Degree of conversion and dentin bond strength of light-cured multi-mode adhesives pretreated or mixed with sulfinate agents

The Effect of a Deproteinizing Pretreatment on the Bonding Performance and Acid Resistance of a Two-step Self-etch Adhesive on Eroded Dentin

OBJECTIVES

This study evaluated how deproteinization using sodium hypochlorite (6% NaOCl) or hypochlorous acid (50 ppm HOCl) with or without the subsequent use of an arylsulfinate salt-containing agent (Clearfil DC Activator; DCA; Kuraray Noritake Dental) affects the micro-tensile bond strength (μTBS) and formation of an acid-base resistant zone (ABRZ) of a two-step self-etch adhesive on eroded dentin.

METHODS

Coronal dentin surfaces of sound human molars were exposed to 48 cycles of demineralization (1% citric acid; 5 minutes) and remineralization (buffer solution with pH=6.4; 3.5 hours). They were then assigned to experimental groups according to the pretreatment used: none (negative control), NaOCl, NaOCl+DCA, HOCl, and HOCl+DCA. Sound dentin surfaces with no pretreatment were used as a positive control. The dentin surfaces were bonded with Clearfil SE Bond 2 (Kuraray Noritake Dental), and μTBS was measured either after 24 hours or 20,000 thermal cycles (TC). The μTBS data were statistically analyzed using a mixed-model analysis of variance (ANOVA) and t-tests with Bonferroni correction. Failure mode was determined with scanning electron microscopy (SEM), which was also used for the observation of ABRZ.

RESULTS

Among experimental groups, there was no significant difference between the negative control, HOCl, and HOCl+DCA after 24 hours, but the HOCl-pretreated groups exhibited significantly higher μTBS than the negative control after TC (p<0.01). Pretreatment with NaOCl and NaOCl+DCA resulted in significantly higher μTBS (p<0.001), but the highest μTBS was measured on sound dentin (p<0.001). TC decreased μTBS significantly in all groups (p<0.001) except for sound dentin and NaOCl+DCA (p>0.05). Adhesive failures prevailed in eroded groups, whereas cohesive failures were predominant on sound dentin. ABRZ was recognized in all groups but marked morphological differences were observed.

CONCLUSIONS

The combined use of 6% NaOCl and the arylsulfinate salt-containing agent partially reversed the compromised bonding performance on eroded dentin, while the effect of 50 ppm HOCl was negligible.

Addition of metal chlorides to a HOCl conditioner can enhance bond strength to smear layer deproteinized dentin

OBJECTIVES

To evaluate the effect of smear layer deproteinization using hypochlorous acid (HOCl) with/without metal chlorides (SrCl₂ and ZnCl₂) on the microtensile bond strength (µTBS) of two simplified adhesives to dentin.

METHODS

Human dentin surfaces with a standardized smear layer were pretreated using a 105 ppm HOCl solution with/without SrCl₂ (0.05 M, 0.1 M, 0.2 M, 0.4 M) or ZnCl₂ (0.05 M, 0.1 M, 0.2 M) for 5 s, 15 s, or 30 s. After the deproteinizing solution was washed out with water for 5 s, 15 s, or 30 s, pretreated surfaces were bonded with one-step self-etch adhesive Bond Force II or universal adhesive Clearfil Universal Bond Quick, and µTBS was measured after 24 h. Additionally, the deproteinizing effects of HOCl solutions with/without the metal chlorides were compared by measuring changes in the amide:phosphate ratio using attenuated total reflection Fourier transform infrared spectroscopy. Statistical analysis was performed using multifactor ANOVA, Tukey's post hoc tests and t-tests (p < 0.05).

RESULTS

Pretreatment with pure HOCl for 15 s and 30 s significantly decreased the amide:phosphate ratio (p < 0.05), indicating effective deproteinization, but the µTBS of both adhesives increased significantly only if HOCl was washed out for 30 s (p < 0.05). Increasing the concentrations of metal chlorides enabled shortening of the wash-out time down to 5 s while maintaining the improved µTBS (p < 0.05). The deproteinizing effect of HOCl was not significantly altered by the addition of metal chlorides (p > 0.05).

