Enhancement of dentin bond strength of resin cement using new resin coating materials

Influence of Immediate Dentin Sealing on Bond Strength of Resin-Based CAD/CAM Restoratives to Dentin: A Systematic Review of In Vitro Studies

Immediate dentin sealing (IDS) is a method of improving the bond strength of indirect dental restorative materials to dentin and belongs to the biomimetic protocols of contemporary dentistry. The purpose of this systematic review was to evaluate the effect of IDS on the bond strength of resin-based CAD/CAM materials to dentin. PubMed and MEDLINE, Scopus, and the Web of Science were searched by two individual researchers, namely for studies that have been published in English between 1 January 2005 and 31 December 2023 in accordance with the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) statement. The inclusion criteria encompassed articles related to in vitro studies, measuring the bond strength through microtensile bond strength (μ-TBS), micro-shear bond strength (μ-SBS), tensile bond strength (TBS) or shear bond strength (SBS) tests after the use of the IDS technique. The included restorative materials comprised resin-based CAD/CAM materials bonded to dentin. A total of 1821 studies were identified, of which 7 met the inclusion criteria. A meta-analysis was not deemed appropriate due to the high level of diversity inthe publications and techniques. The use of IDS yielded higher bond strength outcomesin various experimental conditions and resin-based CAD/CAM materials. Overall, IDS in CAD/CAM restorations may contribute to better clinical outcomesand improved restoration longevity due to this property.

Composite Injection Technique With a Digital Workflow: A Pragmatic Approach for a Protruding Central Incisor Restoration

Esthetic concerns frequently drive individuals to seek dental treatment, leading to a rising demand for minimally invasive and time-efficient procedures. The Minimal Intervention Dentistry (MID) concept, which employs dental adhesive and resin composites, offers an effective approach for enhancing esthetics while preserving natural tooth structure. This case report outlines the esthetic enhancement of a protruding maxillary right central incisor through a direct composite restoration approach, utilizing a composite injection technique with a digital workflow. A 42-year-old male patient presented with a discolored and protruding maxillary right central incisor. After declining orthodontic treatment due to time and cost constraints, the patient opted for an alternative approach. A digital wax-up was 3D printed to create a clear silicone index, enabling precise resin composite injection to achieve the desired esthetic outcome. After internal bleaching and minimal labial surface reduction, a flowable resin composite was applied freehand to the mesial-proximal surface using a curved plastic matrix manufactured universally. The composite injection technique was subsequently employed through the incisal opening of the clear silicone index to shape the labial surface and incisal edge. In order to address insufficient tooth reduction, an additional partial labial resin composite cutback was performed, ensuring minimal reduction while enhancing esthetics. This direct composite veneer restoration, combining conventional proximal surface creation with a composite injection technique utilizing a custom-made clear silicone index prepared via a digital workflow, emerged as a pragmatic solution in a case where orthodontic treatment was not preferred. Moreover, in situations of insufficient dentin preparation, additional cutback preparation and composite placement can enhance color matching with minimal reduction. The direct composite restoration, facilitated by the composite injection technique and digital workflow, effectively rectified the inclination of the protruding maxillary central incisor, highlighting the potential of this approach in addressing esthetic dental concerns. The research and clinical technique presented in this case report hold clinical importance by offering a minimally invasive and practical alternative to orthodontic treatment and conventional restorations for patients with esthetic concerns. The composite injection technique with a digital workflow preserves natural tooth structure, reduces chair time, and enhances esthetic outcomes. This approach is particularly relevant to esthetic dentistry as it addresses anterior dental malalignment and discolored teeth while prioritizing patient satisfaction and individualized care, aligning with the principles of pragmatic esthetics and MID. The potential for long-term durability and patient satisfaction makes it a valuable addition to esthetic dental practice.

Effect of Immediate Dentin Sealing on the Bonding Performance of Indirect Restorations: A Systematic Review

The popular immediate dentin sealing (IDS) technique is used to improve the bond strength of indirect restorations. This systematic review assessed whether bond strength is affected by the type of aging conditions, bonding agents, flowable resin composites, impression materials, temporary materials, and/or resin cement used within the IDS procedure. A comprehensive database search of PubMed, Embase, Scopus, Ovid Medline, Web of Sciences, Cochrane Library, Dentistry & Oral Sciences Source, and ProQuest was carried out up to 30 January 2024 without publication year or language limitations. Only in vitro full-texts regarding the effect of IDS on bond strength were included, and the quality of their methods was assessed via a Risk of Bias (RoB) test. In total, 1023 pertinent studies were initially found, and 60 articles were selected for review after screening for the title, abstract, and full texts. IDS application improves the bond strength of indirect restorations to dentin and reduces the negative effects of temporary materials on the bond durability of final indirect restorations. Filled dentin bonding agents or combinations with flowable resin composite are preferred to protect the IDS layer from conditioning procedures.

