Gil-Pozo A, Astudillo-Rubio D, Ferrando Cascales Á, Inchingolo F, Hirata R, Sauro S, Delgado-Gaete A. Effect of gastric acids on the mechanical properties of conventional and CAD/CAM resin composites - An in-vitro study. J Mech Behav Biomed Mater 2024; 155:106565. [PMID: 38718723 DOI: 10.1016/j.jmbbm.2024.106565] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/21/2024] [Revised: 04/29/2024] [Accepted: 04/30/2024] [Indexed: 05/28/2024]
Abstract
OBJECTIVES Dental erosion in patients with gastroesophageal reflux disease (GERD) is a current and frequent condition that may compromise the mechanical properties and clinical durability of resin-based composites (RBCs). This study assessed the mechanical properties of conventional and computer-aided design/computer-aided manufacturing (CAD/CAM) RBCs subsequent to simulated gastric acid aging. MATERIALS AND METHOD Three conventional and three CAD/CAM composites were assessed. They were divided into an experimental group (exposed to simulated gastric acid aging) and a control group (no aging). Both groups were analyzed for Vickers microhardness (VHN), wear and flexural strength over a period of six months. The failure rate probability for each RBC was calculated through the Weibull cumulative distribution function (m). Statistical analysis was conducted using repeated measures ANOVA, 3-way ANOVA, a non-parametric Kruskal-Wallis and U Mann-Whitney tests (α = 0.05). RESULTS The mechanical properties of all the RBCs dropped significantly after aging (p < 0.05). Lower VHN and flexural strength values, along with greater wear values were evident in the experimental groups, though the effects of the treatment varied between RBCs. The Weibull m of all the RBCs decreased over time. CONCLUSION Conventional RBCs might show greater reduction in mechanical properties compared to CAD/CAM RBCs when exposed to gastric acid attack. Thus, CAD/CAM composites may represent a suitable choice for the treatment of patients presenting erosive issues.
Collapse
Affiliation(s)
- Alexandra Gil-Pozo
- Division of Prosthodontics, School of Dentistry, Universidad Católica de Cuenca, 010107, Cuenca, Ecuador.
| | - Daniela Astudillo-Rubio
- Division of Prosthodontics, School of Dentistry, Universidad Católica de Cuenca, 010107, Cuenca, Ecuador.
| | - Álvaro Ferrando Cascales
- Department of Biomaterials Engineering, Faculty of Medicine, UCAM, Universidad Católica de Murcia, Campus de los Jerónimos, 135 Guadalupe, 30107, Murcia, Spain.
| | - Francesco Inchingolo
- Department of Interdisciplinary Medicine, University of Bari "Aldo Moro", 70124, Bari, Italy.
| | - Ronaldo Hirata
- Department of Biomaterials and Biomimetics, New York University College of Dentistry, New York, NY, 10010, USA.
| | - Salvatore Sauro
- Dental Biomaterials and Minimally Invasive Dentistry, Departamento de Odontología, Facultad de Ciencias de la Salud, Universidad CEU-Cardenal Herrera, C/Del Pozo ss/n, Alfara del Patriarca, 46115, Valencia, Spain.
| | - Andrés Delgado-Gaete
- Division of Prosthodontics, School of Dentistry, Universidad Católica de Cuenca, 010107, Cuenca, Ecuador.
| |
Collapse
|
2
|
Omara AA, Othman HI, Aldamaty MF, Metwally MF. Effect of acidic environment on color and translucency of different indirect restorative materials. BMC Oral Health 2024; 24:472. [PMID: 38641578 PMCID: PMC11027526 DOI: 10.1186/s12903-024-04218-5] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/29/2023] [Accepted: 04/02/2024] [Indexed: 04/21/2024] Open
Abstract
PURPOSE The aim of the current study was to evaluate the effect of simulated gastric acid on the color and translucency of different indirect restorative materials. MATERIALS AND METHODS A total of 36 disc-shaped samples were cut by using an isomet saw and divided into four equal groups (n = 9) according to the material type: Group Z: translucent zirconia (Ceramill® Zolid ht.+ preshade, Amann Girrbach, Koblach, Austria); Group E: lithium disilicate (IPS e.max CAD, Ivoclar Vivadent AG, Schaan, Liechtenstein); Group C: resin nanoceramic (Cerasmart, GC, Tokyo, Japan); Group P: polyether ether ketone (PEEK) (Bettin Zirconia Dentale Italy) veneered with indirect high impact polymer composite (HIPC) (breCAM HIPC, Bredent GmbH & Co. KG, Germany). The samples were immersed in simulated gastric acid (HCl, pH 1.2) for 96 hours at 37 °C in an incubator. The color change (ΔE00) and translucency (RTP00) were measured every 9.6 hours (one-year clinical simulation) of immersion in simulated gastric acid. RESULTS For color change (∆E00) and translucency (RTP00) among the tested materials, there was a highly statistically significant difference (P < 0.001) after every year of follow-up. The color change in both Z and G groups was the lowest after 1 year of acid immersion, followed by that in group H, and the highest change in color was recorded in group P. CONCLUSION High translucent zirconia is recommended in patients who are concerned about esthetic, especially with acidic oral environment.
Collapse
Affiliation(s)
- Abdelaziz A Omara
- Department of Fixed Prosthodontics, Faculty of Dental Medicine, Misr University for Science and Technology, Cairo, Egypt
| | - Hesham I Othman
- Department of Fixed Prosthodontics, Faculty of Dental Medicine, Al-Azhar University, Cairo, 11651, Egypt
| | - Mohamed F Aldamaty
- Department of Fixed Prosthodontics, Faculty of Dental Medicine, Al-Azhar University, Cairo, 11651, Egypt.
| | - Mohamed F Metwally
- Department of Fixed Prosthodontics, Faculty of Dental Medicine, Al-Azhar University, Cairo, 11651, Egypt
| |
Collapse
|
3
|
Deste Gökay G, Oyar P, Durkan R. Impact of various aging treatments on the microhardness and surface roughness of CAD-CAM monolithic restorative materials. J Prosthodont 2024. [PMID: 38638109 DOI: 10.1111/jopr.13846] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 12/14/2023] [Accepted: 03/05/2024] [Indexed: 04/20/2024] Open
Abstract
PURPOSE Dental ceramics deteriorate as a result of thermal aging and exposure to acidic solutions, which change their microhardness and surface roughness. This study assessed the resistance of several computer-aided design and computer-aided manufacturing (CAD-CAM) restorative dental materials in terms of surface roughness and microhardness following exposure to acidic solutions and thermal aging. MATERIALS AND METHODS Five different monolithic CAD-CAM restorative materials, two leucite-reinforced glass ceramics (G-Ceram and CEREC Blocs), a zirconia-infiltrated lithium silicate (Celtra Duo), a resin nanoceramic (Grandio), and monolithic zirconia (inCoris TZI), were used to create 2-mm-thick rectangular specimens (n = 100). After being immersed in either acidic saliva (pH = 4.0) (ST) or gastric juice (pH = 1.2) (GT), each material was subjected to 10,000 cycles of thermal aging. The Vickers microhardness and average surface roughness of the specimens were assessed at baseline, following thermal aging and exposure to either gastric juice or acidic saliva. The surface properties were examined using an atomic force microscope. The Mann‒Whitney U test with Bonferroni correction and the Wilcoxon signed-rank test was used for statistical analysis (a = 0.05). RESULTS The surface roughness of two leucite-reinforced glass ceramics (G-ceram and CEREC) significantly decreased with ST (p = 0.027 and p = 0.044). Only the CEREC was affected when the aging protocols were compared, and the ST group had a significant reduction in roughness (p = 0.009). The microhardness values significantly decreased after both aging protocols in all groups except for the ST subgroup of G-Ceram. Only inCoris was affected when the aging protocols were compared, and the GT group exhibited a significant reduction in microhardness (p = 0.002). CONCLUSION The surface roughness of the tested materials was not affected by the GT. Only leucite ceramics exhibited a decrease in surface roughness in the ST stage. Both aging processes produced a significant decrease in the microhardness of the tested ceramics. Leucite-reinforced glass-ceramic materials may be advantageous for patients with gastroesophageal reflux disease and those with a diet high in acidic foods due to their lower values for changes in microhardness and surface roughness compared to those of other CAD-CAM materials.
