Simultaneous detection of monomers associated with resin-based dental composites using SPME and HPLC

Characteristics of Bulletproof Vests Made from COPEFB Fiber: Implications on Mechanical, Electrical, and Physical Resistance

This research aims to examine the characteristics of bulletproof vests from corncob oil palm empty fruit bunch (COPEFB) biocomposite, where mechanical, electrical, and physical resistance tests have been successfully conducted. The variations in the diameter of the twisted thread used to make the basic material for bulletproof vests include 1 mm, 3 mm, 6 mm, and 10 mm, which were tested for their mechanical, electrical, and physical properties. To identify which biocomposite is good at damping bullets, an impact and a firing test were carried out to determine the kinetic energy and the depth of the bullet, respectively. The results showed that the impact value improved with an increase in the diameter of the twisted yarn used. The largest and the lowest impact values were 1.157 kJ and 0.277 kJ on the epoxy sample with a twisted thread diameter of 10 mm and 1 mm, respectively. It was also discovered that the biocomposite samples made from 6 mm to 10 mm twisted threads were the best samples, impermeable to bullets. This was due to the excess natural fiber content which improved the flexibility and absorption of kinetic energy from the high rate of projectile bullets. According to the results of the firing test, some samples are translucent, while others cannot be penetrated by bullet projectiles. The projectile went inside, and the composite was damaged. All the high filler loading samples were translucent to bullets, while some of the low loading samples were translucent and impermeable to bullets. Based on these results, biocomposite samples made of 6 mm and 10 mm twisted yarn are the best samples that are impermeable to bullets.

Embedding environmental sustainability within oral health professional curricula-Recommendations for teaching and assessment of learning outcomes

The FDI World Dental Federation suggests that "dentistry, as a profession, should integrate Sustainable Development Goals into daily practice and support a shift to a green economy in the pursuit of healthy lives and wellbeing for all, through all stages of life." This article reports on the recent activity of the Association for Dental Education in Europe Special Interest Group for Sustainability in Dentistry. Following on from the group's previous activities, which explored current educational practice, this work aimed to reach a pan-European consensus on a number of learning outcomes for environmental sustainability, in order to (i) support institutions in designing and delivering their curriculum, and (ii) to further harmonise the delivery of oral health professional education across Europe. This article presents specific learning outcomes relating to environmental sustainability and recommendations relating to curriculum development, including methods of teaching and assessment.

Resin-based composite materials: elution and pollution

Pollution arises from all human activity and the provision of oral healthcare using resin-based composite restorative materials (RBCs) should be considered. This paper aims to provide a comprehensive review of the potential pollutant risk to the environment from the chemical compounds found in resin-based restorative materials, by including: 1) the principal pollutant compounds present in the resin matrix; 2) the degradation process of RBCs and its consequences; 3) the methods used for the detection and quantification of monomer elution and RBC microparticles; and 4) a review of the release mechanisms of eluates and RBC microparticles into the environment.RBCs are pollutants by virtue of the compounds created during the degradation processes. These are in the form of the constituent eluted monomers and microparticles. Their impact on the environment and biodiversity is unknown. These materials are currently one of the main direct-placement restorative materials and their success is unquestionable when used and maintained correctly. Mitigation strategies for reducing the impact of pollution on the environment should be considered and implemented by all stakeholders and processes in the supply chain, from manufacturing, clinical use and waste management.

Monomer Release from Dental Resins: The Current Status on Study Setup, Detection and Quantification for In Vitro Testing

Improvements in mechanical properties and a shift of focus towards esthetic dentistry led to the application of dental resins in various areas of dentistry. However, dental resins are not inert in the oral environment and may release monomers and other substances such as Bisphenol-A (BPA) due to incomplete polymerization and intraoral degradation. Current research shows that various monomers present cytotoxic, genotoxic, proinflammatory, and even mutagenic effects. Of these eluting substances, the elution of BPA in the oral environment is of particular interest due to its role as an endocrine disruptor. For this reason, the release of residual monomers and especially BPA from dental resins has been a cause for public concern. The assessment of patient exposure and potential health risks of dental monomers require a reliable experimental and analytical setup. However, the heterogeneous study design applied in current research hinders biocompatibility testing by impeding comparative analysis of different studies and transfer to the clinical situation. Therefore, this review aims to provide information on each step of a robust experimental and analytical in vitro setup that allows the collection of clinically relevant data and future meta-analytical evaluations.