Dental Luting Cements: An Updated Comprehensive Review

The cementation of indirect restoration is one of the most important steps in prosthetic and restorative dentistry. Cementation aims to bond the prosthetic restoration to the prepared enamel or enamel and dentine. Successful cementation protocols prevent biofilm formation at the margin between tooth and restoration and minimize mechanical and biological complications. With the advancements in dental cements, they have been modified to be versatile in terms of handling, curing, and bond strengths. This review presents updates on dental cements, focusing on the composition, properties, advantages, limitations, and indications of the various cements available. Currently, dental restorations are made from various biomaterials, and depending on each clinical case, an appropriate luting material will be selected. There is no luting material that can be universally used. Therefore, it is important to distinguish the physical, mechanical, and biological properties of luting materials in order to identify the best options for each case. Nowadays, the most commonly used dental cements are glass-ionomer and resin cement. The type, shade, thickness of resin cement and the shade of the ceramic, all together, have a tangible influence on the final restoration color. Surface treatments of the restoration increase the microtensile bond strength. Hence, the proper surface treatment protocol of both the substrate and restoration surfaces is needed before cementation. Additionally, the manufacturer's instructions for the thin cement-layer thickness are important for the long-term success of the restoration.

Retention strength of monolithic zirconia crowns cemented with different primer-cement systems

BACKGROUND

The purpose of this in vitro study was to assess the influence of different cement systems with different ceramic primers on the retention strength of zirconia crowns.

METHODS

Thirty extracted molars were prepared with flat occlusal surfaces, 20 degrees taper, and 3 mm axial wall height. A zirconia crown with an occlusal bar was fabricated for each tooth. All specimens were divided (n = 10) into; Group M: Multilink Speed/Monobond N, Group P: Panavia V5/Clearfil Ceramic Primer Plus, Group D: Duo-Link universal/Z-Prime Plus. The intaglio surfaces of crowns were air-abraded using 50 µm alumina at 2.5 bar for 10 s. Then each crown was cemented onto its corresponding tooth. All specimens were thermocycled for 10,000 cycles between 5 and 55 °C. Each crown was subjected to gradually increasing vertical load along the path of insertion through hooks engaging the occlusal bar using a universal testing machine until failure. The force at dislodgment was recorded and retention strength was calculated for each specimen. The failure modes were recorded for each specimen. The data were statistically analyzed using one way ANOVA test followed by Tukey HSD test (α = .05).

RESULTS

Group D showed lowest strength (1.42 ± 0.23 MPa) and differed significantly (P < .001) from Group M (2.71 ± 0.45 MPa) and Group P (2.47 ± 0.41 MPa). There was no significant difference (P = .34) between Group M and Group P. The failure modes for Groups M and Group P were mainly cohesive, while Group D showed adhesive failure.

CONCLUSIONS

The retention strength of zirconia crowns was improved with Multilink Speed and Panavia V5 cement systems, while the use of the Duo-Link Universal cement system only showed half of those retention strength values.

Direct and semi-direct resin composite restoration in large cavity preparations: analysis of dentin bond strength stability and bottom/top microhardness ratio in a cavity model

To evaluate the influence of the restorative approach and aging time on dentin bond strength (BS), failure mode (FM), and bottom/top microhardness ratio (B/T) in a large dentin cavity model. A total of 102 bovine incisors were used to produce models of conical dentin cavities (4.0 mm thickness × 4.8 mm top diameter × 2.8 mm bottom diameter), which were restored using semi-direct filling (SDF) (Filtek™ Z250 XT + Scotchbond™ Universal/RelyX™ Ultimate luting system), direct bulk filling (DBF) (Filtek™ One Bulk Fill), and direct incremental filling (DIF) (Filtek™ Z250 XT) techniques. B/T, BS, and FM (n = 17) were analyzed in a microhardness tester, a universal testing machine, and a stereomicroscope, respectively, after 24 h and 6 months of water storage. BS and B/T data were analyzed using two-way ANOVA/Tukey post-hoc test (p < 0.05), while FM data were analyzed descriptively. There was a statistically significant difference in BS between the restorative techniques, and BS was influenced by aging time in the DBF and SDF groups. Mixed failure was predominant for the SDF technique in both aging times. There was no statistically significant difference in B/T among the restorative approaches regardless of the aging time (p > 0.05). Although all restorative approaches provided similar B/T, the semi-direct technique showed better performance on the material bond strength to dentine in large cavities.