Collapse
Affiliation(s)
- Gonca Deste Gökay
- Faculty of Dentistry, Department of Prosthodontics, Bursa Uludağ University, Bursa, Türkiye
| | - Perihan Oyar
- Dental Prosthetics Technology, School of Health Services, Hacettepe University, Ankara, Türkiye
| | - Rukiye Durkan
- Faculty of Dentistry, Department of Prosthodontics, Istanbul Okan University, Istanbul, Türkiye
| |
Collapse
|
4
|
Kuscu HY, Kurkcuoglu I, Kucukesmen HC. The Impact of Gastric Juice on the Surface Roughness of Surface Sealant-Treated Provisional Restorations. Niger J Clin Pract 2024; 27:304-309. [PMID: 38528349 DOI: 10.4103/njcp.njcp_317_23] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 04/24/2023] [Accepted: 12/01/2023] [Indexed: 03/27/2024]
Abstract
BACKGROUND AND AIM Gastroesophageal reflux disease causes gastric acid to enter the oral cavity, leading to mucosal changes and deterioration of dental hard tissues and materials. The purpose of this in vitro study was to evaluate the impact of gastric juice on the surface roughness of two types of acrylics used in provisional restorations. MATERIALS AND METHODS Acrytemp ® and Temdent acrylic resin discs (10 × 2 mm) totaling 80 were manufactured and divided into eight groups (n = 10). Groups were prepared as follows: Group 1 (Temdent + Universal Polish) (control), Group 2 (Temdent + Universal Polish + Biscover LV), Group 3 (Temdent + Universal Polish + Resin Glaze), Group 4 (Temdent + Universal Polish + Fortify Plus), Group 5 (Acrytemp + Universal Polish) (control), Group 6 (Acrytemp + Universal Polish + Biscover LV), Group 7 (Acrytemp + Universal Polish + Resin Glaze), and Group 8 (Acrytemp + Universal Polish + Fortify Plus). The resin discs were immersed in distilled water for 24 h and in gastric juice (pH = 2) for additional 24 h. The initial and final roughness values of samples were measured and analyzed with non-parametric statistics including Mann-Whitney U-test for pairwise comparison, Kruskall Wallis test for comparing more than two groups, and Wilcoxon signed rank test for within-group comparison (P < 0.05). RESULTS Surface roughness did not differ significantly between control groups. It notably increased for all samples with surface sealants, both initially and after gastric juice immersion (P < 0.05). CONCLUSION Surface sealants noticeably increased the roughness of two types of acrylic resins. After immersing in gastric juice, Group 4 (Temdent + Universal Polish + Fortify Plus) showed the highest roughness, while the untreated control groups remained the smoothest.
Collapse
Affiliation(s)
- Hy Yay Kuscu
- Department of Prosthodontics, Faculty of Dentistry, Mehmet Akif Ersoy University, Burdur, Turkey
| | - I Kurkcuoglu
- Department of Prosthodontics, Faculty of Dentistry, Suleyman Demirel University, Isparta, Turkey
| | - H C Kucukesmen
- Department of Prosthodontics, Faculty of Dentistry, Suleyman Demirel University, Isparta, Turkey
| |
Collapse
|
5
|
Hazar A, Hazar E. Effects of different antiviral mouthwashes on the surface roughness, hardness, and color stability of composite CAD/CAM materials. J Appl Biomater Funct Mater 2024; 22:22808000241248886. [PMID: 38678374 DOI: 10.1177/22808000241248886] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 04/29/2024] Open
Abstract
OBJECTIVE To evaluate the effect of COVID-19 preventive mouthwashes on the surface hardness, surface roughness (Ra), and color change (ΔE) of three different polymer-based composite CAD/CAM materials (Vita Enamic (ENA), Grandio Block (GB), Lava Ultimate (LU)). METHODS A total of 100 rectangular-shaped specimens with dimensions of 2 mm × 7 mm × 12 mm were obtained by sectioning three different CAD/CAM blocks and randomly divided into five subgroups according to the 30 days of mouthwash immersion protocol as follows: Control: artificial saliva, PVP-I: 1% povidone-iodine, HP: 1.5% hydrogen peroxide, CPC: mouthwash containing 0.075% cetylpyridinium chloride, EO: mouthwash containing essential oils. Microhardness, Ra, and ΔE values were measured at baseline and after 30 days of immersion protocols. Data were analyzed using the Wald Chi-square, two-way ANOVA, and post hoc Tukey tests. RESULTS The independent factors (materials and solutions) significantly influenced the microhardness and color (p < 0.001). Ra of the materials was not affected by any of the mouthwashes (p > 0.05). The microhardness and color of each material varied significantly after immersion in PvP-I and HP (p < 0.05). The highest percentage change in microhardness, Ra, and ΔE was found in LU immersed in PvP-I and HP mouthwashes, while the lowest change was found in ENA groups (p < 0.05). CONCLUSION Within the limitations of this study, it was found that the surface hardness and color of tested polymer-based composite CAD/CAM materials are susceptible to degradation and change after 30 days of immersion in 1% PvP-I and 1.5% HP mouthwashes.
Collapse
Affiliation(s)
- Ahmet Hazar
- Faculty of Dentistry, Department of Restorative Dentistry, Zonguldak Bülent Ecevit University, Zonguldak, Turkey
| | - Ecehan Hazar
- Faculty of Dentistry, Department of Endodontics, Zonguldak Bülent Ecevit University, Zonguldak, Turkey
| |
Collapse
|
6
|
Çınar B, Eren D, Akın Ş. Effect of Low pH Dietary Supplements on Discoloration of Resin Composites. Niger J Clin Pract 2023; 26:1784-1791. [PMID: 38158343 DOI: 10.4103/njcp.njcp_345_22] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 05/18/2022] [Accepted: 11/13/2023] [Indexed: 01/03/2024]
Abstract
AIM This study aimed to evaluate the impact of the consumption of low pH dietary supplements on the color stability of different resin composites. MATERIALS AND METHODS Three different restorative materials were used for this in vitro study: Filtek One Bulk-Fill (FOB), Filtek Z550 (Z550), and Fill-Up (FUP). Samples fabricated from each composite group were divided into four subgroups, and color measurements were performed at baseline. The control subgroup was stored in distilled water, and the other three subgroups were immersed in acidic dietary supplement solutions (Redoxon, Supradyn, and Voonka Collagen Shake) for 2 minutes daily for 28 days. Color measurements were obtained using a digital spectrophotometer. Color change values (ΔE1) were calculated after each color measurement. Next, all samples were immersed in a coffee solution for 7 days and repeat color measurements were taken to determine ΔE2 values. The study groups were compared using the Kruskal-Wallis test (α =0.05). RESULTS ΔE1 values were significantly different among the groups (P < 0.05). While Voonka Collagen Shake produced the greatest discoloration in FOB (1.67 ± 1.08) and Filtek Z550 (3.59 ± 1.90) materials, Fill-Up showed the highest discoloration (3.14 ± 0.37) with Supradyn. Analysis of ΔE2 values demonstrated a significant difference only for the Filtek Z550-Redoxon group versus the control group (P < 0.05). CONCLUSION Acidic dietary supplements not only produce color alterations in resin composites but also reduce the staining resistance of the composite further, depending on the type of composite and dietary supplement. Consumption of staining food after taking Redoxon effervescent tablets produces greater discoloration in Filtek Z550 restorations compared with other restorative materials.
Collapse
Affiliation(s)
- B Çınar
- Department of Restorative Dentistry, Sivas Cumhuriyet University Faculty of Dentistry, Sivas, Turkey
| | | | | |
Collapse
|
7
|
Hjerppe J, Shahramian K, Rosqvist E, Lassila LVJ, Peltonen J, Närhi TO. Gastric acid challenge of lithium disilicate-reinforced glass-ceramics and zirconia-reinforced lithium silicate glass-ceramic after polishing and glazing-impact on surface properties. Clin Oral Investig 2023; 27:6865-6877. [PMID: 37821653 PMCID: PMC10630222 DOI: 10.1007/s00784-023-05301-x] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 06/12/2023] [Accepted: 09/29/2023] [Indexed: 10/13/2023]
Abstract
OBJECTIVES To investigate the impact of simulated gastric acid on the surface properties of lithium disilicate-reinforced glass-ceramics and zirconia-reinforced lithium silicate glass-ceramic after certain polishing and glazing procedures. MATERIALS AND METHODS Four different types of square-shaped specimens (10 × 10 × 2 mm3, n = 13) were manufactured: lithium disilicate-reinforced glass-ceramic milled and polished (LDS-P); milled, polished, and glazed (LDS-PG); milled, glazed, and no polishing (LDS-G); and milled and polished zirconia-reinforced lithium silicate glass-ceramic (ZR-LS). Specimens were immersed in hydrochloride acid (HCl 0.06 M, pH 1.2) to simulate gastric acid irritation and stored in the acid for 96 h in 37 °C. Specimen weight, surface gloss, Vickers surface microhardness and surface roughness (Ra, Rq, with optical profilometer), and surface roughness on nanometer level (Sq, Sal, Sq/Sal, Sdr, Sds with atomic force microscope) were measured before and after the acid immersion. RESULTS ZR-LS specimens lost significantly more weight after acid immersion (p = 0.001), also surface microhardness of ZR-LS was significantly reduced (p = 0.001). LDS-G and LDS-PG showed significantly lower surface roughness (Sa, Sq) values compared to LDS-P before (p ≤ 0.99) and after (p ≤ 0.99) acid immersion and ZR-LS after acid immersion (p ≤ 0.99). CONCLUSIONS Gastric acid challenge affects the surface properties of lithium disilicate-reinforced glass-ceramic and zirconia-reinforced lithium silicate glass-ceramic. Glazing layer provides lower surface roughness, and the glazed surface tends to smoothen after the gastric acid challenge. CLINICAL RELEVANCE Surface finish of lithium disilicate-reinforced glass-ceramic and zirconia-reinforced lithium silicate glass-ceramic has a clear impact on material's surface properties. Gastric acidic challenge changes surface properties but glazing seems to function as a protective barrier. Nevertheless, also glazing tends to smoothen after heavy gastric acid challenge. Glazing can be highly recommended to all glass-ceramic restorations but especially in patients with gastroesophageal reflux disease (GERD) and eating disorders like bulimia nervosa.
