The influence of resin composite with high fiber aspect ratio on fracture resistance of severely damaged bovine incisors

Effects of glass fibers reinforced and non-reinforced composite resin on fracture behavior of severely destructed primary incisors and restored with post and core system

Objective

To evaluate fracture resistance and failure type of coronally rehabilitated primary incisors with EverX Flow or Grandio Core post and core with or without fiber post.

Materials and Methods

Forty-eight extracted maxillary primary incisors were root canal treated and obturated with Metapex. The coronal 4-mm of Metapex was removed to create 3-mm intracanal post space. Next, coronal enamel and radicular dentin surfaces were acid-etched, and a bonding agent was applied and light-cured. Based on intracanal post and 2-mm height core buildup materials, specimens were divided equally (n = 12) into 4 groups as follow; Group I (EverX Flow), Group II (Grandio Core), Group III (Fiber post, and EverX Flow), and Group IV(Fiber post and Grandio Core). The coronal restorations were finalized to 4-mm height using G-aenial Anterior composite and specimens were tested for fracture resistance. Force required to induce fracture was recorded and failure type was examined.

Results

Fracture resistance of Fiber post and EverX Flow group was statistically significant high than other tested groups. However, fracture resistance of EverX Flow group showed non-statistically significant difference from that of Fiber post and Grandio Core group. Regarding failure type, no specimen presented root fracture, and all failures were favorable and repairable.

Conclusion

EverX flow post and core with or without fiber post enhanced fracture resistance of restored primary incisors compared to Grandio Core alone.

Clinical relevance

EverX flow post and core system with or without fiber post could be a promising restorative option for severely destructed primary incisors.

Evaluation of microhardness of short fiber-reinforced composites inside the root canal after different light curing methods - An in vitro study

OBJECTIVES

Short fiber-reinforced composite (SFRC) materials make it possible to reinforce root canal treated teeth with individualized, directly layered intraradicular posts (the Bioblock technique). The question arises, however, as to whether the photopolymerization of the material is sufficient deep within the root canal space and if it can be improved through different light-conducting options. Our study aimed to investigate the hardness of intraradicular SFRC material applied using the Bioblock technique and cured with various illumination methods, as measured through nanoindentation.

MATERIALS AND METHODS

For this investigation, thirty plastic artificial teeth that had undergone root canal treatment were selected. These teeth were randomly divided into six study groups (Group 1-6; each group consisting of 5 teeth). The restoration procedures involved the use of SFRC or conventional composite materials, placed 6 mm apically from the root canal orifice. In Group 1 and 2, a conventional composite was used, whereas in Group 3-6, SFRC was employed for interradicular reinforcement (with a layered technique in Group 3 and 4 and a bulk-fill technique in Group 5 and 6). A modified light source was utilized for photopolymerization in Group 2, 4, and 6, whereas in Group 3 and 5, the polymerization light was directed through a prefabricated glass fiber posts. The control group (Group 1) utilized conventional composite material with a standard light-curing method. Following embedding and sectioning, the hardness of the composite materials was measured at 2 mm intervals within the root canal (1st, 2nd, 3rd measurements, in the coronal to apical direction).

RESULTS

During the 1st measurement, light curing conducted through the glass fiber posts (Group 3 and 5) led to markedly higher hardness levels compared to the groups restored with conventional composite (control group with p = 0.002, p = 0.001, and Group 2 with p = 0.043, p = 0.034, respectively). In the 2nd measurement, only Group 5 demonstrated significantly greater hardness in comparison to the control group (p = 0.003) and Group 2 (p = 0.015). However, in the 3rd measurement, no statistically significant differences were observed among the groups.

CONCLUSION

light curing through the glass fiber post provides outstanding hardness for the SFRC material in the apical layer in the root canal.

Adhesion of individually formed fiber post adhesively luted with flowable short fiber composite

This laboratory study aimed to measure the push-out bond strength of individually formed fiber-reinforced composite (FRC) post luted with flowable short fiber-reinforced composite (SFRC) and to evaluate the influence of post coating with light-cured adhesive. Post spaces (Ø 1.7 mm) were drilled into 20 single-rooted decoronated premolar teeth. Post spaces were etched and treated with light-cured universal adhesive (G-Premio Bond). Individually formed FRC posts (Ø 1.5 mm, everStick) were luted either with light-cured SFRC (everX Flow) or conventional particulate-filled (PFC) dual-cure luting cement (G-CEM LinkForce). Half of the posts from each group were treated with dimethacrylate adhesive resin (Stick Resin) for 5 min before luting. After storage in water for two days, the roots were sectioned into 2 mm thick disks (n = 10/per group). Then, a push-out test-setup was used in a universal testing machine to measure the bond strength between post and dentin. The interface between post and SFRC was inspected using optical and scanning electron microscopy (SEM). Data were statistically analyzed using analysis of variance ANOVA (p = .05). Higher bond strength values (p < .05) were obtained when flowable SFRC was used as a post luting material. Resin coating of a post showed no significant effect (p > .05) on bond strength values. Light microscope images showed the ability of discontinuous short fibers in SFRC to penetrate into FRC posts. The use of flowable SFRC as luting material with individually formed FRC posts proved to be a promising method to improve the interface adhesion.

