Chemical alteration of Ag-Pd-Cu-Au alloy surface by alumina air-abrasion and its effect on bonding to resin cement

Effect of multi-purpose primer on bonding of acrylic resin to cast titanium and gold alloy after airborne-particle abrasion

PURPOSE

To clarify the effect of a multi-purpose primer combining several functional monomers on two prosthodontic materials (cast titanium and a gold alloy) after airborne-particle abrasion.

METHODS

Disk-shaped adherends were prepared from cast titanium (CP Titanium JIS2) and a gold alloy (Casting Gold M.C. Type IV). A silane-containing two-liquid primer (M&C primer (MC)) and two silane-free single-liquid primers (Alloy Primer (AP) and V-Primer (VP)) were used as surface-treatment agents. The shear bond strengths were determined before and after thermocycling to evaluate the adhesive durability, and the results were compared using a non-parametric statistical analysis. The effect of airborne-particle abrasion with alumina on the titanium surface was analyzed by X-ray photoelectron spectroscopy (XPS).

RESULTS

There was no significant difference in bond strength between the MC and AP before and after thermocycling, whereas VP showed significantly lower values. XPS revealed that the titanium acquired hydrophilic properties after the airborne-particle abrasion.

CONCLUSIONS

The novelty of this study is that it shows that the presence/absence of the silane had no effect on the bonding of cast titanium with an acrylic resin. The study also showed that the multi-purpose primer can be used without any problems with both cast titanium and gold alloy, in combination with airborne-particle abrasion with alumina.

Evaluation of the effects of three pretreatment conditioners and a surface preparation system on the bonding durability of composite resin adhesive to a gold alloy

This study aimed to evaluate the effect of three pretreatment conditioners and surface preparations on a composite resin adhesive for a gold alloy. Cast disk specimens were made and bonded with RelyX Unicem luting agent under six surface conditions: 1) polished with No.600 carbide paper, 2) air-abraded with alumina, 3) Alloy Primer metal conditioner was applied after alumina-abrasion, 4) Monobond Plus multipurpose conditioner was applied after alumina-abrasion, 5) M. L. Primer metal conditioner was applied after alumina-abrasion, and 6) Rocatec multipurpose silica-coating system was applied. The bond strengths were determined before and after thermocycling (50,000 cycles). The bond strengths of the alumina-abrasion group were significantly decreased after thermocycling. The Rocatec and M. L. Primer exhibited higher bond strengths than other treatments. The application of metal conditioners and multipurpose surface preparations was recommended for improved bonding between the evaluated adhesive resin and gold alloy.

Bonding behavior and chemical and mechanical properties of silver-based dental alloys

This article presents a review of silver-based dental alloys, with a focus on their bonding behavior and their chemical and mechanical properties. The most effective pretreatment for bonding silver-based alloys involves alumina air-abrasion followed by the application of a metal adhesive primer containing both the vinyl-thione monomer and a hydrophobic phosphate monomer. Silver-based alloys are readily sulfurized, making it clinically important to limit their use to cast post and core restorations to avoid direct exposure to salivary components. Fracture of the post and core restorations can be prevented by reinforcing their mechanical properties by applying the cast joining technique with tougher metals.

Effects of Copper Surface Oxidation and Reduction on Shear-Bond Strength Using Functional Monomers

This study was conducted to clarify the influence of the copper surface oxidation and reduction on the shear-bond strength with functional monomers. Unheated copper specimens (UH; n = 88) were wet-ground. Three-quarters of the UH were then heated (HT). Two-thirds of the HT was then immersed in a hydrochloric acid solution (AC). Half of the AC was then reheated (RH). Each group was further divided into two groups (n = 11), which were primed by either 6-methacryloyloxyhexyl 2-thiouracil-5-carboxylate (MTU-6) or 10-methacryloyloxydecyl dihydrogen phosphate (MDP). The shear-bond strength tests were used for bonding with an acrylic resin. The surface roughness values and chemical states of the four groups were analyzed using a confocal scanning laser microscope and X-ray photoelectron spectroscopy (XPS). The shear-bond strengths of HT and RH were the lowest in the MTU-6-primed groups. The result of AC was significantly lower than others in the MDP-primed groups. The XPS results showed that the surfaces of UH and AC consisted of Cu₂O and Cu. The surface changed to CuO upon heating. The presence or absence of copper-oxide films showed the opposite trends in the effectiveness of MTU-6 and MDP to improve bond strength. The results could elucidate the effects of functional monomers on copper-oxide films.