Collapse
Affiliation(s)
- Jenni Hjerppe
- Clinic of Reconstructive Dentistry, Center of Dental Medicine, University of Zürich, Plattenstrasse 11, 8032, Zurich, Switzerland.
- Department of Prosthetic Dentistry and Stomatognathic Physiology, University of Turku, Lemminkäisenkatu 2, 20520, Turku, Finland.
| | - Khalil Shahramian
- Department of Prosthetic Dentistry and Stomatognathic Physiology, University of Turku, Lemminkäisenkatu 2, 20520, Turku, Finland
| | - Emil Rosqvist
- Physical Chemistry, Laboratory of Molecular Science and Engineering, Åbo Akademi University, Henriksgatan 2, 20500, Turku, Finland
| | - Lippo V J Lassila
- Laboratory Manager, Turku Clinical Biomaterials Centre (TCBC), University of Turku, Itäinen Pitkäkatu 4B, 20520, Turku, Finland
| | - Jouko Peltonen
- Physical Chemistry, Laboratory of Molecular Science and Engineering, Åbo Akademi University, Henriksgatan 2, 20500, Turku, Finland
| | - Timo O Närhi
- Department of Prosthetic Dentistry and Stomatognathic Physiology, University of Turku, Lemminkäisenkatu 2, 20520, Turku, Finland
- City of Turku, Welfare Division, Lemminkäisenkatu 2, 20520, Turku, Finland
- Wellbeing Services County of Southwest Finland, PO BOX 52, 20521, Turku, Finland
| |
Collapse
|
8
|
Gulakar TL, Comert GN, Karaman E, Cakan U, Ozel GS, Ahmet SO. Effect of simulated gastric acid on aesthetical restorative CAD-CAM materials' microhardness and flexural strength. Niger J Clin Pract 2023; 26:1505-1511. [PMID: 37929527 DOI: 10.4103/njcp.njcp_131_23] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/07/2023]
Abstract
Background Gastric acid, which is among erosive substances, gradually rises to the mouth in individuals with reflux and bulimia nervosa disorders, and this causes various effects on dental restorations. Aim The objective of this study is in vitro investigation of gastric acid's effect on flexural strength and hardness on aesthetic restorative computer-aided design and computer-aided manufacturing (CAD-CAM) materials. Materials and Methods For this study, four materials have been used, namely Enamic (Vita), Superfect Zir (Aidite) Zirconia, IPS e.max CAD (Ivoclar Vivadent), and Mark II (Vita). From these four different materials, 24 samples with 14 × 4 × 1 dimensions in rectangular prism form are used, which makes a total of 96 samples. One group was separated as the control group, while the rest was allowed to wait at 37°C, 5 ml gastric acid for 96 hours. Hardness value and flexural strengths were measured as pre-exposure and post-exposure to gastric acid. Results There is a statistically significant difference between the groups in terms of the amount of decrease in the mean hardness after exposure to gastric acid compared to pre-exposure values (p: 0,000; P < 0,05). There was no statistically significant difference between the groups in terms of the amount of decrease in the post-exposure average flexural strength compared to the pre-exposure value (p: 0.063; P > 0.05). There is a statistically significant difference between the groups in terms of the average flexural strength after exposure to the acid. Conclusions According to the data obtained, it was concluded that exposure to gastric acid affects the hardness and flexural strength properties of dental restorative ceramic materials.
Collapse
Affiliation(s)
- T L Gulakar
- Department of Prosthodontics, Graduate School of Health Sciences', Istanbul, Medipol University, Istanbul, Turkey
| | - G N Comert
- Department of Prosthodontics, Graduate School of Health Sciences', Istanbul, Medipol University, Istanbul, Turkey
| | - E Karaman
- Department of Prosthodontics, Graduate School of Health Sciences', Istanbul, Medipol University, Istanbul, Turkey
| | - U Cakan
- Department of Prosthodontics, Istanbul Medipol University, Istanbul, Turkey
| | - G S Ozel
- Department of Prosthodontics, Graduate School of Health Sciences', Istanbul, Medipol University, Istanbul, Turkey
| | - S O Ahmet
- Department of Prosthodontics, Graduate School of Health Sciences', Istanbul, Medipol University, Istanbul, Turkey
| |
Collapse
|
9
|
Ille C, Moacă EA, Pop D, Goguță L, Opriș C, Pîrvulescu IL, Avram L, Faur A, Jivănescu A. Compressive strength evaluation of thin occlusal veneers from different CAD/CAM materials, before and after acidic saliva exposure. Odontology 2023; 111:360-374. [PMID: 36097129 PMCID: PMC10020293 DOI: 10.1007/s10266-022-00741-5] [Citation(s) in RCA: 1] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/25/2022] [Accepted: 09/02/2022] [Indexed: 01/09/2023]
Abstract
In the present study are depicted valuable observations for practitioners, obtained from an in vitro study which aims to evaluate the compressive strength of occlusal veneers fabricated from 3 type of restorative materials, before and after 1 month of acidic artificial saliva exposure (pH = 2.939). In this context, 90 extracted human molars were prepared to receive computer-aided design/computer-aided manufacturing (CAD/CAM) occlusal veneers. The restorative materials considered in this study were: Cerasmart; Straumann Nice and Tetric CAD. The occlusal veneers were designed, milled and cemented with an adhesive dual-cure resin cement. From all the extracted human molars, only sixty specimens were immersed in acidic artificial saliva, for 1 month, at 37 °C ± 1 °C and part of this specimens were also thermo-cycled, between 5 and 55 °C ± 2 °C, before compressive strength test. The results showed a lower compressive strength for both the samples exposed to acidic artificial saliva as well as for the samples exposed to acidic artificial saliva and thermo-cycled. Scanning electron microscopy (SEM) showed that after compressive strength, all the specimens non-exposed to acidic artificial saliva, present extensive cracks formation at the surface of the restorations, and after exposure to acidic artificial saliva for 1 month, the surface damage was characterized by longitudinal and profound fractures of the restoration, as well as the fracture of the tooth structure. Between CAD/CAM materials tested, nanoceramic resin shows more favorable fracture patterns, both before and after acidic artificial saliva exposure.
