Effect of two bleaching regimens on enamel bonding performance

Fracture strength and bonding interface morphology of CAD/CAM-fabricated ceramic laminate veneers on bleached enamel treated with two different antioxidants

This study aimed to investigate the effects of two antioxidants and their application time on the fracture strength of computer-aided design and computer-aided manufacturing (CAD/CAM)-fabricated ceramic laminate veneers to bleached enamel, as well as their effects on the bonding interface micromorphology. Eight groups were set: Group NC (without bleaching and antioxidant treatment); Group NA (bleaching without antioxidant treatment); Group SA30, SA60, SA120 and Group PAC30, PAC60, PAC120 (bleaching and treating with sodium ascorbate or proanthocyanidins for 30, 60, and 120 min, respectively). After cementation of veneers, fracture strength values and failure modes were analyzed. The bonding interface morphology was observed by confocal laser scanning microscopy. The fracture strength was impaired when cementation procedure was performed immediately after bleaching. This reduction in fracture strength was reestablished with antioxidant treatment, and an extended treatment time contributed to better improvement. The resin tags at the bonding interfaces of the bleached enamel were impaired. Antioxidant treatments were able to reverse this unfavorable trend.

Influence of primer contamination on the bonding interface of enamel pre-etched with phosphoric acid

In this study, the influence of primer contamination on enamel bonding was analyzed. Adper Scotchbond Multi-Purpose (SMP), CLEARFIL SE Bond 2 (SE2), Scotchbond Universal (SBU) Adhesive, and Scotchbond Etchant (35% phosphoric acid; PA) were used. Ground bovine enamels were divided into eight groups based on the bonding protocols. The bonding interfaces after an acid-base challenge were observed via scanning electron microscopy to determine the acid-base resistant zone (ABRZ). Moreover, the bonding interfaces after the nanoleakage challenge were analyzed via energy-dispersive X-ray spectroscopy. ABRZ was observed in all the samples except PA_ONLY (applied PA etching, No primer and No adhesive resin). The funnel-shaped erosion was detected only in X_SBU (applied SBU without PA etching). The nanoleakage test revealed silver patterns in some groups. The nanoleakage, i.e., the penetration of the silver ions, was detected in the groups wherein primer was applied on PA-pre-etched enamel.