In Vitro Comparison of Fracture Resistance of Severely Damaged Primary Anterior Teeth Restored with Different Post and Core Systems

Objectives

This study aimed to compare the fracture resistance (FR) of severely damaged primary anterior teeth restored with five different post and core systems.

Materials and Methods

This in vitro, experimental study evaluated 60 extracted primary maxillary central incisors. The teeth were horizontally sectioned at 1 mm above their cementoenamel junction (CEJ), underwent pulpectomy, and their root canals were filled with Metapex paste. After post space preparation and sealing of root fillings with light-cure glass ionomer (1 mm thickness), the teeth were randomly assigned to five groups (n = 12) of (1) glass fiber post and everX composite (reinforced with short fibers), (2) glass fiber post and bulk-fill composite, (3) everX composite post and core, (4) bulk-fill composite post and core, and (5) Filtek conventional composite post and core. The teeth underwent 5,000 thermal cycles between 5°C and 55°C, and their FR was measured in a universal testing machine (0.5 mm/min, 148°). The mode of failure was also determined. Data were analyzed by ANOVA and Tukey's test at 0.05 level of significance.

Results

The FR was the highest in fiber post and everX composite, and the lowest in Z250 conventional composite post and core group (P < 0.001). The FR of fiber post and everX composite group was significantly higher than that of everX composite post and core (P = 0.04), bulk-fill composite post and core (P = 0.001), and Z250 composite post and core (P < 0.001) groups. The frequency of repairable fractures was the highest in glass fiber post plus everX composite (91.66%) and the lowest in Filtek conventional post and core group (66.66%) (P > 0.05).

Conclusion

Within the limitations of this in vitro study, the results showed that restoration of severely damaged primary maxillary central incisors with glass fiber post and everX composite reinforced with short fibers enhanced their FR, and increased the chance of reparability in case of restoration fracture. This technique may be recommended for the restoration of primary anterior teeth since it is simple and saves time.

Fracture Resistance of Anterior Crowns Reinforced by Short-Fiber Composite

The aim of this study was to investigate the load-bearing capacity of anterior crowns made of different commercial particulate-filled composites (PFCs) and reinforced by a core of short-fiber composite (SFC) (bilayer structure). Four groups of composite crowns were fabricated for an upper central incisor (n = 20/group). Two groups were made of chair-side PFC composites (G-aenial anterior, GC, Japan and Denfil, Vericom, Korea) with or without SFC-core (everX Flow, GC). One group was made of laboratory PFC composite (Gradia Plus, GC) with or without SFC-core. The last group was made of plain SFC composite polymerized with a hand-light curing unit only or further polymerized in a light-curing oven. Using a universal-testing device, crown restorations were statically loaded until they fractured, and failure modes were visually investigated. Analysis of variance (p = 0.05) was used to evaluate the data, followed by Tukey’s post hoc test. Bilayer structure crowns with SFC-core and surface PFC gave superior load-bearing capacity values compared to those made of monolayer PFC composites; however, significant differences (p < 0.05) were found in the chair-side composite groups. Additional polymerization has no impact on the load-bearing capacity values of SFC crowns. Using SFC as a core material with PFC veneering composite to strengthen anterior crown restorations proved to be a promising strategy for further testing.

Stress distribution in restorations with glass fiber and polyetheretherketone intraradicular posts: An in silico analysis

This study evaluated stresses generated at maxillary central incisor (21) root restored with lithium disilicate crown (LDC), and glass fiber (GFP) or polyetheretherketone (PEEK) post. 3D models created by computed tomographic image (i-CAT Cone Beam 3D Dental Imaging System) reproduced maxillary central incisor. Each model had prosthetic LDCs (2.0 mm thick) cemented to GFP or PEEK posts with dual resin cement. Different loads were applied to each model (cervical, incisal, axial, middle). At maximum principal stress, PEEK showed higher stress than GFP in all loads, but with qualitative similarity. At minimum principal stress, PEEK and GFP showed qualitative and quantitative similarities, except axial load. Maxillary central incisor restored with GFP or PEEK and LDC presented, in general, similar stress intensity and distribution for main occlusal loads. Only two of sixteen occlusal loads tested (cervical for maximum principal; axial for minimum principal) showed significant quantitative difference.