Collapse
Affiliation(s)
- Codruța Ille
- Department of Prosthodontics, Faculty of Dental Medicine, “Victor Babes” University of Medicine and Pharmacy, Revolutiei Ave. 1989, No. 9, 300580 Timișoara, Romania
- TADERP Research Center—Advanced and Digital Techniques for Endodontic, Restorative and Prosthetic Treatment, “Victor Babeș” University of Medicine and Pharmacy, Revolutiei Ave. 1989, No. 9, 300041 Timişoara, Romania
| | - Elena-Alina Moacă
- Department of Toxicology and Drug Industry, Faculty of Pharmacy, “Victor Babeș” University of Medicine and Pharmacy Timisoara, 2nd Eftimie Murgu Square, 300041 Timisoara, Romania
- Research Centre for Pharmaco-Toxicological Evaluation, “Victor Babeș” University of Medicine and Pharmacy, 2nd Eftimie Murgu Square, 300041 Timișoara, Romania
| | - Daniel Pop
- Department of Prosthodontics, Faculty of Dental Medicine, “Victor Babes” University of Medicine and Pharmacy, Revolutiei Ave. 1989, No. 9, 300580 Timișoara, Romania
- TADERP Research Center—Advanced and Digital Techniques for Endodontic, Restorative and Prosthetic Treatment, “Victor Babeș” University of Medicine and Pharmacy, Revolutiei Ave. 1989, No. 9, 300041 Timişoara, Romania
| | - Luciana Goguță
- Department of Prosthodontics, Faculty of Dental Medicine, “Victor Babes” University of Medicine and Pharmacy, Revolutiei Ave. 1989, No. 9, 300580 Timișoara, Romania
| | - Carmen Opriș
- Department for Materials and Manufacturing Engineering, Faculty of Mechanics, Politechnic University of Timisoara, Mihai Viteazu Ave., No. 1, 300222 Timisoara, Romania
| | - Ioana Ligia Pîrvulescu
- Department of Prosthodontics, Faculty of Dental Medicine, “Victor Babes” University of Medicine and Pharmacy, Revolutiei Ave. 1989, No. 9, 300580 Timișoara, Romania
| | - Liane Avram
- Department of Prosthodontics, Faculty of Dental Medicine, “Victor Babes” University of Medicine and Pharmacy, Revolutiei Ave. 1989, No. 9, 300580 Timișoara, Romania
| | - Andrei Faur
- Department of Prosthodontics, Faculty of Dental Medicine, “Victor Babes” University of Medicine and Pharmacy, Revolutiei Ave. 1989, No. 9, 300580 Timișoara, Romania
| | - Anca Jivănescu
- Department of Prosthodontics, Faculty of Dental Medicine, “Victor Babes” University of Medicine and Pharmacy, Revolutiei Ave. 1989, No. 9, 300580 Timișoara, Romania
- TADERP Research Center—Advanced and Digital Techniques for Endodontic, Restorative and Prosthetic Treatment, “Victor Babeș” University of Medicine and Pharmacy, Revolutiei Ave. 1989, No. 9, 300041 Timişoara, Romania
| |
Collapse
|
10
|
Elraggal A, R Afifi R, Alamoush RA, Raheem IA, Watts DC. Effect of acidic media on flexural strength and fatigue of CAD-CAM dental materials. Dent Mater 2023; 39:57-69. [PMID: 36496258 DOI: 10.1016/j.dental.2022.11.019] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/08/2022] [Revised: 11/13/2022] [Accepted: 11/25/2022] [Indexed: 12/12/2022]
Abstract
OBJECTIVE To investigate the effect of acidic media, including beverages and gastric fluids on flexural strength and fatigue of CAD-CAM materials. METHODS Four CAD-CAM materials (high-translucency zirconia (Ceramill Zolid HT+), lithium disilicate (IPS e-max CAD), hybrid ceramic (Vita Enamic), and nanohybrid resin composite (Grandio Blocs) were prepared and immersed in one of five media (gastric HCl, white wine, Coca-Cola, orange juice, and artificial saliva) in an incubator (37 ℃, 24 h). Surface topography and roughness were obtained using a scanning electron microscope (SEM) and a stylus contact profilometer, respectively. Initial 3-point flexural strength was measured for half of the bars (n = 20/gp) using a universal testing machine (0.5 mm/min). The other bars underwent 106 cyclic fatigue loadings before measurement of residual 3-point flexural strength. Data were statistically analyzed (two-way and three-way ANOVA, Tukey's post-hoc, p < 0.05). Weibull distributions were plotted for reliability analysis. RESULTS Zirconia bars has the highest initial flexural strengths followed by lithium disilicate, while resin composite and hybrid ceramic groups had the lowest strength regardless of the erosive medium. Cyclic fatigue significantly reduced initial flexural strengths for all materials except for hybrid ceramic and resin composite. Weibull moduli were the highest for zirconia, lithium disilicate and resin composite and lowest for hybrid ceramic. SIGNIFICANCE Erosive media significantly changed surface roughness of CAD-CAM materials except for zirconia and resin composite without jeopardizing the flexural strength of the CAD-CAM materials. Despite the higher flexural strengths for zirconia and lithium disilicate, resin composite and hybrid ceramic were more resistant to cyclic fatigue.
Collapse
Affiliation(s)
- Alaaeldin Elraggal
- Conservative Dentistry Department, Faculty of Dentistry, Alexandria University, Alexandria, Egypt.
| | - Rania R Afifi
- Conservative Dentistry Department, Faculty of Dentistry, Alexandria University, Alexandria, Egypt
| | - Rasha A Alamoush
- Department of Prosthodontics, School of Dentistry, The University of Jordan, Amman, Jordan
| | - Islam Abdel Raheem
- Conservative Dentistry Department, Faculty of Dentistry, Alexandria University, Alexandria, Egypt
| | - David C Watts
- School of Medical Sciences, University of Manchester, Manchester, UK
| |
Collapse
|
11
|
Alp CK, Gündogdu C, Ahısha CD. The Effect of Gastric Acid on the Surface Properties of Different Universal Composites: A SEM Study. SCANNING 2022; 2022:9217802. [PMID: 36636246 PMCID: PMC9812630 DOI: 10.1155/2022/9217802] [Citation(s) in RCA: 5] [Impact Index Per Article: 2.5] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 09/26/2022] [Revised: 11/28/2022] [Accepted: 12/17/2022] [Indexed: 06/09/2023]
Abstract
The aim of this study is to compare surface roughness and microhardness changes of three monochromatic (Omnichroma, Vittra Unique, and Charisma Diamond One) and three universal shade (Neo Spectra ST, G-ænial A'CHORD, and Nova Compo C) resin composites after exposure to simulated gastric acid. A total of 144 disc-shaped specimens (24 discs of each composite resin) were prepared using plexiglass molds (R = 5 mm × h = 2 mm) for evaluation from each material. Specimens of each material were divided into two main groups for the evaluation of the microhardness and surface roughness and also two subgroups for 7- and 14-day exposures to simulated gastric acid. Initial microhardness and surface roughness measurements of all samples were measured before immersion (T1) followed by exposing the samples to simulated gastric acid for 7 days (T2) and 14 days (T3), and then, the microhardness and roughness measurements were repeated. Randomly selected specimens of each material for each of the time intervals (T1, T2, and T3) were evaluated with scanning electron microscopy (SEM). One-way ANOVA revealed that the surface roughness and hardness values of all tested composite resin restorative materials show no statistically significant difference for the initial (T1) value (p > 0.05). Regarding the 7th day (T2) and 14th day (T3) surface roughness and microhardness value of all composites, there are statistically significant differences between the groups (p < 0.05), while there was no statistically significant difference between the surface hardness reduction percentage between the time intervals (p > 0.05). As a result of this in vitro study, increase in surface roughness and decrease in microhardness of the tested universal composite materials when exposed to simulated gastric acid were statistically significant.
Collapse
Affiliation(s)
- Cemile Kedici Alp
- Faculty of Dentistry, Department of Restorative Dentistry, Gazi University, Emek, Ankara, Turkey
| | - Ceyda Gündogdu
- Faculty of Dentistry, Department of Restorative Dentistry, İstanbul Medipol University, Bagcılar, Istanbul, Turkey
| | - Cansu Dağdelen Ahısha
- Faculty of Dentistry, Department of Restorative Dentistry, Gazi University, Emek, Ankara, Turkey
| |
Collapse
|
12
|
Elraggal A, Afifi R, Abdelraheem I. Effect of erosive media on microhardness and fracture toughness of CAD-CAM dental materials. BMC Oral Health 2022; 22:191. [PMID: 35590294 PMCID: PMC9118722 DOI: 10.1186/s12903-022-02230-1] [Citation(s) in RCA: 2] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/18/2022] [Accepted: 05/09/2022] [Indexed: 11/10/2022] Open
Abstract
Background Erosive acids might create surface flaws and deteriorate the mechanical properties of CAD-CAM materials. This invitro study aimed to investigate the effect of simulated gastric HCl and extrinsic erosive acids on surface microhardness and fracture toughness of CAD-CAM materials. Methods 400 bar-shaped specimens (17×4×2 mm3) were prepared from 4 different CAD-CAM dental materials (n = 100/group); monolithic zirconia (Ceramill Zolid HT+, Amanngirbach, Austria), lithium disilicate ceramic (IPS e.max CAD, Ivoclar Vivadent, Liechtenstein), nanohybrid resin composite (Grandio Blocs, VOCO) and polymer-infiltrated glass network (Vita Enamic, VITA Zahnfabrik). Specimens from each material type were further subdivided into 5 groups (n = 20) according to the erosive media applied (simulated gastric HCl, white wine, Coca-Cola®, orange juice, and artificial saliva that served as a control). Specimens were immersed for 24 h in an incubator at 37 ℃, then ultrasonically cleaned in distilled water and air-dried. Half of the specimens were tested for Vickers microhardness (VHN) at parameters of 500 gf for 10 s, while the rest of the specimens underwent 3-point flexure till fracture. Fractured surfaces were examined under a scanning electron microscope (SEM) for fracture toughness (KIC) calculation using the quantitative fractographic analysis method. Data collected were statistically analyzed using two-way analysis of variance (α = 0.05) after verification of data normality and homogeneity of variances. Results Erosive media created surface flaws that lowered the surface microhardness of the material and initiated the fracture pattern under different loads according to material type. The material type was a more predominant factor than erosive media that affected either the microhardness or the fracture toughness of CAD-CAM dental materials. The highest VHN and KIC values were found among Ceramill Zolid HT+ groups followed by IPS e.max CAD and Grandio Blocs regardless of the erosive media employed. Erosive media significantly reduced the VHN and KIC in Vita Enamic specimens compared to the rest of the material types. Conclusion All CAD-CAM materials used, except Vita Enamic, showed high resistance against the erosive acids indicating higher longevity of the material in patients frequently exposed to either extrinsic or intrinsic acid.
