantly (p < 0.001 for white, blue and yellow; p = 0.006 for green; p = 0.045 for reddish-brown). In the high temperature group, the shift to a green chroma was significant in the white, yellow and green dental stones groups (p = 0.001, p = 0.002, p < 0.001, respectively). The mean b* of the high temperature control group was higher than that of the room temperature control group (p < 0.001). The only ∆E00 score lower than the perceptibility threshold for dental materials (∆E00 = 1.30) was between the room temperature control group and the room temperature green dental stone group (∆E00 = 0.96).

Conclusions

Green and blue dental stones cause less colour degradation in silicone elastomers. Reddish-brown dental stones cause the most colour degradation in silicone elastomers. At 100 °C, the colour of the silicone elastomer lightens and yellows even if the elastomer is vulcanized in a stainless steel mould. White, yellow and reddish-brown dental stones make the silicone elastomer appear more yellow even if the elastomer is vulcanized at room temperature.

Discoloration of PMMA, composite, and PEEK

INTRODUCTION

To assess the discoloration and stain removal potential of different cleaning methods relevant to individual/professional prophylaxis and laboratory cleaning on polyetheretherketone (PEEK), poly(methyl methacrylate) (PMMA)-based, and composite (COMP) materials after storage in different media for 7 days.

METHODS

One thousand three hundred twenty specimens of PEEK, PMMA, and COMP (N = 440 of each group) were prepared and stored in four different media for 7 days to cause stain. Samples were divided into three cleaning groups (n = 10): (i) individual prophylaxis, (ii) laboratory protocols, and (iii) professional prophylaxis. Color was determined by a portable spectrophotometer and calculated between different time points (∆E). The data was statistically evaluated using univariate analyses, Kruskal-Wallis H and Mann-Whitney U tests (p < 0.05).

RESULTS

The significantly (p < 0.001) lowest discoloration was found when specimens were stored in distilled water and chlorhexidine (CHX), followed by red wine. Curry solution caused the highest discoloration. PEEK showed the significantly (p < 0.001) lowest color changes, while COMP showed the highest changes. Ultrasonic bath and Air Flow Plus (AFP) were the significantly (p < 0.001) most effective methods to remove staining. The least cleaning effect was found using a soft toothbrush (ST), a medium-hard toothbrush (MT), and SunSparkle (SS) cleaning system.

CONCLUSIONS

PEEK seems more stable against discolorations than other denture resin materials. Regarding the cleaning potential, individual prophylaxis can be conducted with toothbrushes. For professional prophylaxis, air-abrasion devices using gentle powders are effective. Laboratory protocols should include gentle cleaning methods like ultrasonic bath.

CLINICAL RELEVANCE

Clinicians and dental technicians should inform their patients about the discoloration potential of certain foods/beverages and recommend the most efficient cleaning, but preventive methods.