Effect of heat treatment on cytotoxicity and polymerization of universal adhesives

The Use of Warm Air for Solvent Evaporation in Adhesive Dentistry: A Meta-Analysis of In Vitro Studies

Any excess solvent from dental adhesive systems must be eliminated prior to material photopolymerization. For this purpose, numerous approaches have been proposed, including the use of a warm air stream. This study aimed to investigate the effect of different temperatures of warm air blowing used for solvent evaporation on the bond strength of resin-based materials to dental and nondental substrates. Two different reviewers screened the literature in diverse electronic databases. In vitro studies recording the effect of warm air blowing to evaporate solvents of adhesive systems on the bond strength of resin-based materials to direct and indirect substrates were included. A total of 6626 articles were retrieved from all databases. From this, 28 articles were included in the qualitative analysis, and 27 remained for the quantitative analysis. The results of the meta-analysis for etch-and-rinse adhesives revealed that the use of warm air for solvent evaporation was statistically significantly higher (p = 0.005). For self-etch adhesives and silane-based materials, this effect was observed too (p < 0.001). The use of a warm air stream for solvent evaporation enhanced the bonding performance of alcohol-/water-based adhesive systems for dentin. This effect seems to be similar when a silane coupling agent is submitted to a heat treatment before the cementation of a glass-based ceramic.

Nanofiller Particles and Bonding Durability, Water Sorption, and Solubility of Universal Adhesives

The aim of this study was to evaluate the influence of nanofiller particles in simplified universal adhesive on the long-term microtensile bond strength and silver nitrate up-take, as well as water sorption and solubility. Commercial adhesives Ambar Universal (FGM) in nanofilled-containing version (filled) and same lot without fillers (unfilled) were donated and applied by means of etch-and-rinse strategy. Microtensile bond strength was surveyed after 24-hours or 1-year water storage. Silver nitrate uptake was assayed using scanning electron microscopy (SEM). Water sorption and solubility experiments were performed based on ISO 4049:2009. Statistical analysis was performed using two-way ANOVA and Tukey test (p<0.05). The bond strength of both the adhesives were statistically similar at 24 hours (p>0.05), but the filled group attained significant bond strength reduction after aging when compared to initial bond strength (p<0.001). Conversely, unfilled adhesive presented stable adhesion after 1-year storage (p=0.262). Silver nitrate uptake was similar for both adhesives, with little silver impregnation at the hybrid and adhesive layers. Water sorption was higher with filled adhesive compared to the unfilled one (p=0.01). Conversely, solubility was higher in unfilled in comparison to filled one (p=0.008). The presence of nanofillers in universal adhesive achieves higher water sorption and dentin bond degradation, which did not occur in the unfilled adhesive.

Effect of Time and Temperature of Air Jet on the Mechanical and Biological Behavior of a Universal Adhesive System

OBJECTIVES

To evaluate the influence of heat application on the degree of conversion (DC) of the 3M Single Bond Universal Adhesive System, as well as its transdentinal cytotoxicity and microtensile bond strength to dentin.

METHODS

Experimental groups were established according to the time and temperature of the air jet: G1: 5 seconds-25°C; G2: 10 seconds-25°C; G3: 20 seconds-25°C; G4: 5 seconds-50°C; G5: 10 seconds-50°C; G6: 20 seconds-50°C. In control group (G7), no treatment was performed. The DC was assessed using the Fourier transform infrared spectroscopy-attenuated total reflectance (FTIR-ATR) technique. For the transdentinal cytotoxicity test, dentin discs fitted in artificial pulp chambers (APC) received the application of the adhesive system and the air jets. For the microtensile bond strength, healthy molars were restored and submitted to the microtensile test after 24 hours and 6 months, respectively.

RESULTS

Significant reduction in viability of Mouse Dental Papilla Cell-23 (MDPC-23), which exhibited morphological changes, was observed in all experimental groups compared to control (p<0.05). Although all tested protocols resulted in transdentinal diffusion of 2-hydroxyethyl methacrylate (HEMA), the group G6 presented the highest degree of monomeric conversion and the lowest cytotoxic effect, with higher dentin bond strength values in comparison to group G1 (p<0.05).

CONCLUSIONS

Applying an air blast at 50°C for 20 seconds increases the DC and microtensile bond strength of the 3M Single Bond Universal Adhesive System to dentin, as well as reduces the transdentinal cytotoxicity of the material to pulp cells.