Collapse
Affiliation(s)
- Alaaeldin Elraggal
- Conservative Dentistry Department, Faculty of Dentistry, Alexandria University, Champollion street, Alexandria, Egypt.
| | - Rania Afifi
- Conservative Dentistry Department, Faculty of Dentistry, Alexandria University, Champollion street, Alexandria, Egypt
| | - Islam Abdelraheem
- Conservative Dentistry Department, Faculty of Dentistry, Alexandria University, Champollion street, Alexandria, Egypt
| |
Collapse
|
13
|
Oliveira JR, da Cruz MEM, Dovigo LN, Fonseca RG. Long-term effects of simulated gastric juice alternated with brushing on hardness, substance loss, flexural strength and reliability of CAD-CAM monolithic materials. J Appl Oral Sci 2022; 30:e20210536. [PMID: 35507986 PMCID: PMC9064190 DOI: 10.1590/1678-7757-2021-0536] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 09/14/2021] [Revised: 02/21/2022] [Accepted: 03/04/2022] [Indexed: 11/22/2022] Open
Abstract
OBJECTIVES The purpose of this study is to evaluate, over a simulated 5-year period, the effect of simulated gastric juice alternated with brushing on CAD-CAM monolithic materials considering microhardness, substance loss, flexural strength, and reliability of the materials. METHODOLOGY Blocks from Lava Ultimate (LU), Vita Enamic (VE), IPS Empress CAD (EMP), IPS e.max CAD (EMAX), and Vita Suprinity (VS) were milled into cylinders and sliced into disks. The EMAX and VS were crystallized, and all specimens were polished with silicon carbide papers and allocated as follows: 1) artificial saliva + brushing or 2) simulated gastric juice (0.113% hydrochloric acid (HCl) solution in deionized water, pH 1.2) + brushing, simulating 1, 3, and 5 years of clinical function. Each year of clinical function was simulated by three repetitions of immersion for 3 hours in artificial saliva or simulated gastric juice followed by 1,217 brushing cycles. The microhardness and substance loss were evaluated at baseline (T0) and at each year by using a Vickers hardness tester and an analytical balance. The biaxial flexural strength (BFS) test was performed in a mechanical testing machine at the end of the 5th year. Weibull modulus was calculated from the BFS data. RESULTS The microhardness of the LU was not influenced by the treatment, whereas that of the other materials, in certain years, was significantly lower in the gastric juice + brushing groups in comparison with artificial saliva + brushing groups. In general, the materials did not present a significant change in microhardness over time, for either of the treatments. The LU alone showed greater substance loss in the gastric juice + brushing groups for every year. In both treatments, the LU, VE, and EMP exhibited a significant increase in the substance loss over time. The treatment did not affect the BFS of the materials. The gastric juice + brushing decreased the reliability of the VE. CONCLUSIONS All materials were somehow impaired by the gastric juice + brushing in at least one of the evaluated parameters, except for the BFS. However, in a deeper analysis, the LU would be the least indicated materials, followed by VE, for patients with eating disorders.
Collapse
Affiliation(s)
- Jailson Rodrigues Oliveira
- Universidade Estadual PaulistaFaculdade de Odontologia de AraraquaraDepartamento de Materiais Odontológicos e PróteseAraraquaraSPBrasilUniversidade Estadual Paulista (UNESP), Faculdade de Odontologia de Araraquara, Departamento de Materiais Odontológicos e Prótese, Araraquara, SP, Brasil.
| | - Marlon Eduardo Menezes da Cruz
- Universidade Estadual PaulistaFaculdade de Odontologia de AraraquaraDepartamento de Materiais Odontológicos e PróteseAraraquaraSPBrasilUniversidade Estadual Paulista (UNESP), Faculdade de Odontologia de Araraquara, Departamento de Materiais Odontológicos e Prótese, Araraquara, SP, Brasil.
| | - Lívia Nordi Dovigo
- Universidade Estadual PaulistaFaculdade de Odontologia de AraraquaraDepartamento de Odontologia SocialAraraquaraSPBrasilUniversidade Estadual Paulista (UNESP), Faculdade de Odontologia de Araraquara, Departamento de Odontologia Social, Araraquara, SP, Brasil.
| | - Renata Garcia Fonseca
- Universidade Estadual PaulistaFaculdade de Odontologia de AraraquaraDepartamento de Materiais Odontológicos e PróteseAraraquaraSPBrasilUniversidade Estadual Paulista (UNESP), Faculdade de Odontologia de Araraquara, Departamento de Materiais Odontológicos e Prótese, Araraquara, SP, Brasil.
| |
Collapse
|
14
|
da Cruz MEM, Oliveira JJR, Dovigo LN, Fonseca RG. Long-term effect of gastric juice alternating with brushing on the surface roughness, topography, and staining susceptibility of CAD-CAM monolithic materials. J Prosthet Dent 2022; 127:659.e1-659.e11. [DOI: 10.1016/j.prosdent.2022.01.016] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 04/09/2021] [Revised: 12/30/2021] [Accepted: 01/04/2022] [Indexed: 12/26/2022]
|
15
|
Effects of Simulated Gastric Acid Exposure on Surface Topography, Mechanical and Optical Features of Commercial CAD/CAM Ceramic Blocks. APPLIED SCIENCES-BASEL 2021. [DOI: 10.3390/app11188703] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.3] [Reference Citation Analysis] [Abstract] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 12/15/2022]
Abstract
Gastric acid exposure produces tooth structure demineralization and dental ceramic degradation. The most affected patients are those who suffer from gastroesophageal reflux disease, bulimia nervosa, and pregnant women with prolonged severe nausea. In order to protect this kind of patient, the purpose of this study was to determine whether simulated gastric acid exposure leads to microstructural changes in surface topography, hardness, color changes, and translucency of some ceramic materials, which are already on the market. Forty disks (Triluxe Forte, Cerasmart, Enamic and Empress CAD) were analyzed before and after immersion in simulated gastric acid juice, in terms of microhardness, surface roughness, translucency, and surface morphology using scanning electron microscopy. Color change was assessed by using a spectrophotometer based on CIELab parameters and the results showed that, after exposure, ∆Eab remained under the threshold of acceptability and perceptibility. In terms of microhardness, Cerasmart is the only material that did not undergo changes after immersion. SEM images illustrated observable changes surface topography after acid exposure for all the tested materials. In conclusion, Triluxe Forte suffered the most important changes after simulated gastric acid juice exposure, and Cerasmart proved to be the least affected material.