Influence of the resin-coating technique on the bonding performance of self-adhesive resin cements in single-visit computer-aided design/computer-aided manufacturing resin restorations

OBJECTIVE

This in vitro study investigated the influence of resin coating on the bonding performance of self-adhesive resin cements in single-visit computer-aided design (CAD)/computer-aided manufacturing (CAM) resin restorations.

MATERIALS AND METHOD

CAD/CAM resin (1.5-mm thick) was mounted on 20 noncoated and 20 resin-coated human dentin surfaces using dual-cured self-adhesive resin cements (Panavia SA Cement Plus or Panavia SA Cement Universal, Kuraray Noritake Dental) in either self-curing or dual-curing mode. These specimens were sectioned into beam-shaped sticks and subjected to microtensile bond strength tests after 24 h of water storage. The obtained data were statistically analyzed with three-way analysis of variance (ANOVA) and t tests (α = 0.05).

RESULTS

The three-way ANOVA results revealed the significant influence of resin coating, resin cement, and curing mode. Resin coating and light curing led to higher bond strengths in almost all groups. Resin-coated dentin with Panavia SA Cement Plus exhibited a mean bond strength greater than 35 MPa in both self-curing and dual-curing modes.

CONCLUSIONS

In single-visit CAD/CAM resin restorations, resin coating, resin cement selection, and curing mode influenced the bonding performance of self-adhesive resin cements. In addition, resin coating and light curing increased the bond strength of self-adhesive resin cements. Resin coating and light curing are encouraged for predictable bonding performance of dual-cured self-adhesive resin cements in single-visit CAD/CAM resin restorations.

Immediate Dentin Sealing: A Literature Review

Purpose

The immediate application of a dentin-bonding agent after tooth preparation and before impression-taking (immediate dentin sealing [IDS]) has been suggested to provide several advantages concerning bacterial microleakage, hypersensitivity, and bonding quality. We reviewed the literature and clarified certain aspects related to each step of IDS application.

Materials and Methods

The search strategy comprised an electronic research in MEDLINE, Cochrane, Ovid and Scopus for studies published from January 1990 to December 2020 regarding the IDS technique and including both in vitro and clinical studies.

Results

After exclusion of irrelevant or duplicate articles, 88 articles focusing on aspects of the IDS technique were assessed. IDS seems to be advantageous with regard to bond strength, gap formation, bacterial microleakage, and dentin hypersensitivity. However, issues arising from interaction with impression materials, the provisional phase, and conditioning methods before cementation require further investigation.

Conclusion

There are no documented reasons preventing clinicians applying IDS in their everyday practice. On the contrary, the presented technique seems to be beneficial in certain aspects regarding indirect restorations.

Effect of a temporary sealing material on the bond strength of CAD/CAM inlay restorations with resin-coating technique

This study aimed to assess the effects of a temporary sealing material and cleaning method of resin-coated dentin on the bond strength of computer-aided design/computer-aided manufacturing (CAD/CAM) inlay restorations. Resin-coated dentin surfaces were unsealed or temporarily sealed for 1 h or 1 week. For the temporarily sealed group, a hydraulic temporary sealing material was removed and further divided into four groups: without cleaning, cleaned with a rotational brush, a universal cleaner or an air-polishing device. Some specimens were investigated with energy dispersive X-ray spectroscopy and the others were used for microtensile bond strength (MTBS) test. A sealing material could not be removed with a rotational brush, which resulted in pretest failures in all specimens after 1 h and which resulted in low MTBS after 1 week. An air-polishing device can clean resin-coated dentin temporarily sealed with a hydraulic temporary sealing material and resulted in the similar MTBS as in the unsealed group.