Evaluation of New Hollow Sleeve Composites for Direct Post-Core Construction

The preset shape and diameter of a prefabricated FRC post rarely follows the anatomy of the root canal. To solve this problem, a new hollow sleeve composite (HSC) system for post-core construction was developed and characterized. A woven fiber was impregnated with two types of resins: Bis-GMA or PMMA, and rolled into cylinders with outer diameter of 2 mm and two different inner diameters, namely 1.2 or 1.5 mm. The commercial i-TFC system was used as a control. Dual-cure resin composite was injected into these sleeves. Additionally, conventional solid fiber post was used as the inner part of the sleeve. The three-point bending test was used to measure the mechanical properties of the specimens and the fracture surface was examined using an electron microscope (SEM). The HSC (1.5 mm, Bis-GMA) revealed a statistically similar flexural modulus but higher flexural strength (437 MPa) compared to i-TFC (239 MPa; ANOVA, p < 0.05). When a fiber post was added inside, all values had a tendency to increase. After hydrothermal accelerated aging, the majority of specimens showed a significant (p < 0.05) decrease in flexural strength and modulus. SEM fracture analysis confirmed that the delamination occurred at the interface between the outer and inner materials. The HSC system provided flexibility but still high mechanical values compared to the commercial system. Thus, this system might offer an alternative practical option for direct post-core construction.

Fatigue performance of endodontically treated premolars restored with direct and indirect cuspal coverage restorations utilizing fiber-reinforced cores

Objectives

The aim of this in vitro study was to investigate the fatigue survival and fracture behavior of endodontically treated (ET) premolars restored with different types of post-core and cuspal coverage restorations.

Materials and methods

MOD cavities were prepared on 108 extracted maxillary premolars. During the endodontic treatment, all teeth were instrumented with rotary files (ProTaper Universal) to the same apical enlargement (F2) and were obturated with a matched single cone obturation. After the endodontic procedure, the cavities were restored with different post-core and overlay restorations (n = 12/group). Three groups (A1–A3) were restored with either conventional composite core (PFC; control) or flowable short-fiber-reinforced composite (SFRC) core with/without custom-made fiber posts and without overlays. Six groups had similar post-core foundations as described above but with either direct PFC (B1–B3) or indirect CAD/CAM (C1–C3) overlays. Fatigue survival was tested for all restorations using a cyclic loading machine until fracture occurred or 50,000 cycles were completed. Kaplan-Meyer survival analysis was conducted, followed by pairwise post hoc comparisons.

Results

None of the restored teeth survived all 50,000. Application of flowable SFRC as luting-core material with fiber post and CAD/CAD overlays (Group C3) showed superior performance regarding fatigue survival (p < 0.05) to all the other groups. Flowable SFRC with fiber post and direct overlay (Group B3) showed superior survival compared to all other direct techniques (p < 0.05), except for the same post-core foundation but without cuspal coverage (Group A3).

Conclusions

Custom-made fiber post and SFRC as post luting core material with or without cuspal coverage performed well in terms of fatigue resistance and survival when used for the restoration of ET premolars.

Clinical relevance

The fatigue survival of direct and indirect cuspal coverage restorations in ET MOD premolars is highly dependent on whether the core build-up is fiber-reinforced or not. The combination of short and long fibers in the form of individualized post-cores seems to offer a favorable solution in this situation.

Fracture strength of teeth with coronal destruction after core build-up restoration with bulk fill materials

OBJECTIVE

This study aimed to evaluate the fracture strength and failure modes of different core techniques in teeth with simulated coronal destruction.

MATERIALS AND METHODS

Forty teeth were endodontically prepared and the specimens were divided into four experimental groups (n = 10) according to the core composition: Filtek One Bulk Fill-FOBF, Filtek Z350 XT-FZ350 (standard group), Filtek Bulk Fill Flow-FBFF, and LuxaCore Z-LCZ. CAD/CAM Monolithic zirconia crowns were obtained and cemented with RelyX U200. After storage in distilled water at 37°C for 48 h, the specimens were subjected to thermal cycling and to compressive strength mechanical tests. Statistical analyses (α = 0.05) were performed by non-parametric Kruskal-Wallis, Dunn post hoc, and Fisher's exact tests.

RESULTS

No significant differences (p > 0.05) were observed among FOBF, FZ350, and FBFF (mean ranks = 20.30, 12.20, and 23.20, respectively). LCZ (mean rank = 26.30) produced results similar to those of FOBF and FBFF (p > 0.05) and higher than those of FZ350 (p = 0.042). The most frequent type of failure was irreparable, regardless of the experimental condition. The lowest percentages of reparable fractures were produced by FOBF group (10%).