Collapse
|
16
|
Moharramkhani F, Ranjbar Omrani L, Abbasi M, Kharrazifard MJ, Ahmadi E. Effect of fluoride varnish on glass ionomer microhardness changes in endogenous acid erosion challenge. Biomater Investig Dent 2021; 8:18-23. [PMID: 33629073 PMCID: PMC7889273 DOI: 10.1080/26415275.2021.1880907] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Journal Information] [Subscribe] [Scholar Register] [Received: 05/22/2020] [Accepted: 01/20/2021] [Indexed: 12/01/2022] Open
Abstract
OBJECTIVE This study aimed to assess the effect of fluoride varnish on glass ionomer microhardness changes after endogenous acid erosion challenge. METHODOLOGY In this study, 40 conventional glass ionomer (CGI; Fuji IX) and 40 resin-modified glass ionomer (RMGI; Fuji IILC) discs were fabricated and divided into 4 subgroups (n = 10) for immersion in synthetic gastric acid or saliva for 27 h with/without fluoride varnish application. The surface microhardness was measured at baseline and after immersion, and the change in microhardness was calculated. Data were analyzed using analysis of variance and T-test. RESULTS A reduction in microhardness was noted in all subgroups following immersion. The lowest change in microhardness of both CGI and RMGI occurred in artificial saliva. In CGI groups, the highest reduction in microhardness occurred in synthetic gastric acid with fluoride varnish application, and the reduction was significantly different from that of the CGI group with fluoride varnish application (p value = .01). In RMGI groups, the highest reduction in microhardness was noted in synthetic gastric acid without fluoride varnish application, and the reduction was significantly different from that of the other groups (p value < .05). CONCLUSIONS Exposure to synthetic gastric acid caused a significant reduction in microhardness of RMGI. Varnish application significantly decreased the acid susceptibility of RMGI, but not that of CGI.
Collapse
Affiliation(s)
- Fatemeh Moharramkhani
- Dental Research Center, Dentistry Research Institute, Tehran University of Medical Sciences, Tehran, Iran
| | - Ladan Ranjbar Omrani
- Department of Operative Dentistry, School of Dentistry, Tehran University of Medical Sciences, Tehran, Iran
| | - Mahdi Abbasi
- Department of Operative Dentistry, School of Dentistry, Tehran University of Medical Sciences, Tehran, Iran
| | | | - Elham Ahmadi
- Department of Operative Dentistry, School of Dentistry, Tehran University of Medical Sciences, Tehran, Iran
| |
Collapse
|
17
|
Theocharidou A, Kontonasaki E, Koukousaki I, Koumpouli A, Betsani I, Koidis P. Effect of in vitro aging and acidic storage on color, translucency, and contrast ratio of monolithic zirconia and lithium disilicate ceramics. J Prosthet Dent 2021; 127:479-488. [PMID: 33504431 DOI: 10.1016/j.prosdent.2020.12.015] [Citation(s) in RCA: 3] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 06/06/2019] [Revised: 12/16/2020] [Accepted: 12/16/2020] [Indexed: 11/17/2022]
Abstract
STATEMENT OF PROBLEM How the translucency and color of ceramic restorations are affected by surface changes from the corrosive environment in the oral cavity and aging of materials is unclear. PURPOSE The purpose of this in vitro study was to compare the impact of acidic exposure and aging on the color and translucency of monolithic zirconia and lithium disilicate ceramics. MATERIAL AND METHODS Twenty computer-aided design and computer-aided manufacturing (CAD-CAM) monolithic zirconia specimens and 20 pressed lithium disilicate specimens were fabricated. Half of the specimens of each group were aged in an autoclave (7.5 hours, 134 °C, 0.2 MPa), and the rest were immersed in hydrochloric acid to simulate the acidic conditions in the oral cavity from gastric reflux. The color coordinates L∗, a∗, and b∗ were measured with an ultraviolet spectrophotometer before and after aging or acidic storage. The translucency parameters and contrast ratios were calculated, and the CIEDE2000 color difference formula was used to determine color differences before and after each treatment. ANOVA and ANCOVA test models were used for data analysis (α=.05), while differences of color parameters in respect to acceptability and perceptibility thresholds were evaluated with the 1-sample t test (α=.05). RESULTS Lithium disilicate presented a significantly higher translucency parameter and lower contrast ratio at baseline compared with monolithic zirconia specimens (P<.001). Acidic storage significantly impacted all parameters compared with aging, especially for the lithium disilicate group. Color differences were above the acceptability ΔΕ00 threshold for lithium disilicate after acidic storage (P=.001) and below for monolithic zirconia after acidic storage (P=.003). CONCLUSIONS The performance of lithium disilicate was slightly inferior compared with that of monolithic zirconia specimens, as they presented significant and clinically observable differences for the translucency parameter and ΔΕ00 after acidic storage and aging.
Collapse
Affiliation(s)
- Anna Theocharidou
- Lecturer, Department of Prosthodontics, School of Dentistry, Faculty of Health Sciences, Aristotle University of Thessaloniki, Thessaloniki, Greece
| | - Eleana Kontonasaki
- Associate Professor, Department of Prosthodontics, School of Dentistry, Faculty of Health Sciences, Aristotle University of Thessaloniki, Thessaloniki, Greece
| | - Ioanna Koukousaki
- Predoctoral student, School of Dentistry, Faculty of Health Sciences, Aristotle University of Thessaloniki, Thessaloniki, Greece
| | - Alexandra Koumpouli
- Predoctoral student, School of Dentistry, Faculty of Health Sciences, Aristotle University of Thessaloniki, Thessaloniki, Greece
| | - Ioanna Betsani
- Predoctoral student, School of Dentistry, Faculty of Health Sciences, Aristotle University of Thessaloniki, Thessaloniki, Greece
| | - Petros Koidis
- Professor, Department of Prosthodontics, School of Dentistry, Faculty of Health Sciences, Aristotle University of Thessaloniki, Thessaloniki, Greece.
| |
Collapse
|
18
|
Erosion of CAD/CAM restorative materials and human enamel: An in situ/in vivo study. J Mech Behav Biomed Mater 2020; 110:103903. [DOI: 10.1016/j.jmbbm.2020.103903] [Citation(s) in RCA: 5] [Impact Index Per Article: 1.3] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/24/2020] [Revised: 05/26/2020] [Accepted: 05/31/2020] [Indexed: 12/29/2022]
|
19
|
Willers AE, da Silva BTF, Siriani LK, Cesar PF, Matos AB. Effect of erosive and abrasive challenges on the glaze layer applied to ceramic materials. J ESTHET RESTOR DENT 2020; 32:815-822. [PMID: 32827220 DOI: 10.1111/jerd.12643] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/18/2019] [Revised: 06/23/2020] [Accepted: 07/30/2020] [Indexed: 11/26/2022]
Abstract
PURPOSE This study aims to evaluate the effect of erosive, abrasive, and erosive/abrasive challenges on the glaze layer of ceramic materials. METHODS Ninety-five samples of monolithic zirconia (MZ) (LuxaCam Zircon HT-Plus) and lithium disilicate (LD) (IPS e.max CAD) were divided according to the response variables: Surface roughness and surface loss (n = 10), evaluated with optical profilometry; surface topography, with scanning electron microscopy SEM (n = 3); and biofilm deposition, with microbiological assay (n = 5). The evaluations were performed in three different time evaluations: (a) Sintered, (b) Glaze, and (c) Challenge (Erosion, Abrasion, and Erosion/Abrasion). Erosion consisted in immersing specimens in HCl solution, abrasion was performed with brushing machine, and erosion/abrasion consisted of a combination of the two previous protocols. Data were analyzed with parametric tests (P < 0.05). RESULTS MZ glaze layer presented significantly higher surface roughness (P = 0.00), surface loss (P = 0.03), and biofilm deposition (P = 0.00) than LD. Abrasion and erosion/abrasion showed similar outcomes, generating significantly higher surface roughness (P = 0.00), surface loss (P = 0.00), and biofilm deposition (P = 0.01) than erosion. CONCLUSIONS Glaze layer properties were altered by the challenges, with abrasion and erosion/abrasion generating higher surface roughness, surface loss, and biofilm deposition than erosion. A significant correlation was found between the surface roughness and biofilm deposition. CLINICAL SIGNIFICANCE The glaze layer is susceptible to challenges, especially to abrasion and erosion/abrasion, which generated greater surface roughness and surface loss than erosion. The greater surface roughness lead to a greater biofilm deposition on the glaze layer.
Collapse
Affiliation(s)
| | | | | | - Paulo Francisco Cesar
- Department of Biomaterials and Oral Biology, University of São Paulo, São Paulo, Brazil
| | - Adriana Bona Matos
- Department of Restorative Dentistry, University of São Paulo, São Paulo, Brazil
| |
Collapse
|
20
|
Salema CFBDA, Silva PGDB, Oliveira PMDC, Sousa FB, Silva RHAD, Silva LVD, Bezerra TP. Forensic study of mechanical properties of dental fillings after immersion in marine environment. Forensic Sci Int 2020; 313:110362. [PMID: 32593111 DOI: 10.1016/j.forsciint.2020.110362] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 04/13/2020] [Revised: 05/30/2020] [Accepted: 06/08/2020] [Indexed: 10/24/2022]
Abstract
Human identification and postmortem intervals can be difficult to estimate when corpses are found in drowning situations, and forensic odontologists can bring valuable input to forensic science investigations of this type. Studies that simulate real scenarios are crucial for providing parameters that can be used in real cases. The present study created the necessary circumstances, i.e. immersion in a marine environment, to estimate the changes in the mechanical properties (Knoop microhardness, roughness, and color) of various dental fillings (silver amalgam, composite resin, and glass ionomer cement) over different immersion periods of time (one and three months). The silver amalgam fillings showed a significant increase in surface roughness. The composite resin fillings showed statistically significant increases in surface roughness and Knoop microhardness, and the glass ionomer cement showed a significant increase in surface roughness. These results lead to the conclusion that teeth restored with silver amalgam, composite resin, and glass ionomer cement, when subjected to immersion in marine environments, produce different changes in surface roughness, Knoop microhardness, and color properties depending on the length of immersion time. These findings could help in the field of forensic science to accurately estimate immersion time of dead bodies found in marine environments.