The effect of temporary sealing materials and cleaning protocols on the bond strength of resin cement applied to dentin using the resin-coating technique

This study evaluated the effect of temporary sealing materials and cleaning protocols on the bond strength of resin cement applied to dentin using resin-coating technique. Scotchbond Universal Adhesive and Filtek Supreme Ultra Flowable were applied to bovine dentin. Forty-five specimens were divided into the following three groups according to the temporary sealing materials: Cav-: CAVITON EX, Vas-: COCOA BUTTER and FIT SEAL, and Sep-: Washable SEP and FIT SEAL. Each material was placed on resin-coated dentin. After 1-week water storage, one of the following three cleaning protocols was performed: -WA: washed with water, -BR: brushed with PRESSAGE, and -AF: cleaned with AIR-FLOW. Microtensile bond strength test and EDS analysis were conducted. Irrespective of the cleaning protocol used, Washable SEP demonstrated less residual debris on resin-coated dentin, resulting in high bond strength. Regardless of the temporary sealing material applied, AIR-FLOW demonstrated less residual debris, resulting in high bond strength.

Replacing mandibular central incisors with a direct resin-bonded fixed dental prosthesis by using a bilayering composite resin injection technique with a digital workflow: A dental technique

A straightforward technique is presented for an interim or short-term definitive esthetic replacement of missing anterior teeth requiring no tooth preparation. Composite resins are injected into transparent silicone indices fabricated from 3-dimensional-printed casts of a digital waxing. The dentin core is formed of a durable short fiber-reinforced injectable composite resin and veneered with an enamel-shade composite resin for enhanced esthetics. Besides being noninvasive, this technique is more straightforward than traditional options, reducing chair time while providing an accurate outcome.

Post-orthodontic recontouring of anterior teeth using composite injection technique with a digital workflow

OBJECTIVE

Restorative treatment of anterior teeth is often required as the final step of orthodontic therapy to optimize the esthetics and function. This case report presents a direct minimally invasive approach for post-orthodontic recontouring of anterior teeth using the composite injection technique with a digital workflow.

CLINICAL CONSIDERATIONS

The extraction of central incisors with short roots was indicated to resolve maxillary anterior crowding. The gained space was closed with lateral incisors, and it was necessary to recontour them and canines to resemble central and lateral incisors, respectively. The restorations were digitally designed, and a transparent silicone index was fabricated from a 3D-printed cast of the digital wax-up. After lateral incisors and canines were bonded with a universal adhesive in the etch-and-rinse mode, a highly filled injectable composite resin was applied into the index. The restorative treatment was preceded by gingivectomy using an Er:YAG laser and home bleaching.

CONCLUSIONS

In cases where more complex recontouring of anterior teeth is necessary, the composite injection technique could be a suitable alternative to indirect restorations, because it is straightforward, cost-effective, and does not require any preparation. The digital workflow simplified and expedited the treatment while contributing to its precision.

CLINICAL SIGNIFICANCE

Post-orthodontic recontouring using direct composite restorations is well accepted by patients due to low cost and non-invasiveness. However, in complicated cases, the free-hand technique is time-consuming and technique-sensitive. The presented composite injection technique with a digital workflow significantly simplifies and expedites the composite placement while predictably enhancing the treatment outcome.

CAD/CAM-fabricated inlay restorations: Can the resin-coating technique improve bond strength and internal adaptation?

This study assessed the effect of the resin-coating technique on the bond strength and internal adaptation of computer-aided design/computer-aided manufacturing (CAD/CAM)-fabricated inlays. Seventy-two mesio-occlusal-distal (MOD) cavities were prepared and distributed into 3 groups according to the resin-coating technique utilized: uncoated group, G-Premio Bond (1-step) group, and Clearfil SE Bond 2+Clearfil Majesty ES Flow (2-step+Flow) group. The MOD inlays were fabricated and cemented with RelyX Ultimate (RXU), G-CEM LinkForce (LinkForce), or Panavia V5 (PV5). After 5,000 thermal cycles, each specimen was sectioned and subjected to microtensile bond strength (MTBS) testing and an internal adaptation evaluation. For the uncoated group, RXU exhibited higher MTBS than LinkForce and PV5 (p<0.05). The MTBS of all 1-step and 2-step+Flow groups was greater than 30 MPa. Resin coating did not influence the MTBS of RXU, whereas resin coating increased the MTBS of LinkForce and PV5. More than 95% gap-free margins were found in all groups.