Effects of Both Fiber Post/Core Resin Construction System and Root Canal Sealer on the Material Interface in Deep Areas of Root Canal

This study aimed to examine the resin polymerization of a fiber post/core resin construction system and the interface between resin and root canal sealers, which are important for root canal sealing. We used the i-TFC Luminus fiber post and i-TFC Luminus LC flow (i-TFC-L), the GC fiber post and Unifil Core EM (GCF), and the FiberKor post and Build-It FR (FKP) as core construction systems, and Nishika Canal Sealer BG (CS-BG), Metaseal Soft (META), and Nishika Canal Sealer EN (CS-EN) as sealers. The light transmission of fiber posts (n = 5), the polymerization of core resin (n = 5), and the adhesion between the sealer and core resin (n = 10) were evaluated. The i-TFC Luminus fiber post light transmission was significantly higher than that of other posts. Without shielding, i-TFC-L showed a significantly greater amount of polymerized resin than the other systems. With shielding, although i-TFC-L showed a significantly greater amount of polymerized resin immediately after light irradiation, polymerized resin was significantly greater in GCF and FKP after 10 min. All systems adhered to CS-BG and META but not to CS-EN. These results indicate that resin polymerization in the cavity differs among fiber post/core resin construction systems and that the adhesion of the resin and sealer depends on the property of the sealer.

Influence of Oxidation of Copper on Shear Bond Strength to an Acrylic Resin Using an Organic Sulfur Compound

The aim of this study was to clarify the influence of the copper surfaces changed from Cu or Cu₂O to CuO on the bonding strength of resin with organic sulfur compounds. The disk-shaped specimens (n = 44) of copper were wet-ground. Half of the specimens were heated at 400 °C for 4 min in an electric furnace (HT: heated). Half of the specimens were not heated (UH: unheated). The specimens were further divided into two groups. Each group was primed by 6-methacryloyloxyhexyl 2-thiouracil-5-carboxylate (MTU-6) or unprimed (n = 11). A statistical analysis of the results of shear bond strength testing was performed, and the failure mode of the bonded areas was classified with an optical microscope. Two types of specimen surface (UH or HT) were analyzed chemically using X-ray photoelectron spectroscopy (XPS). When primed with MTU-6, unheated Cu (28.3 MPa) showed greater bond strength than heated (19.1 MPa). When unprimed, heated Cu (4.1 MPa) showed greater bond strength than unheated (2.3 MPa). The results of the debonded surfaces observation showed that only the UH-MTU-6 group demonstrated a combination of adhesive and cohesive failures in all specimens. The XPS results showed that the surface of copper changed from Cu or Cu₂O to CuO when HT. These results confirmed that it is necessary to take care of the copper oxide contained in noble metal alloys when using organic sulfur compounds for adhesion.

Adhesive bonding of alumina air-abraded Ag-Pd-Cu-Au alloy with 10-methacryloyloxydecyl dihydrogen phosphate

The aim of this paper is to study changes in the Ag-Pd-Cu-Au alloy surfaces by alumina air-abrasion process and effect of those changes on the adhesive bonding characteristic. Surface roughness, surface composition and chemical state of the alumina air-abraded alloys were analyzed by a confocal laser scanning microscope, an energy dispersive X-ray spectroscopy and an X-ray photoelectron spectroscopy. The results showed that the alumina air-abrasion changed the alloy surface by mechanical roughening, alumina remain and copper oxidation. Effect of the changes in the alloy surface on the adhesive bonding characteristic was examined by using a methyl methacrylate/tri-n-butylborane derivative (MMA/TBB) resin cement with the 10-methacryloyloxydecyl dihydrogen phosphate (MDP) contained primer. The shear bond strength test results indicated that the surface oxidation by the abrasion is the main contributor that improved the adhesive bonding rather than other effects such as mechanical roughening or alumina remain.