CONCLUSIONS

The use of bulk fill materials, including the "core-and-post" LCZ dual-cure resin composite, did not impair the fracture strength of endodontically treated teeth with coronal destruction.

CLINICAL SIGNIFICANCE

Resin composite bulk fill materials that can be used as a core-and-post cementation in an only stage are interesting, since they enable clinicians to work with one only material, and avoid several materials interfaces, technical sensitivity, and longer chair-time due to multistep procedures.

Effect of cervical lesion centered access cavity restored with short glass fibre reinforced resin composites on fracture resistance in human mandibular premolars- an in vitro study

AIM

The aim of this study was to evaluate the fracture resistance of cervical lesion centered access cavity restored with short glass fibre reinforced resin materials in human mandibular premolars.

MATERIALS AND METHODS

Sixty freshly extracted human mandibular premolars were collected and assigned to positive control group (G1- Intact teeth) and other experimental groups (G2, G3. G4, G5, G6), Traditional Access Cavity(TAC) and Cervical Lesion Centered Access Cavity(CLCAC). Following endodontic therapy, samples were grouped accordingly, G2-CLCAC without restoration (Negative Control), G3-CLCAC restored with conventional nano-hybrid composite (Tetric-N-Ceram), G4-TAC restored with short glass fibre reinforced resin composite (Ever-X Posterior), G5-CLCAC restored with short glass fibre reinforced resin composite (Ever-X Posterior), G6- CLCAC restored with individually formed unidirectional fibre-reinforced post (Everstick post) and short glass fibre-reinforced resin composite (Ever-X Posterior). The samples were thermocycled (35 °C/28s, 15 °C/2s, 35 °C/28s, 45 °C/2s/10,000 cycles) and cyclically fatigued(2,50,000 cycles/15-30N/2 Hz) and then subsequently loaded to failure. The mean load to fracture (Newtons) were statistically analyzed using one-way ANOVA and Tukey's post HOC test and failure mode analysis was also done.

RESULTS

The mean fracture resistance of the CLCAC design restored with fibre reinforced materials was higher when compared to the TAC design but the difference was not statistically significant. The negative control group (CLCAC without restoration) showed significantly the least fracture resistance (P < 0.05) when compared to all the other groups except for group 3 (CLCAC restored with conventional composites).

CONCLUSIONS

Within the limitations of the study, it can be concluded that short glass fibre reinforced resin composites improved the fracture resistance of endodontically treated mandibular premolars irrespective of the type of access cavity designs. Favourable fractures were seen more in cervical lesion centered access cavity restored with short glass fibre reinforced composite materials. Nevertheless, the applicability of this design in multirooted teeth, canal cleanliness efficacy, and long term clinical performance are yet to be explored to complement this new access design.

Influence of Post-Core and Crown Type on the Fracture Resistance of Incisors Submitted to Quasistatic Loading

The aim of this paper was to evaluate the fracture resistance and failure type of maxillary incisor teeth, rebuilt with various types of post-core restorations and full crowns made of either direct conventional particulate filler composite (PFC, G-aenial Anterior, GC, Tokyo, Japan) or indirect CAD/CAM restorations (composite Cerasmart 270 and glass ceramic LiSi Block from GC). One hundred (n = 10/group) central incisors were cut and divided into 10 experimental groups restored with different approaches. In approach A, teeth were restored with a core build-up composite (Gradia Core, GC) for a core and full crown of PFC. Approach B had teeth restored using composite core and prefabricated fiber posts, and a complete crown of either PFC or CAD/CAM. Approach C contained teeth restored with a core of short fiber-reinforced composite (everX Flow, GC) and prefabricated fiber posts, and a complete crown of either PFC or CAD/CAM. In approach D, the teeth had a core of short fiber-reinforced composite only, and a complete crown of either PFC or CAD/CAM restorations. The root canals were prepared, and when posts were used, they were luted with either a dual-cure resin cement (LinkForce, GC) or everX Flow. As the control, sound teeth (n = 10) were used. Restorations were quasi-statically loaded until fracture. Failure type was visually investigated. The interface between the fiber post and luting cement was investigated using SEM, before and after completion of the loading test. The data were analyzed by analysis of variance (p = 0.05) followed by Tukey's test. None of the restorative approaches restored the fracture load strength of intact teeth (p < 0.05). Restorations with additional fiber posts (Approaches B and C) had higher load-bearing capacity (p < 0.05) than restorations without fiber posts (Approaches A and D). Restorations that had short fiber-reinforced composite cores with or without fiber posts presented more repairable failures. Using short fiber-reinforced composite as post-luting and core build-up material with conventional fiber posts proved to be a promising method to strengthen severely damaged incisors.