Collapse
Affiliation(s)
| | | | | | - Fabricio Bitu Sousa
- Centro Universitário Christus: Street Adolfo Gurgel, 133, Cocó, Fortaleza-Ceará, Brazil
| | - Ricardo Henrique Alves da Silva
- Universidade de Sao Paulo Faculdade de Odontologia de Ribeirao Preto: Avenue do Café - Subsector Oest- 11(N-11), Ribeirão Preto, SP, Brazil
| | - Lívia Vieira da Silva
- Centro Universitário Christus: Street Adolfo Gurgel, 133, Cocó, Fortaleza-Ceará, Brazil
| | | |
Collapse
|
21
|
Cruz MEM, Simões R, Martins SB, Trindade FZ, Dovigo LN, Fonseca RG. Influence of simulated gastric juice on surface characteristics of CAD-CAM monolithic materials. J Prosthet Dent 2019; 123:483-490. [PMID: 31383520 DOI: 10.1016/j.prosdent.2019.04.018] [Citation(s) in RCA: 12] [Impact Index Per Article: 2.4] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/30/2018] [Revised: 04/12/2019] [Accepted: 04/13/2019] [Indexed: 01/11/2023]
Abstract
STATEMENT OF PROBLEM How the surfaces of monolithic esthetic restorations behave in the presence of acidic substances is unclear. PURPOSE The purpose of this in vitro study was to evaluate the effect of simulated gastric juice on roughness, morphology, microhardness, substance loss, and color change of computer-aided design and computer-aided manufacturing (CAD-CAM) monolithic materials. MATERIAL AND METHODS Disks from Lava Ultimate, VITA ENAMIC, IPS e.max CAD, and VITA SUPRINITY were analyzed for roughness, morphology, and microhardness by using a confocal microscope, scanning electron microscope (SEM), and Vickers hardness tester. Substance loss was determined by weighing the specimens on an analytical balance, and color change (ΔE) was assessed by using a spectrophotometer based on the CIELab parameters. All analyses were carried out before and after acid exposure. RESULTS Acid exposure significantly decreased the roughness, having a very high effect size on this property. The material was highly decisive in determining the microhardness, presenting the following order: VITA SUPRINITY>IPS e.max CAD>VITA ENAMIC>Lava Ultimate. The mass was not significantly affected by the acidic challenge. No significant difference in ΔE was found between Lava Ultimate and VITA ENAMIC and between IPS e.max CAD and VITA SUPRINITY. Lava Ultimate showed a higher ΔE than IPS e.max CAD and VITA SUPRINITY, whereas VITA ENAMIC exhibited higher ΔE only when compared with VITA SUPRINITY. All materials presented ΔE<1. CONCLUSIONS The simulated gastric juice significantly influenced the roughness of all the evaluated materials and promoted a color change classified as clinically undetectable in all materials.
Collapse
Affiliation(s)
- Marlon E M Cruz
- Graduate student, Araraquara Dental School, São Paulo State University (UNESP), Araraquara, Brazil
| | - Rafaela Simões
- Graduate student, Araraquara Dental School, São Paulo State University (UNESP), Araraquara, Brazil
| | - Samira B Martins
- Doctoral student, Department of Dental Materials and Prosthodontics, Araraquara Dental School, São Paulo State University (UNESP), Araraquara, Brazil
| | - Flávia Z Trindade
- Postdoctoral Fellow, Department of Dental Materials and Prosthodontics, Araraquara Dental School, São Paulo State University (UNESP), Araraquara, Brazil
| | - Lívia N Dovigo
- Assistant Professor, Department of Dental Materials and Prosthodontics, Araraquara Dental School, São Paulo State University (UNESP), Araraquara, Brazil
| | - Renata G Fonseca
- Assistant Professor, Department of Dental Materials and Prosthodontics, Araraquara Dental School, São Paulo State University (UNESP), Araraquara, Brazil.
| |
Collapse
|
22
|
El Gezawi M, Kaisarly D, Al-Saleh H, ArRejaie A, Al-Harbi F, Kunzelmann KH. Degradation Potential of Bulk Versus Incrementally Applied and Indirect Composites: Color, Microhardness, and Surface Deterioration. Oper Dent 2018; 41:e195-e208. [PMID: 27820694 DOI: 10.2341/15-195-l] [Citation(s) in RCA: 18] [Impact Index Per Article: 3.0] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/23/2022]
Abstract
This study investigated the color stability and microhardness of five composites exposed to four beverages with different pH values. Composite discs were produced (n=10); Filtek Z250 (3M ESPE) and Filtek P90 (3M ESPE) were applied in two layers (2 mm, 20 seconds), and Tetric N-Ceram Bulk Fill (TetricBF, Ivoclar Vivadent) and SonicFill (Kerr) were applied in bulk (4 mm) and then light cured (40 seconds, Ortholux-LED, 1600 mW/cm2). Indirect composite Sinfony (3M ESPE) was applied in two layers (2 mm) and cured (Visio system, 3M ESPE). The specimens were polished and tested for color stability; ΔE was calculated using spectrophotometer readings. Vickers microhardness (50 g, dwell time=45 seconds) was assessed on the top and bottom surfaces at baseline, 40 days of storage, subsequent repolishing, and 60 days of immersion in distilled water (pH=7.0), Coca-Cola (pH=2.3), orange juice (pH=3.75), or anise (pH=8.5) using scanning electron microscopy (SEM). The materials had similar ΔE values (40 days, p>0.05), but TetricBF had a significantly greater ΔE than P90 or SF (40 days). The ΔE was less for P90 and TetricBF than for Z250, SonicFill, and Sinfony (60 days). Repolishing and further immersion significantly affected the ΔE (p<0.05) except for P90. All composites had significantly different top vs bottom baseline microhardnesses. This was insignificant for the Z250/water, P90/orange juice (40 days), and Sinfony groups (40 and 60 days). Immersion produced variable time-dependent deterioration of microhardness in all groups. Multivariate repeated measures analysis of variance with post hoc Bonferroni tests were used to compare the results. ΔE and microhardness changes were significantly inversely correlated at 40 days, but this relationship was insignificant at 60 days (Pearson test). SEM showed degradation (40 days) that worsened (60 days). Bulk-fill composites differ regarding color-stability and top-to-bottom microhardness changes compared with those of other composites. P90 showed better surface degradation resistance. In conclusion, bulk-fill composites are not promising alternatives to incremental and indirect composites regarding biodegradation.
