Shear bond strength of veneering porcelain to porous zirconia

Shear bond strength of porcelain to milled and stereolithography additively manufactured zirconia with and without surface treatment: An in vitro study

STATEMENT OF PROBLEM

Delamination of veneering ceramic is one of the most common challenges relating to veneered zirconia restorations. Additive manufacturing (AM) is a fast-expanding technology that has gained widespread acceptance in dentistry and is increasingly being used to produce dental restorations. However, information about bonding of porcelain to AM zirconia is lacking.

PURPOSE

The purpose of this in vitro study was to investigate the shear bond strength (SBS) of porcelain to milled and additively manufactured zirconia, and the effect of surface treatment on bond strength.

MATERIAL AND METHODS

A Ø12×5-mm disk was designed virtually to fabricate all specimens, which were divided into 2 groups according to the manufacturing technique: additively manufactured or milled zirconia. The effect of airborne-particle abrasion and a zirconia liner before porcelain application was investigated in both groups. Veneering porcelain was fired into an alumina ring mold on the zirconia surface. SBS was measured by using a universal testing machine at a crosshead speed of 1 mm/min before and after aging (n=10). SBS data were analyzed with 3-way ANOVA (α=.05) RESULTS: A significant difference was found between milled and AM zirconia. The SBS of porcelain to milled zirconia was significantly higher (1.38 MPa) than to AM zirconia (0.68 MPa) (P<.001). The surface treatment of zirconia had no significant effect on porcelain SBS in either group (P=.254), whereas thermocycling significantly reduced the SBS of porcelain to zirconia in both milled and AM groups (P=.001).

CONCLUSIONS

Porcelain bonding to milled zirconia was better than to AM zirconia. Pretreating the zirconia substrate before porcelain application did not improve the porcelain bond.

On the behaviour of zirconia-based dental materials: A review

Zirconia-based dental materials are extensively used in clinical practice due to their tooth-like appearance, biofunctionality, biocompatibility, and affordability. However, premature clinical failures of veneering porcelains raise a concern about their integrity. Extensive studies have been performed over a decade to resolve this issue, but it is challenging to reference all information effectively. A single source identifying the significance of potential parameters on material performance has not previously been available. An evidence-based meta-narrative review technique was used to review the characteristic parameters that can affect the overall behaviour of zirconia-based materials. Keywords were chosen to assess manuscripts based on scientific coherence with this paper's research objective. Online keyword searches were carried out on ScienceDirect, PubMed, and SAGE databases for relevant published manuscripts from year 1985-2020.261 out of 3170 identified manuscripts were included. A total of 10 parameters were identified and classified into the material, manufacturing, and geometric aspects. The effect of every parameter was reviewed on the performance of the material. A discrepancy in findings was observed and is attributed to the fact that there is no standard methodology. This review acts as a single source that summarizes various parameters' contribution to zirconia-based dental materials' performance. This review facilitates manufacturing improvements by accounting for every parameter's effect on overall performance.

Effects of dimensions of laser-milled grid-like microslits on shear bond strength between porcelain or indirect composite resin and zirconia

PURPOSE

Zirconia cores and frameworks are widely used in restorative dentistry. Although these structures are veneered with porcelain for esthetic reasons, the use of indirect composite resins (ICRs) is expected to increase in the future. The purpose of this study was to investigate the effects of microslits of different dimensions formed by Nd:YVO 4 laser machining on the bond strength between two types of zirconia (3 mol% yttria-partially stabilized zirconia (Y-TZP) and ceria-partially stabilized zirconia/alumina nanocomposite (Ce-TZP/A)) and porcelain or an ICR.

METHODS

The zirconia disks were assigned as follows: 1) blasted with alumina particles (AB) and 2-4) surface machined with gridded microslits with a width, pitch, and depth of 50, 75, or 100 µm (MS50, MS75, and MS100, respectively). After the bonding of the veneering materials to the disks, half of the specimens veneered with the ICR were subjected to thermocycling (4-60°C, 20000 cycles). All the specimens were subsequently shear tested (n = 10/group).

RESULTS

There was no significant difference between the groups of the disks bonded to porcelain. On the other hand, for the disks bonded to the ICR, the bond strengths of the MS groups after thermocycling were statistically higher than that of the AB group. However, there was no significant difference in the bond strengths of the disks with different microslits.

CONCLUSIONS

Within the study limitations, it can be concluded that, for porcelain, the design of the mechanical retentive structure must be modified. However, for the investigated ICR, a simple gridded pattern can improve the bond strength with zirconia.

Influence of the Conditioning Method for Pre-Sintered Zirconia on the Shear Bond Strength of Bilayered Porcelain/Zirconia

This study evaluated the bond strength of veneering porcelain with an experimental conditioner-coated zirconia. Pre-sintered Y-TZP specimens (n = 44) were divided in two groups based on conditioning type. After sintering, all sample surfaces were sandblasted and layered with veneering porcelain. Additionally, half of the specimens in each group underwent thermal cycling (10,000 cycles, 5–55 °C), and all shear bond strengths were measured. After testing, the failure mode of each fractured specimen was determined. Differences were tested by parametric and Fisher’s exact tests (α = 0.05). The differences in bond strength were not statistically significant. Adhesive fractures were dominantly observed for the non-thermal cycled specimens. After thermal cycling, the conditioner-coated group showed cohesive and mixed fractures (p = 0.0021), whereas the uncoated group showed more adhesive fractures (p = 0.0021). Conditioning of the pre-sintered Y-TZP did not change the shear bond strength of the veneering porcelain, but did improve the failure mode after thermal cycling.

Fabrication of all-ceramic crowns by a new method

A new method of all-ceramic production using alumina coping has been developed. The present study investigates the influence of secondary firing (glass infiltration firing) conditions. Samples of porcelain build-up without secondary firing were also assessed. The suitability of coping that included secondary firing was found to be affected by the rate of temperature increase during the secondary firing. However, cracking developed in the fired porcelain if porcelain was built up onto secondarily-fired coping. In contrast, cracking did not occur with coping that was not secondarily fired. The bending strength after porcelain build-up was 70 MPa or higher, suggesting the possibility of clinical applications as an anterior crown. These findings establish that this is method of producing all-ceramic crowns that allows for low-cost manufacture in a short period of about 1 h.

Fitting accuracy and fracture resistance of crowns using a hybrid zirconia frame made of both porous and dense zirconia

The purpose of this study is to evaluate the fitting accuracy and fracture resistance of crowns using a hybrid zirconia frame made of both porous and dense zirconia. Commercial semi-sintered zirconia, sintered dense zirconia and sintered hybrid zirconia were used. Sintered zirconia was milled using the CAD/CAM system, and semi-sintered zirconia was milled and sintered to fabricate molar crown frames. Completed frames were veneered with tooth-colored porcelain. The marginal and internal gaps between frames/crowns and abutments were measured. Each crown specimen was subjected to a fracture test. There were no significant differences in marginal and internal gap among all the frames and crowns. The crown with the hybrid zirconia frame had a 31-35% greater fracture load than that with the commercial or dense zirconia frame (p<0.01). This suggests that the all-ceramic crowns with a hybrid zirconia frame have a high fracture resistance.