SIGNIFICANCE

The effectiveness of smear layer deproteinization using HOCl can be improved by the addition of metal chlorides, as their increasing concentration allowed to shorten the wash-out time from 30 s down to 5 s.

Triacrylamide-Based Adhesives Stabilize Bonds in Physiologic Conditions

In this study, an acrylamide-based adhesive was combined with a thiourethane-based composite to improve bond stability and reduce polymerization stress, respectively, of simulated composite restorations. The stability testing was conducted under physiologic conditions, combining mechanical and bacterial challenges. Urethane dimethacrylate was combined with a newly synthesized triacrylamide (TMAAEA) or HEMA (2-hydroxyethyl-methacrylate; control) to produce a 2-step total-etch adhesive system. Methacrylate-based composites (70 wt% silanized filler) were formulated, containing thiourethane oligomers at 0 (control) or 20 wt%. Standardized preparations in human third molars were restored; then, epoxy replicas were obtained from the occlusal surfaces before and after 7-d storage in water or with Streptococcus mutans biofilm, which was tested after storage in an incubator (static) or the bioreactor (mechanical challenge). Images were obtained from the replicas (scanning electron microscopy) and cross sections of the samples (confocal laser scanning microscopy) and then analyzed to obtain measurements of gap, bacterial infiltration, and demineralization. Microtensile bond strength of specimens stored in water or biofilm was assessed in 1-mm2 stick specimens. Data were analyzed with analysis of variance and Tukey's test (α = 0.05). HEMA-based materials had greater initial gap measurements, indicating more efficient bonding for the acrylamide materials. When tested in water, the triacrylamide-based adhesive had smaller gaps in the incubator or bioreactor. In the presence of biofilm, there was less difference among materials, but the acrylamide/thiourethane combination led to statistically lower gap formation in the bioreactor. HEMA and TMAAEA-based adhesives produced statistically similar microtensile bond strengths after being stored in water for 7 d, but after the same period with biofilm-challenged specimens, the TMAAEA-based adhesives were the only ones to retain the initial bond strength values. The use of a stable multiacrylamide-based adhesive led to the preservation of the resin-dentin bonded interface after a physiologically relevant challenge. Future studies will include a multispecies biofilm model.

Sodium p-Toluenesulfinate Enhances the Bonding Durability of Universal Adhesives on Deproteinized Eroded Dentin

The effects of deproteinization using sodium hypochlorite (NaOCl) and the subsequent application of an antioxidant (sodium p-toluenesulfinate, STS) onto the bonding durability of universal adhesives on eroded dentin were investigated. Untreated sound dentin served as the control, whereas eroded dentin, which had been prepared by pH-cycling in 1% citric acid and a remineralization solution, was either untreated, deproteinized with a 10% NaOCl gel or deproteinized with the 10% NaOCl gel and subsequently treated with an STS-containing agent. The dentin surfaces were bonded using a universal adhesive (Clearfil Universal Bond Quick, Scotchbond Universal or G-Premio Bond), and the micro-tensile bond strength (µTBS) test was performed after 24 h or 10,000 thermal cycles. The µTBS data were statistically analyzed using a three-way ANOVA and Tukey’s HSD post hoc tests. The lowest µTBS was measured on untreated eroded dentin (p < 0.001). Deproteinization of eroded dentin resulted in µTBS similar to untreated sound dentin (p > 0.05), but the highest µTBS was obtained if deproteinization was followed by the application of STS. Thermocycling significantly decreased µTBS in all groups (p < 0.001), except for STS-treated deproteinized eroded dentin (p > 0.05). This indicated that deproteinization, followed by the application of STS, could enhance the bonding durability of universal adhesives on eroded dentin.