Collapse
|
23
|
Effect of different beverages on the color stability and microhardness of CAD/CAM hybrid versus feldspathic ceramic blocks: An in-vitro study. ACTA ACUST UNITED AC 2017. [DOI: 10.1016/j.fdj.2017.07.001] [Citation(s) in RCA: 15] [Impact Index Per Article: 2.1] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/22/2022]
|
24
|
Backer AD, Münchow EA, Eckert GJ, Hara AT, Platt JA, Bottino MC. Effects of Simulated Gastric Juice on CAD/CAM Resin Composites-Morphological and Mechanical Evaluations. J Prosthodont 2015; 26:424-431. [DOI: 10.1111/jopr.12420] [Citation(s) in RCA: 19] [Impact Index Per Article: 2.1] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Accepted: 08/21/2015] [Indexed: 11/29/2022] Open
Affiliation(s)
- Adriana D. Backer
- Department of Biomedical and Applied Sciences, Division of Dental Biomaterials; Indiana University School of Dentistry (IUSD); Indianapolis IN
- Department of Prosthodontics; Graduate Prosthodontics, IUSD; Indianapolis IN
| | - Eliseu A. Münchow
- Department of Biomedical and Applied Sciences, Division of Dental Biomaterials; Indiana University School of Dentistry (IUSD); Indianapolis IN
- Department of Operative Dentistry, School of Dentistry; Federal University of Pelotas; Pelotas Brazil
| | - George J. Eckert
- Department of Biostatistics; Indiana University School of Medicine; Indianapolis IN
| | - Anderson T. Hara
- Department of Cariology, Operative Dentistry and Dental Public Health; IUSD; Indianapolis IN
| | - Jeffrey A. Platt
- Department of Biomedical and Applied Sciences, Division of Dental Biomaterials; Indiana University School of Dentistry (IUSD); Indianapolis IN
| | - Marco C. Bottino
- Department of Biomedical and Applied Sciences, Division of Dental Biomaterials; Indiana University School of Dentistry (IUSD); Indianapolis IN
| |
Collapse
|
25
|
Khan AA, Siddiqui AZ, Al-Kheraif AA, Zahid A, Divakar DD. Effect of different pH solvents on micro-hardness and surface topography of dental nano-composite: An in vitro analysis. Pak J Med Sci 2015; 31:854-9. [PMID: 26430417 PMCID: PMC4590396 DOI: 10.12669/pjms.314.7517] [Citation(s) in RCA: 3] [Impact Index Per Article: 0.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/15/2022] Open
Abstract
Objective: Erosion of tooth surface is attributed to recent shift in diet pattern and frequent use of beverages. The aim of this research was to evaluate the effects of different beverages on surface topography and hardness of nano-filled composite material. Methods: Sixty flat disc shaped resin composite samples were fabricated and placed in distilled water for 24 hours. After 24 hours test samples were dried and divided into 4 groups. Group A (n=15) specimens were placed in tight amber bottle comprising 25 ml of artificial saliva. Similarly Group B, C and D were stored in equal amounts of orange juice, milk and coca cola drink respectively. Samples were checked for hardness and surface changes were evaluated with scanning electron microscopy. Results: There were strong significant difference observed in samples immersed in orange juice and artificial saliva. A strong significant difference was seen between Group D and Group A. Group A and Group C showed no significant difference. The micro-hardness test showed reduced values among all samples. Conclusion: Beverages consumed daily have a negative influence on hardness and surface degradation of nano-filled dental composite. Comparatively, nano-filled composites possess higher surface area to volume ratio of their fillers particle size may lead to higher surface roughness than other resin based dental biomaterials.
Collapse
Affiliation(s)
- Aftab Ahmed Khan
- Aftab Ahmed Khan, MSc, M.Bioeth, B.D.S Researcher, Dental Biomaterials Research Chair, College of Applied Medical Sciences, King Saud University, Riyadh 11433; Saudi Arabia
| | - Adel Zia Siddiqui
- Adel Zia Siddiqui, MSc, B.D.S Associate Professor, Dental Material Sciences, Baqai Dental College, Baqai Medical University, 51 Deh Tor, Toll Plaza, Super Highway, Gadap Road, Karachi 74600; Pakistan
| | - Abdulaziz A Al-Kheraif
- Abdulaziz A. Al-Kheraif, Ph.D, MSc Associate Professor and Chair, Dental Biomaterials Research Chair, College of Applied Medical Sciences, King Saud University, Riyadh 11433; Saudi Arabia
| | - Ambreen Zahid
- Ambreen Zahid, B.D.S Lecturer, Oral Pathology, Muhammad Bin Qasim Dental College, Gulshan-e-Benazir, Razaqabad, Bin Qasim Town, Karachi; Pakistan
| | - Darshan Devang Divakar
- Darshan Devang Divakar, M.D.S, B.D.S Researcher, Dental Biomaterials Research chair, College of Applied Medical Sciences, King Saud University, Riyadh 11433; Saudi Arabia
| |
Collapse
|
26
|
Effect of Heat Treatment on the Physical Properties of Provisional Crowns during Polymerization: An in Vitro Study. MATERIALS 2015; 8:1766-1777. [PMID: 28788031 PMCID: PMC5507018 DOI: 10.3390/ma8041766] [Citation(s) in RCA: 9] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 12/12/2014] [Revised: 04/02/2015] [Accepted: 04/07/2015] [Indexed: 11/17/2022]
Abstract
This study concerned the effect of heat treatment during setting on the physical properties of four resin-based provisional restorative materials: Duralay (polymethyl methacrylate), Trim II (polyethyl methacrylate), Luxatemp (bis-acrylic composite), and Protemp 4 (bis-acrylic composite). Specimens were prepared at 23, 37, or 60 °C for evaluation of flexural strength, surface roughness, color change and marginal discrepancy. Flexural strength was determined by a three-point bending test. Surface profile was studied using atomic force microscopy. Color change was evaluated by comparing the color of the materials before and after placement in coffee. A travelling microscope helped prepare standardized crowns for assessment of marginal discrepancy. Flexural strength of all tested materials cured at 23 °C or 37 °C did not significantly change. The surface roughness and marginal discrepancy of the materials increased at 60 °C curing temperature. Marginal discrepancies, color stability, and other physical properties of materials cured at 23 °C or 37 °C did not significantly change. Flexural strength of certain provisional materials cured at 60 °C increased, but there was also an increase in surface roughness and marginal discrepancy.
Collapse
|
27
|
Wang Y, Yamamoto Y, Shigemori S, Watanabe T, Oshiro K, Wang X, Wang P, Sato T, Yonekura S, Tanaka S, Kitazawa H, Shimosato T. Inhibitory/suppressive oligodeoxynucleotide nanocapsules as simple oral delivery devices for preventing atopic dermatitis in mice. Mol Ther 2014; 23:297-309. [PMID: 25502904 DOI: 10.1038/mt.2014.239] [Citation(s) in RCA: 25] [Impact Index Per Article: 2.5] [Reference Citation Analysis] [Abstract] [Journal Information] [Subscribe] [Scholar Register] [Received: 05/06/2014] [Accepted: 12/05/2014] [Indexed: 12/19/2022] Open
Abstract
Here, we report a simple and low-cost oral oligodeoxynucleotide (ODN) delivery system targeted to the gut Peyer's patches (PPs). This system requires only Dulbecco's modified eagle's medium, calcium chloride, ODNs, and basic laboratory equipment. ODN nanocapsules (ODNcaps) were directly delivered to the PPs through oral administration and were taken up by macrophages in the PPs, where they induced an immune response. Long-term continuous oral dosing with inhibitory/suppressive ODNcaps (iODNcaps, "iSG3caps" in this study) was evaluated using an atopic dermatitis mouse model to visually monitor disease course. Administration of iSG3caps improved skin lesions and decreased epidermal thickness. Underlying this effect is the ability of iSG3 to bind to and prevent phosphorylation of signal transducer and activator of transcription 6, thereby blocking the interleukin-4 signaling cascade mediated by binding of allergens to type 2 helper T cells. The results of our iSG3cap oral delivery experiments suggest that iSG3 may be useful for treating allergic diseases.
Collapse
Affiliation(s)
- Yeqin Wang
- Interdisciplinary Graduate School of Science and Technology, Shinshu University, Kamiina, Japan
| | | | - Suguru Shigemori
- 1] Interdisciplinary Graduate School of Science and Technology, Shinshu University, Kamiina, Japan [2] Research Fellow of the Japan Society for the Promotion of Science (JSPS), Chiyoda-ku, Japan
| | | | - Kazushi Oshiro
- Graduate School of Agriculture, Shinshu University, Kamiina, Japan
| | - Xinyu Wang
- Graduate School of Agriculture, Shinshu University, Kamiina, Japan
| | - Pengfei Wang
- Graduate School of Agriculture, Shinshu University, Kamiina, Japan
| | - Takashi Sato
- Department of Internal Medicine and Clinical Immunology, Graduate School of Medicine, Yokohama City University, Yokohama, Japan
| | - Shinichi Yonekura
- Department of Interdisciplinary Genome Sciences and Cell Metabolism, Institute for Biomedical Sciences, Interdisciplinary Cluster for Cutting Edge Research (ICCER), Shinshu University, Kamiina, Japan
| | - Sachi Tanaka
- Frontier Agriscience and Technology Center (FAST), Shinshu University, Kamiina, Japan
| | - Haruki Kitazawa
- Food and Feed Immunology Group, Graduate School of Agricultural Science, Tohoku University, Sendai, Japan
| | - Takeshi Shimosato
- 1] Interdisciplinary Graduate School of Science and Technology, Shinshu University, Kamiina, Japan [2] Graduate School of Agriculture, Shinshu University, Kamiina, Japan [3] Department of Interdisciplinary Genome Sciences and Cell Metabolism, Institute for Biomedical Sciences, Interdisciplinary Cluster for Cutting Edge Research (ICCER), Shinshu University, Kamiina, Japan
| |
Collapse
|